DOE OSTI2020

Exchange of Ions across the TiN/TaO x Interface during Electroformation of TaO x -Based Resistive Switching Devices

The valence change model describes the resistive switching in metal oxide-based devices as due to electroreduction of the oxide and subsequent electromigration of oxygen vacancies. Here, we present cross-sectional X-ray energy-dispersive spectroscopy elemental maps of Ta, O, N, and Ti in electroformed TiN/TaO 2.0 /TiN structures. O, N, and Ti were exchanged between the anode and the functional oxide in devices formed at high power (~1 mW), but the exchange was below the detection limit at low power (<0.5 mW). All structures exhibit a similar Ta-enriched and O-depleted filament formed by the elemental segregation in the functional oxide by the temperature gradient. The elemental interchange is interpreted as due to Fick’s diffusion caused by high temperatures in the gap of the filament and is not an essential part of electroformation.

36 MATERIALS SCIENCE↗

NASA NTRS2006

CFD Growth of 3C-SiC on 4H/6H Mesas

This article describes growth and characterization of the highest quality reproducible 3C-SiC heteroepitaxial films ever reported. By properly nucleating 3C-SiC growth on top of perfectly on-axis (0001) 4H-SiC mesa surfaces completely free of atomic scale steps and extended defects, growth of 3C-SiC mesa heterofilms completely free of extended crystal defects can be achieved. In contrast, nucleation and growth of 3C-SiC mesa heterofilms on top of 4H-SiC mesas with atomic-scale steps always results in numerous observable dislocations threading through the 3C-SiC epilayer. High-resolution X-ray diffraction and transmission electron microscopy measurements indicate non-trivial in-plane lattice mismatch between the 3C and 4H layers. This mismatch is somewhat relieved in the step-free mesa case via misfit dislocations confined to the 3C/4H interfacial region without dislocations threading into the overlying 3C-SiC layer. These results indicate that the presence or absence of steps at the 3C/4H heteroepitaxial interface critically impacts the quality, defect structure, and relaxation mechanisms of single-crystal heteroepitaxial 3C-SiC films.

Neudeck, Philip G.↗

NASA NTRS2006

Recent Results from Epitaxial Growth on Step Free 4H-SiC Mesas

This paper updates recent progress made in growth, characterization, and understanding of high quality homoepitaxial and heteroepitaxial films grown on step-free 4H-SiC mesas. First, we report initial achievement of step-free 4H-SiC surfaces with carbon-face surface polarity. Next, we will describe further observations of how step-free 4H-SiC thin lateral cantilever evolution is significantly impacted by crystal faceting behavior that imposes non-uniform film thickness on cantilever undersides. Finally, recent investigations of in-plane lattice constant mismatch strain relief mechanisms observed for heteroepitaxial growth of 3C-SiC as well as 2H-AlN/GaN heterofilms on step-free 4H-SiC mesas will be reviewed. In both cases, the complete elimination of atomic heterointerface steps on the mesa structure enables uniquely well-ordered misfit dislocation arrays to form near the heterointerfaces with remarkable lack of dislocations threading vertically into the heteroepilayers. In the case of 3C-SiC heterofilms, it has been proposed that dislocation half-loops nucleate at mesa edges and glide laterally along the step-free 3C/4H interfaces. In contrast, 3C-SiC and 2H-AlN/GaN heterofilms grown on 4H-SiC mesas with steps exhibit highly disordered interface misfit dislocation structure coupled with 100X greater density of dislocations threading through the thickness of the heteroepilayers. These results indicate that the presence of steps at the heteroepitaxial interface (i.e., on the initial heteroepitaxial nucleation surface) plays a highly important role in the defect structure, quality, and relaxation mechanisms of single-crystal heteroepitaxial films.

Neudeck, Philip G.↗

NASA NTRS2004

Growth and Characterization of Silicon-Carbide Hetero-Polytype Structures

Films discussed in this repok were deposited at NASA Glenn Research Center on on- orientation 4H-Sic substrates. Substrates were patterned in order to form mesa structures of different shapes and sizes. The nominal thickness of the 3C-Sic film was approximately 10 microns although the thickness could change considerably between defect-free and defected mesa structures. The primary objective was to identify defect structures in defect-free mesas and in particular determine the degree and mode of strain relaxation in 3C films with thickness exceeding critical thickness.

Skowronski, Marek↗

NASA NTRS2002

Characterization of 3C-SiC Films Grown on 4H- and 6H-SiC Substrate Mesas During Step-Free Surface Heteroepitaxy

This paper reports detailed structural characterization of 3C-SiC heteroepitaxial films grown on 4H- and 6H-SiC mesa surfaces. 3C-SiC heterofilms grown by the "step-free surface heteroepitaxy" process, free of double-positioning boundary (DPB) and stacking-fault (SF) defects, were compared to less-optimized 3C-SiC heterofilms using High Resolution X-ray Diffraction (HRXRD), High Resolution Cross-sectional Transmission Electron Microscopy (HRXTEM), molten potassium hydroxide (KOH) etching, and dry thermal oxidation. The results suggest that step free surface heteroepitaxy enables remarkably benign partial lattice mismatch strain relief during heterofilm growth.

Neudeck, Philip G.↗