NASA NTRS1999

Effects Investigated of Ambient High-Temperature Exposure on Alumina-Titania High-Emittance Surfaces for Solar Dynamic Systems

Solar-dynamic space power systems require durable, high-emittance surfaces on a number of critical components, such as heat receiver interior surfaces and parasitic load radiator (PLR) elements. An alumina-titania coating, which has been evaluated for solar-dynamic heat receiver canister applications, has been chosen for a PLR application (an electrical sink for excess power from the turboalternator/compressor) because of its demonstrated high emittance and high-temperature durability in vacuum. Under high vacuum conditions (+/- 10(exp -6) torr), the alumina-titania coating was found to be durable at temperatures of 1520 F (827 C) for approx. 2700 hours with no degradation in optical properties. This coating has been successfully applied to the 2-kW solar-dynamic ground test demonstrator at the NASA Lewis Research Center, to the 500 thermal-energy-storage containment canisters inside the heat receiver and to the PLR radiator. The solar-dynamic demonstrator has successfully operated for over 800 hours in Lewis large thermal/vacuum space environment facility, demonstrating the feasibility of solar-dynamic power generation for space applications.

deGroh, Kim K.↗

NASA NTRS1998

Effects of Ambient High Temperature Exposure on Alumina-Titania High Emittance Surfaces for Solar Dynamic Systems

Solar dynamic (SD) space power systems require durable, high emittance surfaces on a number of critical components, such as heat receiver interior surfaces and parasitic load radiator (PLR) elements. To enhance surface characteristics, an alumina-titania coating has been applied to 500 heat receiver thermal energy containment canisters and the PLR of NASA Lewis Research Center's (LeRC) 2 kW SD ground test demonstrator (GTD). The alumina-titania coating was chosen because it had been found to maintain its high emittance under vacuum (less than or equal to 10(exp -6) torr) at high temperatures (1457 F (827 C)) for an extended period (approximately 2,700 hours). However, preflight verification of SD systems components, such as the PLR require operation at ambient pressure and high temperatures. Therefore, the purpose of this research was to evaluate the durability of the alumina-titania coating at high temperature in air. Fifteen of sixteen alumina-titania coated Incoloy samples were exposed to high temperatures (600 F (316 C) to l500 F (816 C)) for various durations (2 to 32 hours). Samples, were characterized prior to and after heat treatment for reflectance, solar absorptance, room temperature emittance and emittance at 1,200 F (649 C). Samples were also examined to detect physical defects and to determine surface chemistry using optical microscopy, scanning electron microscopy operated with an energy dispersive spectroscopy (EDS) system, and x ray photoelectron spectroscopy (XPS). Visual examination of the heat-treated samples showed a whitening of samples exposed to temperatures of 1,000 F (538 C) and above. Correspondingly, the optical properties of these samples had degraded. A sample exposed to 1,500 F (816 C) for 24 hours had whitened and the thermal emittance at 1,200 F (649 C) had decreased from the non-heat treated value of 0.94 to 0.62. The coating on this sample had become embrittled with spalling off the substrate noticeable at several locations. Based on this research it is recommended that preflight testing of SD components with alumina-titania coatings be restricted to temperatures no greater than 600 F (316 C) in air to avoid optical degradation. Moreover, components with the alumina-titania coating are likely to experience optical property degradation with direct atomic oxygen exposure in space.

deGroh, Kim K.↗

NASA NTRS1998

Optical Property Enhancement and Durability Evaluation of Heat Receiver Aperture Shield Materials

Under the Solar Dynamic Flight Demonstration (SDFD) program, NASA Lewis Research Center worked with AlliedSignal Aerospace, the heat receiver contractor, on the development, characterization and durability testing of refractory metals to obtain appropriate optical and thermal properties for the SDFD heat receiver aperture shield. Molybdenum and tungsten foils were grit-blasted using silicon carbide or alumina grit under various grit-blasting conditions for optical property enhancement. Black rhenium coated tungsten foil was also evaluated. Tungsten, black rhenium-coated tungsten, and grit-blasted tungsten screens of various mesh sizes were placed over the pristine and grit-blasted foils for optical property characterization. Grit-blasting was found to be effective in decreasing the specular reflectance and the absorptance/emittance ratio of the refractory foils. The placement of a screen further enhanced these optical properties, with a grit-blasted screen over a grit-blasted foil producing the best results. Based on the optical property enhancement results, samples were tested for atomic oxygen and vacuum heat treatment durability. Grit-blasted (Al2O3 grit) 2 mil tungsten foil was chosen for the exterior layer of the SDFD heat receiver aperture shield. A 0.007 in. wire diameter, 20 x 20 mesh tungsten screen was chosen to cover the tungsten foil. Based on these test results, a heat receiver aperture shield test unit has been built with the screen covered grit-blast tungsten foil exterior layers. The aperture shield was tested and verified the thermal and structural durability of the outer foil layers during an off-pointing period.

deGroh, Kim K.↗

NASA NTRS1997

Investigation of Teflon FEP Embrittlement on Spacecraft in Low Earth Orbit

Teflon(registered trademark) FEP (fluorinated ethylene-propylene) is commonly used on exterior spacecraft surfaces in the low Earth orbit (LEO) environment for thermal control. Silverized or aluminized FEP is used for the outer layer of thermal control blankets because of its low solar absorptance and high thermal emittance. FEP is also preferred over other spacecraft polymers because of its relatively high resistance to atomic oxygen erosion. Because of its low atomic oxygen erosion yield, FEP has not been protected in the space environment. Recent, long term space exposures such as on the Long Duration Exposure Facility (LDEF, 5.8 years in space), and the Hubble Space Telescope (HST, after 3.6 years in space) have provided evidence of LEO environmental degradation of FEP. These exposures provide unique opportunities for studying environmental degradation because of the long durations and the different conditions (such as differences in altitude) of the exposures. Samples of FEP from LDEF and from HST (retrieved during its first servicing mission) have been evaluated for solar induced embrittlement and for synergistic effects of solar degradation and atomic oxygen. Micro-indenter results indicate that the surface hardness increased as the ratio of atomic oxygen fluence to solar fluence decreased for the LDEF samples. FEP multilayer insulation (MLI) retrieved from HST provided evidence of severe embrittlement on solar facing surfaces. Micro-indenter measurements indicated higher surface hardness values for these samples than LDEF samples, but the solar exposures were higher. Cracks induced during bend testing were significantly deeper for the HST samples with the highest solar exposure than for LDEF samples with similar atomic oxygen fluence to solar fluence ratios. If solar fluences are compared, the LDEF samples appear as damaged as HST samples, except that HST had deeper induced cracks. The results illustrate difficulties in comparing LEO exposed materials from different missions. Because the HST FEP appears more damaged than LDEF FEP based on depth of embrittlement, other causes for FEP embrittlement in addition to atomic oxygen and ultraviolet (UV) radiation, such as thermal effects and the possible role of soft x-ray radiation, need to be considered. FEP that was exposed to soft x-rays in a ground test facility, showed embrittlement similar to that witnessed in LEO, which indicates that the observed differences between LDEF and HST FEP might be attributed to the different soft x-ray fluences during these two missions.

deGroh, Kim K.↗

NASA NTRS1997

Investigation of Teflon FEP embrittlement on spacecraft in low earth orbit

Teflon(TM) fluorinated ethylene-propylene (FEP) is used on the exterior of spacecraft surfaces in the low earth orbit environment for thermal control. Silverized or aluminized Teflon(TM) FEP used in the Long Duration Exposure Facility (LDEF) and the Hubble Space Telescope (HST) provided evidence of the low earth orbit environments. Samples from the LDEF and HST were evaluated for solar induced embrittlement and for synergistic effects of solar degradation and atomic oxygen.

deGroh, Kim K.↗

NASA NTRS1996

Atomic Oxygen Durability of Second Surface Silver Microsheet Glass Concentrators

Second surface silver microsheet glass concentrators are being developed for potential use in future solar dynamic space power systems. Traditional concentrators are aluminum honeycomb sandwich composites with either aluminum or graphite epoxy face sheets, where a reflective aluminum layer is deposited onto an organic leveling layer on the face sheet. To protect the underlying layers, a SiO2 layer is applied on top of the aluminum reflective layer. These concentrators may be vulnerable to atomic oxygen degradation due to possible atomic oxygen attack of the organic layers at defect sites in the protective and reflective coatings. A second surface microsheet glass concentrator would be inherently more atomic oxygen durable than these first surface concentrators. In addition, a second surface microsheet glass concentrator design provides a smooth optical surface and allows for silver to be used as a reflective layer, which would improve the reflectivity of the concentrator and the performance of the system. A potential threat to the performance of second surface microsheet glass concentrators is atomic oxygen attack of the underlying silver at seams and edges or at micrometeoroid and debris (MMD) impacts sites. Second surface silver microsheet glass concentrator samples were fabricated and tested for atomic oxygen durability. The samples were iteratively exposed to an atomic oxygen environment in a plasma asher. Samples were evaluated for potential degradation at fabrication seams, simulated MMD impact sites, and edges. Optical microscopy was used to evaluate atomic oxygen degradation. Reflectance was obtained for an impacted sample prior to and after atomic oxygen exposure. After an initial atomic oxygen exposure to an effective fluence of approx. 1 x 10(exp 21) atoms/cm(exp 2), oxidation of the silver at defect sites and edges was observed. Exposure to an additional approx. 1 x 10(exp 21) atoms/cm(exp 2) caused no observed increase in oxidation. Oxidation at an impact site caused negligible changes in reflectance. In all cases oxidation was found to be confined to the vicinity of the seams, impact sites, edges or defect sites. Asher to in-space atomic oxygen correlation issues will be addressed.

deGroh, Kim K.↗

NASA NTRS1995

Degradation of FEP thermal control materials returned from the Hubble Space Telescope

After an initial 3.6 years of space flight, the Hubble Space Telescope was serviced through a joint effort with the NASA and the European Space Agency. Multi-layer insulation (MLI) was retrieved from the electronics boxes of the two magnetic sensing systems (MSS), also called the magnetometers, and from the returned solar array (SA-I) drive arm assembly. The top layer of each MLI assembly is fluorinated ethylene propylene (FEP, a type of Teflon). Dramatic changes in material properties were observed when comparing areas of high solar fluence to areas of low solar fluence. Cross sectional analysis shows atomic oxygen (AO) erosion values up to 25.4 mu m (1 mil). Greater occurrences of through-thickness cracking and surface microcracking were observed in areas of high solar exposure. Atomic force microscopy (AFM) showed increases in surface microhardness measurements with increasing solar exposure. Decreases in FEP tensile strength and elongation were measured when compared to non-flight material. Erosion yield and tensile results are compared with FEP data from the Long Duration Exposure Facility. AO erosion yield data, solar fluence values, contamination, micrometeoroid or debris impact sites, and optical properties are presented.

Zuby, Thomas M.↗

NASA NTRS1994

Environmental Durability Issues for Solar Power Systems in Low Earth Orbit

Space solar power systems for use in the low Earth orbit (LEO) environment experience a variety of harsh environmental conditions. Materials used for solar power generation in LEO need to be durable to environmental threats such as atomic oxygen, ultraviolet (UV) radiation, thermal cycling, and micrometeoroid and debris impact. Another threat to LEO solar power performance is due to contamination from other spacecraft components. This paper gives an overview of these LEO environmental issues as they relate to space solar power system materials. Issues addressed include atomic oxygen erosion of organic materials, atomic oxygen undercutting of protective coatings, UV darkening of ceramics, UV embrittlement of Teflon, effects of thermal cycling on organic composites, and contamination due to silicone and organic materials. Specific examples of samples from the Long Duration Exposure Facility (LDEF) and materials returned from the first servicing mission of the Hubble Space Telescope (HST) are presented. Issues concerning ground laboratory facilities which simulate the LEO environment are discussed along with ground-to-space correlation issues.

Degroh, Kim K.↗