In‐Situ Product Removal for the Enzymatic Depolymerization of Poly(ethylene terephthalate) via a Membrane Reactor

Poly(ethylene terephthalate) (PET) is a common single-use plastic and a major contributor to plastic waste. PET upcycling through enzymatic depolymerization has drawn significant interests, but lack of robust enzymes in acidic environments remains a challenge. This study investigates in-situ product removal (ISPR) of protons and monomers from enzymatic PET depolymerization via a membrane reactor, focusing on the ICCG variant of leaf branch compost cutinase. More than two-fold improvements in overall PET depolymerization and terephthalic acid yields were achieved employing ISPR for an initial PET loading of 10 mgPET ml buffer −1 . The benefit of ISPR was reduced for a lower initial loading of 1 mgPET ml buffer −1 due to decreased need for pH stabilization of the enzyme-containing solutions. A back-of-envelop analysis suggests that at a modest dilution ratio, ISPR could help achieve savings on caustic base solutions used for pH control in a bioreactor. Our study provides valuable insights for future ISPR developments for enzymatic PET depolymerization, addressing the pressing need for more sustainable solutions towards plastic recycling and environmental conservation.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2024

Enzymatic depolymerization of polyester: Foaming as a pretreatment to increase specific surface area

Abstract Poly(ethylene terephthalate) (PET) is widely used for its high strength‐to‐weight ratio, gas barrier properties, and chemical resistance. The growing PET use highlights the demand for a better recycling system. Enzymatic recycling, alongside mechanical and chemical methods, is eco‐friendly and yields properties similar to virgin PET. Substrate properties ( T g , crystallinity, and specific surface area [SSA]) and enzyme stability significantly impact conversion efficiency. Higher SSA and lower crystallinity tend to yield improved depolymerization when employing leaf compost‐cutinase (LCC‐ICCG) enzymes. This study explored melt extrusion and foaming as pretreatment techniques to modify PET structural properties, using a low‐cost chemical foaming agent (CFA). The monomer conversion rate and efficiency during depolymerization were measured and related to the processing, extrudate micro‐ and meso‐structure, and polyester type. Pretreated PET substrates showed reduced T g , crystallinity, density, and enhanced SSA, resulting in a 90% mass loss for foamed RPET and VPET substrates within 2 days. In contrast, PET with ~30% of cyclohexanedimethanol comonomer exhibited a nearly 50% lower depolymerization rate, with zero BHET production. It indicates that the combination of low crystallinity, low T g , and high SSA leads to improved monomer conversion. These findings emphasize the significance of amorphization and foaming in enhancing PET enzymatic depolymerization.

42 ENGINEERING↗

DOE OSTI2024

Influence of Carboxymethyl Cellulose as a Thickening Agent for Glauber’s Salt-Based Low Temperature PCM

This work is focused on a novel, promising low temperature phase change material (PCM), based on the eutectic Glauber’s salt composition. To allow phase transition within the refrigeration range of temperatures of +5 °C to +12 °C, combined with a high repeatability of melting–freezing processes, and minimized subcooling, the application of three variants of sodium carboxymethyl cellulose (Na-CMC) with distinct molecular weights (700,000, 250,000, and 90,000) is considered. The primary objective is to optimize the stabilization of this eutectic PCM formulation, while maintaining the desired enthalpy level. Preparation methods are refined to ensure repeatability in mixing components, thereby optimizing performance and stability. Additionally, the influence of Na-CMC molecular weight on stabilization is examined through differential scanning calorimetry (DSC), T-history, and rheology tests. The PCM formulation of interest builds upon prior research in which borax, ammonium chloride, and potassium chloride were used as additives to sodium sulfate decahydrate (Glauber’s salt), prioritizing environmentally responsible materials. The results reveal that CMC with molecular weights of 250 kg/mol and 90 kg/mol effectively stabilize the PCM without phase separation issues, slowing crystallization kinetics. Conversely, CMC of 700 kg/mol proved ineffective due to the disruption of gel formation at its low gel point, hindering higher concentrations. Calculations of ionic concentration indicate higher Na ion content in PCM stabilized with 90 kg/mol CMC, suggesting increased ionic interactions and gel strength. A tradeoff is discovered between the faster crystallization in lower molecular weight CMC and the higher concentration required, which increases the amount of inert material that does not participate in the phase transition. After thermal cycling, the best formulation had a latent heat of 130 J/g with no supercooling, demonstrating excellent performance. This work advances PCM’s reliability as a thermal energy storage solution for diverse applications and highlights the complex relationship between Na-CMC molecular weight and PCM stabilization.

25 ENERGY STORAGE↗

DOE OSTI2024

Stabilizing a low temperature phase change material based on Glaubers salt

The aim of this research is to enhance the performance of Glauber's salt (sodium sulfate decahydrate, SSD) as a phase change material (PCM) for thermal energy storage applications, as well as for shipping of temperature-sensitive materials. The study investigates the effects of modifying SSD with potassium chloride (KCl) and ammonium chloride (NH 4 Cl) to achieve lower phase transition temperatures of between +6 °C and + 13 °C. Sodium polyacrylate (PAAS) is employed as a thickening agent to prevent phase separation, and borax is used as a nucleating agent to suppress supercooling. Various ratios of KCl:NH 4 Cl are tested, and the impact of PAAS concentration on phase segregation is explored. The results show that a 2 wt% concentration of PAAS effectively prevents phase separation. Samples with a KCl:NH 4 Cl ratio of 1:1.83 exhibit stable phase transition behavior and maintain latent heat values within the range of 130–140 J/g after 30 thermal cycles. Maintaining a total KCl and NH 4 Cl proportion of 10 wt% is crucial to achieve the desired lower melting temperature. As a result, the study highlights the significance of thermal cycling in improving the stability of the PCM. The optimized SSD-based eutectic PCM formulations hold promise for applications in the cold chain industry.

25 ENERGY STORAGE↗