Specht, Paul Elliott

Publications and source records attributed to Specht, Paul Elliott.

14 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Investigation of novel twinning in additive body centered cubic titanium (Fiscal Year 2024 Final Report)

This report summarizes the result of a one year seedling project to investigate unusual twinning behavior in shock loaded additive Ti5552. The twinning behavior only occurs when the β phase of Ti5553 is metastable, and it appears to be a type of double twin involving two different twin variants, first a {332}⟨113⟩ twin forms before being consumed by a specific {112}⟨111⟩ twin variant to create a 20 o . This behavior has only been detected during shock loading around incipient spall damage. The twinning is investigated by performing postmortem EBSD and PED analysis of gas-gun loaded specimens and preliminary molecular dynamics simulations.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Dynamic response of additively manufactured Ti–5Al–5V–5Mo–3Cr as a function of heat treatment

Both shock and shockless compression experiments were performed on laser powder bed fusion (LPBF) Ti–5Al–5V–5Mo–3Cr (Ti-5553) to peak compressive stresses near 15 GPa. Experiments were performed on the as-built material, containing a purely β (body centered cubic) microstructure, and two differing heat treatments resulting in a dual phase α (hexagonal close packed) and β microstructure. The Hugoniot, Hugoniot elastic limit (HEL), and spallation strength were measured and compared to wrought Ti-6Al-4V (Ti-64). The results indicate the LPBF Ti-5553 Hugoniot response is similar between heat treatments and to Ti-64. The HEL stress observed in the LPBF Ti-5553 was considerably higher than Ti-64, with the as-built, fully β alloy exhibiting the largest values. The spallation strength of the LPBF Ti-5553 was also similar to Ti-64. Clear evidence of initial porosity serving as initiation sites for spallation damage was observed when comparing computed tomography measurements before and after loading. Post-mortem scanning electron microscopy images of the recovered spallation samples showed no evidence of retained phase changes near the spall plane. The spall plane was found to have kinks aligned with the loading direction near areas with large concentrations of twin-like, crystallographic defects in the as-built condition. For the heat-treated samples, the concentrations of twin-like, crystallographic defects were absent, and no preference for failure at the interface between the α and β phases was observed.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Flow Strength Measurements of Wrought and AM SS304L via Pressure Shear Plate Impact Experiments

Pressure-shear plate impact experiments were performed to quantify flow strength of wrought, as-built additively manufactured (AM), and heat-treated and recrystallized AM 304 L stainless steel (SS304L) under combined loading. Impact velocities spanned between 0.03 and 0.24 mm/μs, resulting in corresponding pressures of 0.62–5.93 GPa. Flow strength measurements are comparable for the sample variants across the studied loading conditions; however, shear wave structures significantly differ between sample type. Microstructurally aware simulations indicate local strain differences attributed to anisotropic elastic constants of large grains (~1 mm) in the as-built and heat-treated AM may impede the ability to uniformly transmit a shear wave.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Understanding Microstructural Effects on Dynamic Performance Towards the Development of Shock Metamaterials

With the recent advances in additive manufacturing (AM), long-range periodic lattice assemblies are being developed for vibration and shock mitigation components in aerospace and military applications with unique geometric and topological structures. There has been extensive work in understanding the static properties associated with varying topology of these lattice architectures, but there is almost no understanding of microstructural affects in such structures under high-strain rate dynamic loading conditions. Here we report the shock behavior of lattices with varying intrinsic grain structures achieved by post process annealing. High resolution 316L stainless steel lattices were 3D printed by a laser-powder bed fusion machine and characterized by computed tomography. Subsequent annealing resulted in stress-relieved and recrystallized lattices. Overall the lattices had strong cubic texture aligning with the x-, y- and z-directions of the build with a preference outside the build direction (z). The recrystallized sample had more equiaxed polygonal grains and a layer of BCC ferrite at the surface of the structure approximately 1 grain thick. Upon dynamic compression the as-deposited lattice showed steady compaction behavior while the heat-treated lattices exhibit negative velocity behavior indicative of failure. We attribute this to the stiffer BCC ferrite in the annealed lattices becoming damaged and fragmenting during compression.

36 MATERIALS SCIENCE↗