Small, Sharee | Search NASA

NASA NTRS2003

Structural Evolution and Mechanical Properties of PMR-15/Layered Silicate Nanocomposites

In the first year of this research, we successfully synthesized and characterized Polymer/ Layered Silicate nanocomposite using the polyimide PMR-15 as the polymer and several layered silicate nanoparticles. We have scaled up the process to allow fabrication of monoliths using these nanocomposites. The morphology of these systems was found to evolve during processing to an exfoliated structure for one system and intercalated for the rest. Correlation with Transmission Electron Microscopy studies is underway. Dynamic mechanical analysis (DMA) results showed a significant increase in the thermomechanical properties (E' and E'') of 2.5 wt.% clay loaded nanocomposites in comparison to the neat polyimide. Increasing the clay loading to 5 wt.% decreased these properties. Higher glass transition temperatures were observed for 2.5 wt.% nanocomposites compared to the neat polyimide. A lower coefficient of thermal expansion was observed only for the PGV/PMR-15 nanocomposite. An improvement in the flexural properties (modulus, strength and elongation) was observed for the 2.5 wt.% nanocomposite but not for the 5 wt.% nanocomposites. The improved barrier properties polymer/ silicate nanocomposites suggest that moisture uptake should be decreased for PMR-15 nanocomposites. The results of some recent experiments to examine delineate the ability of the silicate nanoparticles in improving the hydrolytic degradation of PMR-15 will be discussed.

Campbell, Sandi↗

NASA NTRS2001

Polyimide Based Nanocomposites for Affordable Space Transport

In setting forth its strategic plan, NASA has indicated that low-cost access to space is the key to unleashing the commercial potential of space and greatly expanding space research and exploration. The development of advanced materials will be an enabling technology for this quest for low-cost space access. In this research program, we are attempting to address the need for new advanced materials by developing high-performance nanodispersed inorganic/organic and organic/organic polyimide composites utilizing specific interactions. Our goal is to systematically manipulate these interactions and investigate the resulting processing morphology-property relationships. Specifically, we will investigate three main parameters on these relationships. These include (1) the type of polyimide; (2) the structure of the inorganic nanoparticle being used; and (3) manipulation of the interfacial energy. During the first year of this effort, we have demonstrated the successful synthesis of PMR-15/layered silicate nanocomposites. Morphological studies indicate that exfoliated structures were obtained in most instances, with a mixture of exfoliated and intercalated structures being observed also. Significant enhancements of the onset of decomposition were obtained by varying the strength of the interaction between the nanoparticle and the polymer. Varying the amount of a specific nanoparticle also affected the decomposition temperatures. A slight catalytic effect of the nanoparticles on both the imidization and crosslinking reaction has been observed and will be presented. In addition, incorporation of the nanoparticles was found to increase the glass transition temperature and slightly broaden the breadth of this relaxation.

Dean, Derrick↗