Spataru, Sergiu

Publications and source records attributed to Spataru, Sergiu.

10 records

DOE OSTI2024

Field‐representative evaluation of PID‐polarization in TOPCon PV modules by accelerated stress testing

Abstract Potential‐induced degradation‐polarization (PID‐p) can reduce module power, but how to project the extent to which PID‐p may occur in field conditions considering the factors of system voltage, condensed moisture, temperature, and illumination has not been clarified. Using tunnel oxide passivated contact (TOPCon) modules, this work demonstrates a method to test full‐size crystalline silicon PV modules for PID‐p to provide field‐representative results. In initial screening tests with positive or negative 1000 V electrical bias applied at 60°C for 96 h using Al foil electrodes on the glass surfaces, the module type exhibited reversible PID‐p only on the front face when the cell circuit was in negative voltage potential. No PID was detected on the rear after testing in either polarity. We then evaluated the PID‐p sensitivity on the front side under different UV irradiances while maintaining the glass surface wet to estimate real‐world susceptibility to PID‐p. The magnitude of the observed behavior was fit using a previously developed charge transfer and depletion by light model. Whereas power loss with −1000 V applied to the cell circuit at 60°C for 96 h in the dark was about 30%, testing the module front under 0.051 W·m −2 nm −1 at 340 nm UVA irradiation using fluorescent tubes, the mean degradation was only 3%. When the modules were tested in the dark for PID‐p with in situ dark current–voltage (I‐V) characterization, the thermal activation energy for degradation was 0.71 eV; for recovery in the dark, it was 0.58 eV. Whereas recovery from the degraded state at 60°C in the dark without voltage bias was 5% absolute in 38 h, rapid recovery of about 5% absolute was observed with 1000 W·s/m 2 exposure at 25°C using a flash tester.

14 SOLAR ENERGY↗

DOE OSTI2023

Examining Light-Induced Degradation with Combined-Accelerated Stress Testing

While further understanding is sought, the results suggest that a module can show no degradation in performance through a qualification test light soak, (IEC 61215: 2021 MQT 19.1 requirement of 10 kW minimum on one side). Yet, such cells may degrade significantly by LID under conditions within the statistical extremes of the natural environment applied in combined-accelerated stress testing (CAST).

combined-accelerated stress testing↗

DOE OSTI2023

Acceleration Factors for Combined‐Accelerated Stress Testing of Photovoltaic Modules

Combined‐accelerated stress testing (C‐AST) is developed to establish the durability of photovoltaic (PV) products, including for degradation modes that are not a priori known or examined in standardized tests. C‐AST aims to comprehensively represent the sample, stress factors, and their combinations using levels at the statistical tails of the natural environment. Acceleration factors for relevant climate sequences within the C‐AST cycle with respect to the Florida USA climate are estimated for selected degradation mechanisms. It is found that for degradation of the outer backsheet polymer layer, the acceleration factor of the tropical climate sequence (the longest of the climate sequences) is f ( T , G ) = 17.3 with ultraviolet photodegradation; for polyethylene terephthalate hydrolysis (backsheets), f ( T , RH ) = 426; for electrochemical corrosion (PV cell), f ( I ) = 14.1; and for PbSn solder fatigue f (Δ T , r ( T )) = 17.3. Here, T is the module temperature, G is the broadband spectrum irradiance on the plane of array of the module, RH is the relative humidity on the module surface, I is the leakage current through the module packaging, and r ( T ), the number of temperature reversals. The methods discussed herein are generally applicable for evaluating acceleration factors in other accelerated test methods.

14 SOLAR ENERGY↗

DOE OSTI2022

Evaluation of bifacial module technologies with combined–accelerated stress testing

In view of the increasing interest and market share of bifacial cells and modules, suitable substrates such as glass and transparent backsheets along with ethylene vinyl acetate (EVA) and polyolefin elastomer (POE) encapsulants were examined in combined-accelerated stress testing (C-AST) to evaluate and compare degradation modes. Testing with both monofacial and bifacial cells, we found glass-glass modules with monofacial cells led to greater grid finger breakage than those with polymeric backsheets. Furthermore, this is attributed to previous X-ray topography and modeling work showing higher stress in cells and interconnections in glass-glass modules than glass-backsheet modules. Consistent with the objectives of C-AST, which stresses modules at levels corresponding to the limits seen in the natural environment, we observed the UV-fluorescence signatures of modules tested in C-AST (considering the degradation associated with developing chromophores, moisture penetration and photobleaching effects) to be like those in fielded modules, more so than other chamber stress testing implemented for comparison. We found light-induced degradation (LID) in module types with regenerated (inactive) cells with C-AST, suggesting the possibility of LID destabilization in some field conditions. We could also distinguish potential-induced degradation (PID) on the back of the bifacial passivated emitter and rear cells (PERC) in C-AST. Confirming with ex-situ tests, we found polarization-type PID most prevalent in glass-glass modules with EVA as would be anticipated considering the greater leakage current through such module encapsulation. Unlike PID tests performed in the dark, which can lead to false positive PID test results, field-representative illumination is experienced by the modules on the front and back side while –1200 V system voltage is applied in C-AST, supporting the conclusion that this module type with glass-glass construction would be susceptible to PID in the field.

14 SOLAR ENERGY↗

DOE OSTI2021

Inverters: A Pivotal Role in PV Generated Electricity

This presentation discusses the pivotal role inverters play in PV generated electricity. Topics include: the inverter as the center of the system--increasingly becoming the brain, with more features and capabilities (hybrid systems, safety, islanding, monitoring, etc.); increasing inverter-based generated electricity associated with many renewable energy sources; increased dependence for grid support and forming capability; communication within the grid and security increasingly required; increasing complexity leads to more chances to fail; as in most PV segments, there is cost reduction pressure, which makes it more challenging to keep the reliability high.

ENGINEERING,SOLAR ENERGY↗

DOE OSTI2020

In-Situ Measurement of Power Loss for Crystalline Silicon Modules Undergoing Thermal Cycling and Mechanical Loading Stress Testing

An in-situ method is proposed for monitoring and estimating the power degradation of mc-Si photovoltaic (PV) modules undergoing thermo-mechanical degradation tests that primarily manifest through cell cracking, such as mechanical load tests, thermal cycling and humidity freeze tests. The method is based on in-situ measurement of the module’s dark current-voltage (I-V) characteristic curve during the stress test, as well as initial and final module flash testing on a Sun simulator. The method uses superposition of the dark I-V curve with final flash test module short-circuit current to account for shunt and junction recombination losses, as well as series resistance estimation from the in-situ measured dark I-Vs and final flash test measurements. The method is developed based on mc-Si standard modules undergoing several stages of thermo-mechanical stress testing and degradation, for which we investigate the impact of the degradation on the modules light I-V curve parameters, and equivalent solar cell model parameters. Experimental validation of the method on the modules tested shows good agreement between the in-situ estimated power degradation and the flash test measured power loss of the modules, of up to 4.31 % error (RMSE), as the modules experience primarily junction defect recombination and increased series resistance losses. However, the application of the method will be limited for modules experiencing extensive photo-current degradation or delamination, which are not well reflected in the dark I-V characteristic of the PV module.

14 SOLAR ENERGY↗

DOE OSTI2020

Advancing reliability assessments of photovoltaic modules and materials using combined-accelerated stress testing

Previously undiscovered failure modes in photovoltaic (PV) modules continue to emerge in field installations despite passing protocols for design qualification and quality assurance. Failure to detect these modes prior to widespread use could be attributed to the limitations of present-day standard accelerated stress tests (ASTs), which are primarily designed to identify known degradation or failure modes at the time of development by applying simultaneous or sequential stress factors (usually two at most). Here, we introduce an accelerated testing method known as the combined-accelerated stress test (C-AST), which simultaneously combines multiple stress factors of the natural environment. Simultaneous combination of multiple stress factors allows for improved identification of failure modes with better ability to detect modes not known a priori. A demonstration experiment was conducted that reproduced the field-observed cracking of polyamide- (PA-) and polyvinylidene fluoride (PVDF)–based backsheet films, a failure mode that was not detected by current design qualification and quality assurance testing requirements. In this work, a two-phase testing protocol was implemented. The first cycle (“Tropical”) is a predominantly high-humidity and high-temperature test designed to replicate harsh tropical climates. The second cycle (“Multi-season”) was designed to replicate drier and more temperate conditions found in continental or desert climates. Testing was conducted on 2 × 2-cell crystalline-silicon cell miniature modules constructed with both ultraviolet (UV)–transmitting and UV-blocking encapsulants. Cracking failures were observed within a cumulative 120 days of the Tropical condition for one of the PA-based backsheets and after 84 days of Tropical cycle followed by 42 days of the Multi-season cycle for the PVDF-based backsheet, which are both consistent with failures seen in fielded modules. In addition to backsheet cracking, degradation modes were observed including solder/interconnect fatigue, various light-induced degradation modes, backsheet delamination, discoloration, corrosion, and cell cracking. The ability to simultaneously apply multiple stress factors may allow many of the test sequences within the standardized design qualification procedure to be performed using a single test setup.

14 SOLAR ENERGY↗

DOE OSTI2020

Methods for In Situ Electroluminescence Imaging of Photovoltaic Modules Under Varying Environmental Conditions

Electroluminescence (EL) imaging is a powerful tool used to identify defects in photovoltaic solar cells. Typically, this type of characterization is performed in the dark using a current injection that equals short-circuit current measured at standard test conditions (STC). Restricting imaging to such a temperature range limits the information obtained about the module and cells. However, it is not trivial to develop a tool that would allow for EL imaging to be performed under a wider range of temperatures. Here we demonstrate an in situ EL imaging capability developed within an environmental chamber that allows for control of sample temperatures between –40 and 90 °C. Additionally, we demonstrate EL imaging of 4-cell mini-modules (MiMo) under front-side mechanical loading. A Raspberry Pi-connected camera with short-pass filter removed is used for EL imaging. The camera is low-cost with a small form-factor, appropriate for use in a harsh, enclosed environment. The camera is installed within a thermally isolating housing mounted within the environmental chamber. Three example cases are given for MiMos that exhibit various forms of degradation including solder fatigue and cell cracking. It is shown that by measuring at conditions above and below STC, different behaviors may be identified. In some cases, restricting characterization to STC may lead to a failure to detect damage existing in the sample.

14 SOLAR ENERGY↗

DOE OSTI2020

Combined-Accelerated Stress Testing for Advanced Reliability Assessment of Photovoltaic Modules

New and previously undiscovered degradation mechanisms continue to be identified after field exposure in new photovoltaic module designs or materials oftentimes results in significant losses in investment. This is despite passing certification tests. Testing is insufficient largely due to their single-or double-stress nature. A Combined-Accelerated Stress Test (C-AST) has recently been developed. The test combines multiple stress factors of the natural environment to better replicate conditions experienced by modules in the field and detect mechanisms not a-priori known in new materials and designs.

accelerator factor modeling↗

DOE OSTI2020

Reproducing the 'Framing' by a Sequential Stress Test

The 'Framing' (local discoloration along cell edges) was induced by a simple sequential accelerated stress test (consisting of hygrothermal- and UV-stressors) applied to the PV modules with high OTR (oxygen transmission rate) backsheet, irrespective of the inclusion of UV-absorber in poly(ethylene-co-vinyl acetate) (EVA) encapsulant. UV-fluorescence imaging of the PV modules suggests that the spatially-inhomogeneous degradation of EVA material under UV-irradiating conditions is correlated to this 'Framing' indicating an underlying common mechanism. These findings would contribute to the development of test procedures to broadly mimic the actual failures observed in fielded PV.

14 SOLAR ENERGY↗