Microstructural evolution in ion irradiated cold spray Cr coated Zr-alloy
Not Available
Dabney, Tyler (ORCID:0000000280588996)↗
Engineering topics
Sridharan, Kumar
Publications and source records attributed to Sridharan, Kumar.
Microstructural evolution of compositionally complex solid-solution alloys under in-situ dual-beam irradiation
Here, this work attempts to link the microstructural evolution of single-phase compositionally complex alloy (CCA) compositions under dual-beam irradiation to their Mn-content via the stacking-fault energy (SFE) and vacancy migration energies. Two alloys, Cr 18 Fe 27 Mn 27 Ni 28 and Cr 15 Fe 35 Mn 15 Ni 35 , along with less compositionally complex pure Ni and Fe 56 Ni 44 binary were irradiated at 500 and 600 °C under dual-beam 1 MeV Kr 2+ and 16 keV He + heavy-ions up to 7 displacements per atom (dpa) with a He/dpa ratio of 0.75 %/dpa using in situ transmission electron microscopy (TEM). Due to the bubble-stabilizing effect of implanted He, bubbles were observed in all irradiations, and populations of faulted interstitial loops were characterized in Cr 18 Fe 27 Mn 27 Ni 28 and Cr 15 Fe 35 Mn 15 Ni 35 . A reduction in swelling was observed in the two CCAs compared to pure Ni and Fe 56 Ni 44 . Although swelling increased from 500 to 600 °C in Fe 56 Ni 44 , Cr 15 Fe 35 Mn 15 Ni 35 and Cr 18 Fe 27 Mn 27 Ni 28 both swelled slightly more at 500 °C. This was attributed to the difference in vacancy mobility, stronger pinning effect of vacancies on He, and the sink strength of faulted dislocation loops. Faulted interstitial loops nucleated with a higher number density and dislocation line density in Cr 15 Fe 35 Mn 15 Ni 35 at both temperatures, and at 600 °C in both materials. The differences in faulted loop population and temperature effect on swelling are correlated to the Mn-content and the measured SFE (20.2 ± 6.7 mJ/m 2 for Cr 18 Fe 27 Mn 27 Ni 28 and 9.2 ± 3.4 mJ/m 2 for Cr 15 Fe 35 Mn 15 Ni 35 ).
36 MATERIALS SCIENCE↗
Unusual nanoscale amorphization of metallic chromium interfacing with SiC under high energy irradiation
Not Available
Quillin, Kyle (ORCID:0000000186684084)↗
Radionuclide tracing based in situ corrosion and mass transport monitoring of 316L stainless steel in a molten salt closed loop
In the study, we report an in situ corrosion and mass transport monitoring method developed using a radionuclide tracing technique for the corrosion study of 316L stainless steel (316L SS) in a NaCl–MgCl 2 eutectic molten salt natural circulation loop. This method involves cyclotron irradiation of a small tube section with 16 MeV protons, later welds at the hot leg of the molten salt flow loop, generating radionuclides 51 Cr, 52 Mn, and 56 Co at the salt–alloy interface. By measuring the activity variations of these radionuclides at different sections along the loop, both the in situ monitoring of the corrosion attack depth of 316L SS and corrosion product transport and its precipitation in flowing NaCl–MgCl 2 molten salt are achieved. While 316L SS is the focus of this study, the technique reported herein can be extended to other structural materials being used in a wide range of industrial applications.
36 MATERIALS SCIENCE↗
In situ synchrotron investigation of tensile deformation and failure mechanisms in cold spray Cr-coated Zr-alloy system
Not Available
11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
Fuel performance analysis of Cr-coated Zircaloy-4 cladding during a prototypical LOCA event using BISON
Here, deformation and failure of chromium (Cr) coated Zircaloy-4 (Zry-4) were studied in loss-of-coolant accident (LOCA) conditions using the BISON fuel performance code. The BISON validation model simulating Halden research reactor experiments was extended to include Cr coatings and higher rod internal pressures to simulate high-burnup fuel. The transient simulations show Cr coatings help relieve stress in the Zry-4 substrate during the transient, delaying the onset of high-temperature creep, which leads to ballooning and bursting of the cladding. A nominal Cr coating thickness of 30 µm delays clad failure by 26 seconds and increases the clad burst temperature by 40 K. A parametric study showed that time to failure and burst temperature both increase with coating thickness, and Cr-coated cladding offers burst resistance under a wide range of rod internal pressures simulating high-burnup fuel. Results indicate that a thin Cr coating provides resistance against ballooning and bursting of cladding during LOCA events.
11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
Development of Corrosion Resistant Coatings for Structural Materials for Liquid Fueled Molten Salts Reactors Applications (Final Report)
Current structural alloys, code certified for the MSRs temperature ranges, contain high levels of chromium, making them highly susceptible to molten halide salt corrosion. One potential solution to circumvent the need for code certification of novel alloys, which is expensive and time consuming, is to design claddings that will protect the underlying code certified materials from corrosion damage during operation. In this work, we examined the corrosion of Ni and Cu electroplated, Ni and CuNi weld overlay, Mo-laser clad, and carburized claddings on SS316H for use in molten salt reactor environments. After characterization of the cladded materials (Task 1), static corrosion tests were used to assess corrosion resistance of the claddings in typical molten fluoride salts (Task 2). The corrosion tests were performed in molten FLiNaK at 700°C up to 1000 hours. Pre- and post-corrosion Scanning Electron Microscopy (SEM), energy-dispersive-spectroscopy (EDS), Transmission Electron Microscopy (TEM), X-ray Diffraction (XRD) and glow-discharge-optical-emission-spectroscopy (GDOES) were performed on cladding cross-sections and surfaces to evaluate degradation. The Cu and Ni electroplated samples, as well as the carburized samples, showed excellent corrosion resistance relative to the bare SS316H. To assess high temperature cladding stability, ageing experiments were performed at temperatures up to 900 C in inert atmosphere for the electroplated and carburized samples and a diffusion model was developed to predict long term cladding behavior (Task 3). It was found that the Cu cladding was basically insensitive to the high temperature ageing, except for small secondary phases forming at the interface. On the other hand, the Ni electroplated cladding experienced significant interdiffusion. Nevertheless, the gain in corrosion resistance for a 100μm Ni electroplated cladding is phenomenal, with more than 50% reduction in chromium dissolution from the substrate material for the first 15 years of salt exposure at 700°C. To assess radiation resistance and phase stability, high-temperature 4MeV Ni heavy ion irradiation was performed across the cladding/substrate interface up to 50 displacement-per-atom (DPA) at 500°C and 700°C to assess the phase stability and irradiation behaviors of the electroplated systems (Task 4). The Ni and Cu electroplated systems did not experience void swelling at the contrary to the SS316H substrate due to their nanocrystalline nature. Some level of recrystallization was observed in the cladding, as well as radiation induced segregation and enhanced diffusion. The interface acted as a potent sink for point defects with the presence of a void denuded zone. The mechanical properties of the claddings were assessed using thermal shock, micro-indentation, nano-indentation, and four-point bend testing experiments (Task 5). These experiments were performed on the claddings in as-received, corroded, irradiated, and thermally aged states to determine the effects of typical molten salt reactor environments on cladding integrity. No significant mass loss was observed after repeated thermal shocks. While the electroplated samples softened after high-temperature ageing, irradiation hardening compensate this effect, such that there is little different with the as-received materials. The results of these experiments suggest that the electroplated (copper/nickel) show the greatest promise for application in molten salt reactor development. These claddings prevented any chromium dissolution from occurring during the static corrosion experiments. Additionally, they demonstrated favorable properties for high temperature diffusion, phase stability, interfacial mechanical properties, and irradiation resistance. Weld-overlay cladding are also of great interest and could reach properties similar to the electroplated samples upon optimization (especially with multiple weld passes). The carburized SS316H showed excellent behavior as well, but more work needs to be done to assess their long-term stability. Finally, the Mo-laser clad system was not pursued further due to the manufacturing challenges. It is also worth noting that the Ni cladding systems should behave relatively well in terms of weldability since the Ni-weld overlay microstructure and associated corrosion rate are sound. While the NiCu weld-overlay has even lower corrosion rates than the Ni-weld overlay, more studies on welding of Cu-electroplated systems are necessary since Cu clusters are known to embrittle steels.
36 MATERIALS SCIENCE↗
Radius of Contact During Friction Surfacing of Stainless Steel 304L: Effect of Spindle Speed and Rod Diameter
Abstract The “radius of contact” or the “real-rotational contact plane,” has been increasingly mentioned terminology in friction surfacing. However, the fundamental understanding of the flow dynamics behind this phenomenon is still very limited. The goal of this study was to understand the influence of spindle speed and consumable rod diameter on the flow dynamics and the radius of contact during friction surfacing of 304L stainless steel over a substrate of the same material. Friction surfacing was performed using consumable rods with diameters of 4.76 mm, 9.52 mm, and 12.7 mm while using spindle speeds from 1500 rpm to 20,000 rpm. The impact of spindle speed on deposition morphology, including the radius of contact, was studied. The radius of contact was calculated empirically and was found to be inversely proportional to the tangential velocity of the rod. The coupling between flow stresses and localized forces is hypothesized to be the key factor behind the variation of the radius of contact with processing conditions.
Engineering↗
Initial study on thermal stability of cold spray tantalum coating irradiated with deuterium for fusion applications
Abstract Removal of neutral hydrogen atoms in the plasma edge reduces the number of charge exchange events and thus, the net energy losses in the plasma, significantly improving performance of fusion devices. Effective control of the residual pressure of hydrogen isotopes (HIs) in the plasma edge may be achieved by utilizing a hydrogen absorbing first wall interface capable of withstanding the harsh fusion environment. In this study, we have investigated tantalum (Ta) coating deposited by cold spray technology on 316L stainless steel substrate as a potential plasma-facing material surface. High fluence low energy deuterium plasma irradiation experiments and subsequent thermal annealing cycles associated with thermal desorption spectrometry (TDS) demonstrated superior structural stability of the Ta coating. TDS experiments revealed the outgassing of deuterium (as measure of its retention) for cold spray Ta coatings to be three times higher than bulk Ta and two orders of magnitude greater than bulk polycrystalline W. X-ray photoelectron spectroscopy revealed evolution of oxidation states upon deuterium irradiation and a partial recovery of the metallic signature of Ta after the thermal treatment at 1100 K.
Physics↗
Effects of elevated temperature exposure on the residual stress state and microstructure of PVD Cr coatings on SiC investigated via in situ X-ray diffraction and transmission electron microscopy
Pure Cr coatings are being considered as corrosion-resistant layers for SiC-SiC f composite fuel cladding in light water reactors. The residual stress state and interdiffusion behavior of Cr coatings deposited on SiC substrates using bipolar high-power impulse magnetron sputtering (B-HiPIMS) and direct current impulse magnetron sputtering (DCMS) were studied using in situ X-ray diffraction experiments at 300 °C, 700 °C, and 1200 °C. After elevated temperature exposure, evolution of the coating microstructure and coating/substrate interdiffusion was characterized by transmission electron microscopy. The compressive residual stress of the dense B-HiPIMS coating at room temperature was gradually relieved at 300 °C, while the stress transitioned to a tensile state at 700 °C. Grain growth of the Cr coating and a Cr–SiC interdiffusion layer consisting of newly formed Cr–C and Cr–Si phases were observed in the B-HiPIMS coating after exposure at 700 °C. The phases in the interdiffusion layer were identified to be Cr 7 C 3 , Cr 3 Si, and Cr 5 Si 3 C x experimentally and by thermodynamic predictions. For the DCMS coating, however, changes in residual stress and microstructure at the elevated temperatures were limited by the inherent porosity and inhomogeneous structure of the as-deposited coating. At 1200 °C, both coating types interacted rapidly with the underlying SiC substrate in the early stages of the experiment. The results from this study suggest that the characteristics of the Cr coatings do not significantly change at the reactor operating temperature of 300 °C, while changes in microstructure and stress state are expected in off-normal conditions of 700 °C and 1200 °C. Finally the results from this study suggest the B-HiPIMS coating is best-suited as a protective coating for SiC fuel cladding.
36 MATERIALS SCIENCE↗
Activity gradient mass transport accelerated corrosion of stainless steel in molten salt
Advanced energy systems based on molten salt technologies have gained increasing interest, and their design and construction are likely going to involve the use of materials of dissimilar chemistries. With dissimilar materials being used, galvanic coupling induced corrosion acceleration is one of the mechanisms believed to be an issue for the deployment of molten salt systems. However, non-galvanic interaction mechanisms such as activity gradient mass transport have also been theorized to represent a potential challenge. Unfortunately, the two effects have often been compounded in the literature, such that it is still unclear which degradation mechanisms are at play in these systems. In the following study, electrochemical measurements are used to predict the effect that galvanic coupling would have on dissimilar materials submerged in the same molten salt medium. Dissimilar material salt exposure tests are then performed to investigate whether galvanic coupling or activity gradient driven processes account for the levels of materials degradation observed. Finally, these separate effect electrochemical and corrosion experiments uniquely elucidate the degradation mechanisms in dissimilar materials systems.
36 MATERIALS SCIENCE↗
Novel pyrolytic boron nitride coating to reduce graphite interactions in molten fluoride salt
Future salt reactors like the Fluoride-salt-cooled-High Temperature Reactor require varying material flavors. Graphite is required for neutron moderation and potential fuel forms, while structural metals are required for containment. Studies show graphite/metal interactions exist when both materials share a salt medium. These interactions may accelerate the corrosion of the metal and change the surface of graphite materials. A novel pyrolytic boron nitride coating on graphite is investigated for reducing graphite/metal interactions. Finally, this is the first known application of such a coating, and salt exposure tests reveal the pyrolytic boron nitride coating reduces the interactions between stainless steel and uncoated graphite.
21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗
Corrosion of 316L & 316H stainless steel in molten LiF-NaF-KF (FLiNaK)
The corrosion behavior of 316L and 316H stainless steels (low and high carbon, respectively) in molten LiF-NaF-KF (FLiNaK) salt at 700 °C for 500 h has been investigated. Tests were performed in 316L stainless steel, pyrolytic boron nitride, and glassy carbon capsule materials. The capsule material had a notable effect on the corrosion behavior of the two stainless steels. Further, the modes of corrosion for the two types of stainless steel in various capsule materials were classified into three categories, namely, uniform surface recession, selective grain boundary Cr dissolution, and the dissolution of Cr in the bulk grains. By most metrics, the 316H stainless steel exhibited slightly superior corrosion resistance, while by others the two stainless steels were comparable. These differences in corrosion behavior are attributed to the differences in grain size and the degree of sensitization.
36 MATERIALS SCIENCE↗
Accelerated Materials Design for Molten Salt Technologies Using Innovative High-Throughput Methods
The focus of the project is on building an innovative accelerated materials design platform for molten salt technologies using novel high-throughput methods coupled to data analytics. The main objectives is to predict a FeCrMnNi alloy compositional space with better corrosion resistance than stainless steel 316 and identify new molten salt corrosion mechanisms. The project demonstrates the feasibility to use high-throughput methods coupled to data analytics to accelerate alloy design for extreme environments applications. Using a trained and tested machine learning (ML) model, 2000 FeCrMnNi alloy corrosion rate in molten chloride salts were predicted and a compositional field with corrosion rate lower than 316 stainless steel was identified. The ML model interpretability unveiled multiple features of importance in the model prediction. Some features were expected to be of relative significance, such as work function, surface energy and alloy electronegativity, and the ML model interpretability analysis confirmed those. On the other hand, the most important feature is the diffusion coefficient of Ni in the bulk alloy which indicates that a surface diffusion mechanism plays an important role in the overall corrosion mechanism in molten salts.
36 MATERIALS SCIENCE↗
Novel effects of grain size and ion implantation on grain boundary segregation in ion irradiated austenitic steel
Nuclear reactor environments are extreme in nature due to the combination of exposure to corrosive coolant, mechanical stresses, and neutron irradiation damage. This combination of environments can lead to irradiation induced/assisted precipitation, segregation, and embrittlement coupled with enhanced creep and stress corrosion cracking. While nanostructured materials are of interest in a variety of applications due to their unique properties including high mechanical strength, for nuclear applications nanostructured materials have the added benefit of irradiation resistance due to the high volume density of sinks for irradiation-induced defects. In this study, we show unique radiation-induced segregation (RIS) behavior in nanocrystalline 304 stainless steel (SS304). Typical RIS in austenitic steels includes Ni enrichment and Cr depletion within the grain boundaries. In nanostructured SS304 this RIS is reduced. Furthermore, interestingly, some grain boundaries in the nanocrystalline SS304 in this study were found to be enriched in Cr after Fe 2+ ion irradiation at 500 °C up to 50 displacements per atom (dpa). To understand this unique observation, lattice-based atomic kinetic Monte Carlo simulations were performed to investigate the effects of grain size, thermal segregation, as well as injected interstitials (introduced as Fe self-ions). The results indicate that the Cr enrichment at grain boundaries may be caused by combined effects of grain size, self-ion injection and preferential Cr diffusion via the interstitial mechanism. In conclusion, the findings also suggest a possible difference in RIS between ion and neutron irradiations.
36 MATERIALS SCIENCE↗
Cold spray manufacturing of oxide-dispersion strengthened (ODS) steels using gas-atomized and ball-milled 14YWT powders
The cold spray deposition process has been investigated for the manufacture of 14YWT oxide-dispersion strengthened (ODS) steel, a nanostructured ferritic alloy (NFA), using gas-atomized and ball-milled feedstock powders. Cold spraying of the gas-atomized powder resulted in a thick dense deposit, but annealing them above 900 °C induced grain growth and heterogeneous precipitation of nanoparticles, thus resulting in lower hardness (~ 170 HV) compared to 14YWT ODS steel manufactured by the conventional method. The ball-milled powder (Fe-14Cr-3W-0.4Ti-0.2Y-0.125O) was cryomilled in liquid N 2 to achieve small particle sizes followed by annealing in a H 2 /Ar environment at 1000 °C and 1100 °C to reduce the hardness from ~ 8 GPa to ~ 5 GPa. Both smaller particle sizes and lower hardness of annealed powders made them amenable to the cold spray deposition process, resulting in thick and dense deposits, while retaining the favorable fully solutionized microstructure of the ball-milled powders. The microstructure of the as-deposited ODS exhibited very fine grain sizes (50–250 nm) with a uniform dispersion of Y-Ti-O nanoprecipitates in the ferritic steel matrix. The hardness values of the cold spray deposits using the powders annealed at 1000 °C and 1100 °C was 770 HV and 496 HV, respectively. Post-heat treatment of the as-deposited material up to 1100 °C showed a high-density microstructure with uniformly dispersed nanoscale oxide particles. The hardness of the annealed deposits up to 1000 °C had a notably higher hardness than bulk 14YWT ODS steel manufactured by conventional methods. The study demonstrates that cold spray deposition of the microstructurally-tailored feedstock powders can be used to successfully manufacture ODS steel with microstructure and properties comparable to those produced by the conventional methods, while providing for an attractive option for the more rapid and cost-effective manufacturing of ODS steel cladding tubes.
14YWT↗
An electrochemical mesoscale tool for modeling the corrosion of structural alloys by molten salt
Understanding the impact of microstructure on corrosion rates can aid the development of corrosion-resistant alloys for molten salt reactors. Here in this work, we develop an electrochemical phase-field model for capturing the microstructure-dependent corrosion of structural alloys by molten salts. As a demonstration problem, we apply this model to capture the selective depletion of Cr from Ni-Cr grain boundaries during corrosion in molten FLiBe salt. We perform sensitivity analysis and model verification on 1D simulations to confirm that the model predicts diffusion-limited kinetics. The model is validated using 1D, 2D, and 3D simulations against experimental data for Ni-5Cr and Ni-20Cr corrosion in molten FLiBe. The 1D simulations predict the corrosion behavior with reasonable accuracy when using an effective diffusion coefficient that accurately represents the grain boundary diffusion. 2D simulations that represent the grain structure underpredict the corrosion. 3D simulations that represent the grain structure predict the corrosion with reasonable accuracy. The corrosion rate predicted by the 3D simulations is proportional to the average grain size at the alloy/salt interface.
11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗