Additively Reinforced Thermoformable PETG Composite Sheets for Improved Structural Efficiency
Thermoforming of short-fiber reinforced thermoplastic sheets offers a viable pathway for producing lightweight composite components; however, inherent anisotropy in fiber-reinforced sheets can limit structural performance under multidirectional loading. In this work, short carbon fiber, glass fiber, and hybrid fiber–reinforced PETG sheets were evaluated as candidate feedstock materials for thermoforming, with flexural and tensile testing performed both along the primary fiber direction and in the off-axis orientation to establish baseline stiffness, strength, and anisotropy. As expected, short carbon fiber PETG exhibited the highest stiffness and strength in the primary fiber direction, while all systems showed reduced performance in the off-axis direction. This off-axis performance reduction provides clear justification for the use of additive reinforcement when such thermoformed sheets are intended for structural applications. The intended manufacturing sequence involves thermoforming the reinforced sheet first, followed by the application of additively manufactured lattice reinforcement; therefore, the reinforcement strategy does not impose limitations on sheet formability during thermoforming. Post-forming lattice reinforcement significantly reduced load-normalized displacement by approximately 95–99% relative to non-reinforced sheets and improved weight-normalized stiffness by ~70%. These findings demonstrate that geometry-driven additive reinforcement can effectively compensate for off-axis property reductions in thermoformed PETG composites, enabling enhanced multidirectional structural performance without compromising manufacturability.