Microstructural Engineering of Mn-Alloyed Austenitic Steel for Hydrogen Storage and Delivery
Austenitic stainless steels are commonly used for hydrogen storage and transportation. These alloys have a high nickel (Ni) content, which increases alloy cost. In this study, high manganese (Mn) austenitic alloys were evaluated as potential lower cost alternatives. Two heats of high Mn alloys with different stacking fault energies (SFE) of ~29 mJ·m -2 and 49 mJ·m -2 were acquired. Additionally, a new vanadium (V)-microalloyed high Mn alloy was designed to achieve a SFE of 47 mJ·m -2 to minimize planar slip deformation mechanisms. Post-processing via cold working in conjunction with aging was also performed on the V-microalloyed high Mn steel. Hydrogen embrittlement sensitivity was investigated using circumferential notch tensile specimens cathodically charged with hydrogen in a 0.05M NaOH electrolytic solution. The alloys were compared to a cold-worked 316L stainless steel, which exhibited no strength loss due to hydrogen. The high Mn alloys with SFE of ~29 mJ·m 2 and 49 mJ·m -2 had notch strength losses of 11 and 6 pct, respectively. The V-microalloyed high Mn steel in the as-hot-rolled condition had a notch strength loss of 17 pct. Furthermore, the V-microalloyed high Mn steel in the cold worked and aged condition indicated no notch strength loss in hydrogen, which was comparable to the performance of the 316L stainless steel.
Austenite Formation and Manganese Partitioning during Double Soaking of an Ultralow Carbon Medium‐Manganese Steel
Double soaking (DS) is a thermal processing route intended to produce austenite–martensite microstructures in steels containing austenite‐stabilizing additions and consists of intercritical annealing (primary soaking), followed by heating and brief isothermal holding at an increased temperature (secondary soaking), and quenching. Herein, experimental dilatometry during DS of a medium‐manganese (Mn) steel with nominally 7 wt% Mn and an ultralow residual carbon concentration, in combination with phase‐field simulations of austenite formation during secondary soaking, is presented. The feasibility of maintaining heterogeneous Mn distributions during DS is demonstrated and insight is provided on the effects of the secondary soaking temperature and prior Mn distribution on the ferrite‐to‐austenite phase transformation during the secondary soaking portion of the DS treatment.
The Role of Retained Austenite in Tempered Martensite Embrittlement of 4340 and 300-M Steels Investigated through Rapid Tempering
Tempered martensite embrittlement (TME) is investigated in two medium carbon, high strength steels, 4340 (low silicon) and 300-M (high silicon), via rapid (1, 10, or 100 s) and conventional (3600 s) tempering. Rapid tempering of 4340 diminishes the depth of the TME toughness trough, where improvements in impact toughness correspond to the suppression of retained austenite decomposition. In 300-M, retained austenite decomposition is suppressed to an even greater extent by rapid tempering. While toughness improves overall after rapid tempering, TME severity remains consistent in 300-M across the tempering conditions examined. Through interrupted tensile tests, it was found that the 300-M conditions that exhibit TME are associated with mechanically unstable retained austenite. Unstable retained austenite is shown to mechanically transform early in the deformation process, presumably resulting in fresh martensite adjacent to interlath cementite that ultimately contributes to TME. The present results emphasize the role of both the thermal decomposition and mechanical transformation of retained austenite in the manifestation of TME.
Diffusional and Partitionless Ferrite‐to‐Austenite Phase Transformations during Intercritical Annealing of Medium‐Mn Steels
Experimental research on intercritical annealing of a cold‐rolled Fe–7Mn steel with ultralow carbon concentration is presented, providing insight into the efficacy of generating Mn‐enriched austenite during relatively short (≈1000 s) heat treatments compared with batch annealing, as well as the phase transformation mechanisms that can occur during intercritical annealing. It is shown through both bulk characterization and electron microscopy in conjunction with energy‐dispersive X‐ray spectroscopy that Mn partitioning to austenite occurs via diffusional, partitioning growth of austenite during these shorter treatments and that the intercritical temperature influences the level of Mn enrichment in austenite. Evidence of massive (partitionless) and diffusional (partitioning) transformations of ferrite to austenite occurring simultaneously in a single sample are also shown along with a thermodynamic rationale for this occurrence, which is suggested to be related to residual Mn‐banding that develops during solidification.
The In Situ Observation of Phase Transformations During Intercritical Annealing of a Medium Manganese Advanced High Strength Steel by High Energy X-Ray Diffraction
Microstructural changes during thermal processing of a medium manganese steel containing (in wt%) 0.19C and 4.39 Mn were evaluated in situ with a high energy X-ray diffraction system (HEXRD). Samples with an initial fully martensitic microstructure were heated to intercritical annealing (IA) temperatures of 600 or 650°C, held for 30 min, and cooled to room temperature. Diffraction data were analyzed to determine the variations in austenite and ferrite phase fractions and phase lattice constants throughout the ICA cycles. On heating, the 2 vol. pct of austenite present in the starting microstructure decomposed, and cementite precipitation then occurred. During isothermal holding, the austenite fraction increased, up to 20% for the sample annealed at 650°C. The measured austenite fractions were less than those calculated by Thermo-Calc for equilibrium conditions, indicating that the 30-min hold time was insufficient to achieve near-equilibrium conditions. Observed changes in lattice parameters during isothermal holding were interpreted to reflect composition changes due to redistribution of the C and Mn between austenite and ferrite. The results are discussed in relation to the potential for controlling austenite stability during ambient temperature deformation.
Tempering and Austempering of Double Soaked Medium Manganese Steels
The addition of a tempering or austempering step to the double soaking of a 0.14C–7.17Mn (wt pct) steel was investigated in the present contribution. The double soaking heat treatment is a two-step intercritical annealing heat treatment, which generates microstructures of athermal martensite, retained austenite and ferrite when applied to medium manganese steels. Microstructures following double soaking and (aus)tempering contained a combination of retained austenite, athermal or tempered martensite, and blocky or bainitic ferrite. X-ray diffraction, dilatometry and transmission Kikuchi diffraction were utilized to investigate microstructural changes which occurred during tempering or austempering. The resulting mechanical properties were measured using uniaxial tensile testing. The double soaking plus tempering heat treatment was shown to generate an ultimate tensile strength of 1,340 MPa in combination with 28 pct total elongation while the double soaking plus austempering heat treatment resulted in an ultimate tensile strength of 1,675 MPa and total elongation of 22 pct. Overall, both novel heat treatments produced a combination of strength and ductility desired for the third generation of advanced high strength steels.
Hydrogen Embrittlement of Medium Mn Steels
Recent research efforts to develop advanced–/ultrahigh–strength medium-Mn steels have led to the development of a variety of alloying concepts, thermo-mechanical processing routes, and microstructural variants for these steel grades. However, certain grades of advanced–/ultrahigh–strength steels (A/UHSS) are known to be highly susceptible to hydrogen embrittlement, due to their high strength levels. Hydrogen embrittlement characteristics of medium–Mn steels are less understood compared to other classes of A/UHSS, such as high Mn twinning–induced plasticity steel, because of the relatively short history of the development of this steel class and the complex nature of multiphase, fine-grained microstructures that are present in medium–Mn steels. The motivation of this paper is to review the current understanding of the hydrogen embrittlement characteristics of medium or intermediate Mn (4 to 15 wt pct) multiphase steels and to address various alloying and processing strategies that are available to enhance the hydrogen-resistance of these steel grades.