The 650 °C Tensile Deformation of Graded IN718-René41 Superalloy Fabricated by Laser Blown-Powder Directed Energy Deposition

The microstructure and 650 °C tensile properties of a compositionally graded IN718-René41 (718-R41) superalloy fabricated by laser blown-powder directed energy deposition (DED-LB/M) are investigated to understand structure–property relationships and baseline tensile properties. Digital Image Correlation (DIC), in situ neutron diffraction, and conventional characterization techniques are performed to study the as-built and heat-treated states. The applied heat treatment generates static recrystallization and equiaxed grains in 718-rich compositions, while R41-rich compositions remain partially or un-recrystallized possibly influenced by a higher MC carbide fraction (>0.5%). The yield strengths of the 718 and R41 sections in the heat-treated state are comparable to wrought forms but the graded compositions show weakness due to unoptimized heat treatment. Diffraction elastic constants first decrease and then increase along the 718-R41 composition gradient, while a small difference is observed between the as-built and heat-treated states and γ, γ′ phases. Overall, the compositionally graded region shows a smooth transition in the elastic properties. Grain-level load transfer from the (220) to (200) grains shows compositional dependence, and qualitatively agrees with DIC-measured macroscopic yield strength. Within the (200) grains, the γ/γ′ phases deform elastically until the γ phase yields and afterwards, the γ′ phase takes load from the γ phase.

Huang, Shenyan (ORCID:0000000196528114)↗
DOE OSTI2024

Influence of grain size on α' Cr precipitation in an isothermally aged Fe-21Cr-5Al alloy

Cr-rich α' precipitation during aging typically leads to hardening and accordingly embrittlement of FeCrAl alloys, which needs to be suppressed. The influence of grain size on α' precipitation was studied by aging coarse-grained (CG), ultra-fine grained (UFG), and nanocrystalline (NC) ferritic Kanthal-D [KD; Fe-21Cr-5Al (wt.%) alloy] at 450, 500 and 550 °C for 500 h. After aging at 450 and 500 °C, less hardening was observed in the UFG KD than in CG KD. Atom probe tomography indicated a lower number density and larger sized intragranular α' in the UFG versus the CG alloy. The smaller grain size and higher defect (vacancy and dislocation) density in the UFG KD facilitated diffusion and accordingly enhanced precipitation kinetics, leading to coarsening of precipitates, as well as saturation of precipitation at lower temperatures, as compared to those in CG KD. No hardening occurred in UFG and CG KD after aging at 550 °C, indicating that the miscibility gap is between 500 and 550 °C. NC KD exhibited softening after aging owing to grain growth. α' precipitation occurred in NC KD aged at 450 °C but not at 500 °C, indicating that miscibility gap is between 450 and 500 °C. Thus, the significantly smaller grain size in NC KD decreased the miscibility gap, as compared to that in CG and UFG KD. Finally, this is attributed to the absorption of vacancies by migrating grain boundaries during aging, suppressing α' nucleation and enhancing Cr solubility.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Tensile Deformation of DED Graded IN718-René41 Superalloy at 650°C by in-situ Neutron Diffraction and Digital Image Correlation

A compositionally graded material comprised IN718 (718, γ'/γ" strengthened superalloy) and René41 (R41, a medium γ' strengthened superalloy) was fabricated using laser blown-powder directed energy deposition (DED/LB-M). Hot gas path components that require high and low temperature capabilities at different locations may benefit from such graded superalloy, potentially eliminating the use of welded or mechanically joined components and reducing cost. In the present work, microstructure and 650°C tensile behavior of 718-R41 graded superalloy in as-built and heat-treated states are investigated by Digital Image Correlation (DIC), in-situ neutron diffraction, coupled with conventional characterization techniques. The applied heat treatment generates static recrystallization and equiaxed grains in 718 rich compositions, while R41 rich compositions remain partially or un-recrystallized. Yield strengths of 718 and R41 sections in heat-treated state are comparable to wrought forms but the graded compositions show weakness. From neutron experiment, diffraction elastic constants and single crystal elastic constants are calculated, which show small difference between the as-built and heat-treated states and between the γ and γ' phases. Grain-level load transfer from the (220) grains to (200) grains is found to be composition dependent, and qualitatively agrees with DIC measured macroscopic yield strength. Within the (200) grains, the γ/γ' phases deform elastically until the γ phase yields and afterwards the γ' phase takes load from γ phase.

digital image correlation↗
DOE OSTI2022

Residual stress and microstructure in IN718-René41 graded superalloy fabricated by laser blown directed energy deposition

Additively printed Ni-based superalloy with a compositionally graded transition from IN718 to René41 was fabricated by laser blown-powder directed energy deposition (DED/LB-M), with the goals of meeting location-specific temperature capability and reducing component cost for hot gas path turbine components. Residual stress distribution in thin wall specimens with three sets of DED build parameters in the as-built and stress-relieved states was measured by neutron diffraction. For calculating residual stress, the calculated d0 method was found to be more appropriate as stress-free reference than using the lattice spacing measured from the stress-relief heat treated specimens. Longer dwell time (lower interpass temperature), higher energy input, smaller layer thickness resulted in a higher magnitude of tensile residual stresses at edges and compressive residual stresses at center of the specimens. The residual stress results did not show a strong dependence on graded compositions, indicating that the residual stress build-up was more geometry and process dependent. Non-destructive neutron imaging based on the attenuation coefficient qualitatively visualized the compositional variation in the bulk and showed good agreement with quantitative Electron Probe Micro-Analysis (EPMA) measurement. Grain structure, texture, and residual plastic strain along the build direction were characterized by Electron Backscatter Diffraction (EBSD). Long columnar grains with (001) preferred grain orientation were dominant along the build direction. Compositional change did not show an obvious effect on the epitaxial growth of dendrites and the continuation of the columnar grains. Residual plastic strain was relatively low in the as-built specimens.

36 MATERIALS SCIENCE↗
DOE OSTI2022

The relationship between grain size distribution and ductile to brittle transition temperature in FeCrAl alloys

A FeCrAl (Fe12Cr6Al2Mo) alloy was prepared by two methods, (a) traditional wrought and (b) powder metallurgy (PM). Further, both alloys exhibited the same average grain size (~40 um), but the PM alloy displayed a wider grain size distribution. Charpy impact testing showed that the ductile to brittle transition temperature width is dependent on the grain size distribution width.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Powder Metallurgy HIP Process Study and Mechanical Property Evaluations for IN740H

The effects of hot isostatic pressing (HIP) parameters and powder size distribution (PSD) on the resulting microstructure and properties of powder metallurgy (P/M) IN740H have been investigated. Properties can be substantially tailored through the appropriate management of these parameters. Applying a thermal presoak to the input powder prior to the sintering stage of HIP can significantly increase average grain size and coarse grain fraction, enabling a trade for improved creep resistance at the expense of tensile strength. Here, powder thermal presoak was found to have a larger impact on microstructure and properties than the use of a coarser PSD alone. Additionally, substantial grain growth and grain boundary migration is observed in P/M IN740H at HIP temperatures above 1260°C. Given its inherently finer grain size, P/M HIP IN740H typically outperforms its cast and wrought counterparts in tensile response. Creep life at 700–800°C was inferior to wrought due to PPBs coincident with grain boundaries which served as cavity nucleation sites, leading to lower creep ductility. The ability to adjust the microstructure toward a more balanced creep and tensile behavior allows P/M HIP IN740H to be considered for high-temperature applications in advanced ultra-supercritical steam and supercritical carbon dioxide power cycles.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Measuring residual stress in Ti-6Al-4V with HR-EBSD, using reference patterns from annealed material

In this study, elastic strain and residual stress values in an engineering material were determined by high-resolution EBSD (HR-EBSD) using reference patterns from annealed, recrystallized material. Specifically, rolled Ti-6Al-4V sheet was analyzed using HR EBSD in both an as-annealed and a strained state, the latter established via a static two-point bend fixture. The commercial software CrossCourt4 (CC4) was used to evaluate the relative intragranular strain tensor components of the alpha grains mapped by HR-EBSD. The intragranular reference patterns identified in each grain by the software were then replaced with similarly-oriented patterns from scans of the as-annealed, recrystallized material. The CC4 analysis was then repeated to provide calibrated strain and residual stress values. Elastic strains on the order of 10–3 were detected, with corresponding residual stress values on the order of 1 GPa. Subsequent analyses using high energy synchrotron x-ray diffraction showed good correlation with the elastic strains measured by HR-EBSD using the annealed reference patterns. Additionally, the maximum macroscopic stress analytically predicted for two-point bending was in agreement with the residual stress observed. Good repeatability of the methodology and insight into the state of individual grains were also observed. The findings provide encouraging evidence that accurate intragranular and long-range residual stress measurements of engineering significance can be made with HR-EBSD using a physical reference pattern library.