Use of Spectralon as a diffuse reflectance standard for in-flight calibration of earth-orbiting sensors

Spectralon, a commercially available diffuse reflectance material made from polytetrafluoroethylene (PTFE), is being evaluated for the multiangle imaging spectroradiometer (MISR), currently under development for the Earth Observing System. Results of a series of environmental exposure tests indicate that no degradation of the optical properties was apparent following proton bombardment, and stability through UV illumination was satisfactory, provided simple cleaning and handling procedures were implemented. A buildup of several thousand volts of static charge was found to develop while simulating a rare pass through an auroral storm.

Bruegge, Carol J.↗

NASA NTRS1993

Ultraviolet stability and contamination analysis of Spectralon diffuse reflectance material

A detailed chemical analysis was carried out on Spectralon, a highly Lambertian, diffuse reflectance material. Results of this investigation unambiguously identified the presence of an organic (hydrocarbon) impurity intrinsic to the commercial material. This impurity could be removed by a vacuum bake-out procedure and was identified as the cause of optical changes (degradation) that occur in the material when exposed to UV light. It was found that when this impurity was removed, the Spectralon material was photochemically stable and maintained its reflectance properties even after extensive solar UV exposure.

Stiegman, Albert E.↗

NASA NTRS1991

Reflectance stability analysis of Spectralon diffuse calibration panels

The Multi-angle Imaging SpectroRadiometer (MISR) plans to use deployable diffuse reflectance panels to provide periodic radiometric calibrations of its nine cameras while in-flight. Near-Lambertian reflectance characteristics are desirable to facilitate flat-field camera intercomparisons. Also required is panel spatial and spectral uniformity, and stability with time. Spectralon, a commercially available polytetrafluoroethylene (PTFE) compound, has been baselined in the MISR design. To assess the suitability of this material, a series of degradation tests were planned and implemented. These included UV vacuum exposure and proton bombardment tests which simulated the exposure levels to be encountered during the mission life. Proton levels are now considered too low to be of concern, but UV vacuum tests demonstrate sensitivity to material contamination. Material investigations have concluded that hydrocarbons are present in the bulk of the material, and that plastic packaging materials can introduce additional surface-layer contamination. It is found however, that these unwanted elements can be eliminated through vacuum pumping at elevated temperatures. Exposure to a UV source, while in vacuum, is again planned for a set of targets which have been vacuum baked. This will assess the stability of the pure PTFE form.

Bruegge, Carol J.↗