Durability of YSZ Coated Ti2AlC in 1300°C Mach 0.3 Burner Rig Tests

A thermal barrier coating system survived burner rig testing at 1300°C for 500 h. A 160 µm thick YSZ coating was applied to a Ti2AlC MAX phase sample by PS-PVD and tested face-on in an atmospheric Mach 0.3 jet fuel burner, using 5-h thermal cycles. No TBC spallation or recession was observed, only a 2.4 mg/sq. cm mass gain. The modest weight gain precluded severe volatility losses under high velocity burner conditions. The coating surface exhibited colonies of (111) flourite fiber-textured columns separated by craze patterns, with no visible moisture attack. The metastable tetragonal t' YSZ phase was obtained initially, transitioning to teq and cubic YSZ, but with little detrimental monoclinic. The thickness of the alumina TGO was ~21-23 m under the heated YSZ face and ~13-15 m on the uncoated, cooler backside. The backside exhibited removal of initial transient TiO2 nodules and etching of the underlying Al2O3 scale by volatile hydroxides in high temperature, high velocity water vapor. Aerodynamic forces produced some bending of the cantilevered sample due to creep. The test indicated exceptional stability of YSZ coatings on Ti2AlC under turbine conditions.

Smialek, J.↗

NASA NTRS1983

Interfacial layers in high-temperature-oxidized NiCrAl

The utility of Auger electron spectroscopy combined with ball cratering for depth analysis of oxide and diffusion layers produced in a Ni-14Cr-24Al alloy by oxidation in air at 1180 C for 25 hr is demonstrated. During postoxidation cooling, the oxide layers formed by this alloy spalled profusely. The remaining very thin oxide was primarily Cr2O3 with a trace of Ni. The underlying metal substrate exhibited gamma/gamma-prime and beta phases with a metallic interfacial layer which was similar to the bulk gamma/gamma-prime phase but slightly enriched in Cr and Al. These data are compared to electron microprobe results from a nominally identical alloy. The diffusion layer thickness is modelled with a simple mass balance equation and compared to recent results on the diffusion process in NiCrAl alloys.

Larson, L. A.↗

NASA NTRS1982

New oxidation features in NiCrAl-Zr revealed by an Auger microprobe

A NiCrAl-0.5 (wt %) Zr alloy, oxidized in air for 1 h at 1180 C was studied using a 30-nm resolution Auger microprobe. Depth analysis was achieved using crater edge profiling. This first application of AES to these alloys enabled several new observations of the chemical composition of microstructural features in the corrosion layer. The external oxide was rough, about 2-3 microns thick, and contained Ni, Cr, Al, and O. It was discovered that stoichiometric Al2O3 was restricted to a homogeneous layer about 300-nm thick between the oxide and the base metal. The metal immediately beneath this Al2O3 layer was found to be depleted in Al and roughly ten times richer in Zr than the bulk alloy. These observations are compared with the predictions of current models of the oxidation of MCrAl alloys.

Larson, L. A.↗

NASA NTRS1979

Some TEM observations of Al2O3 scales formed on NiCrAl alloys

The microstructural development of Al2O3 scales on NiCrAl alloys has been examined by transmission electron microscopy. Voids have been observed within grains in scales formed on a pure NiCrAl alloy. Both voids and oxide grains grew measurably with oxidation time at 1100 C. The size and amount of porosity decreased towards the oxide-metal growth interface. It was postulated that the voids resulted from an excess number of oxygen vacancies near the oxide-metal interface. Short-circuit diffusion paths were discussed in reference to current growth stress models for oxide scales. Transient oxidations of pure, Y-doped, and Zr-doped NiCrAl was also examined. Oriented alpha-(Al,Cr)2O3 and Ni(Al,Cr)2O4 scales often coexisted in layered structures on all three alloys. Close-packed oxygen planes and directions in the corundum and spinel layers were parallel. The close relationships between oxide layers provided a gradual transition from initial transient scales to steady state Al2O3 growth.

Smialek, J.↗

NASA NTRS1979

Some TEM observations of Al2O3 scales formed on NiCrAl alloys

The microstructural development of Al2O3 scales on NiCrAl alloys has been examined by transmission electron microscopy. Voids were observed within grains in scales formed on a pure NiCrAl alloy. Both voids and oxide grains grew measurably with oxidation time at 1100 C. The size and amount of porosity decreased towards the oxide-metal growth interface. The voids resulted from an excess number of oxygen vacancies near the oxidemetal interface. Short-circuit diffusion paths were discussed in reference to current growth stress models for oxide scales. Transient oxidation of pure, Y-doped, and Zr-doped NiCrAl was also examined. Oriented alpha-(Al, Cr)2O3 and Ni(Al, Cr)2O4 scales often coexisted in layered structures on all three alloys. Close-packed oxygen planes and directions in the corundum and spinel layers were parallel. The close relationship between oxide layers provided a gradual transition from initial transient scales to steady state Al2O3 growth.