NASA NTRS2019

Heatshield for Extreme Entry Environment Technology (HEEET) Thermal Protection System (TPS)

Starting in 2013 and completing in 2019, the Heatshield for Extreme Entry Environment Technology (HEEET) project has been working to mature a 3-D Woven Thermal Protection System (TPS) to Technical Readiness Level (TRL) 6 to support future NASA missions to destinations with extreme entry environments such as Venus, Saturn, Uranus, Neptune and high-speed sample return missions to Earth. A key aspect of the project has been the building and testing of a 1-meter base diameter Engineering Test Unit (ETU) representative of what could be used for a Saturn probe. This paper provides a high-level overview of the HEEET project including manufacturing and testing of the ETU for structural model verification, establish system capability and verify manufacturing workmanship.

Extreme Entry Environment↗

NASA NTRS2018

Remote Recession Measurements of Wire-Seeded PICA Samples in an Arc-Jet Flow

Various methods for remote recession sensing of PICA have been developed and several seeding methods have been tested. The most recent method involved seeding the ablator with wires fed to the sample from the backside with a defined amount of PICA left towards the upstream front of the sample. This seed method mimics the installation of in-depth thermocouples as they are frequently used in ground testing and flight. Arc-jet tests were conducted in the NASA Langley HYMETS facility at a heat flux of 320 W/sq.cm. The emission of the post-shock layer was observed in spectral resolution from the side along an optical axis perpendicular to the arc-jet flow and from the front, looking at the sample surface from an upstream position. Various metallic seed materials with different melting points were used. In addition to the emission spectroscopy measurements, the samples were monitored during the tests through pyrometry and videography. The time resolved response of the seeded material is described and compared to earlier tests with different seeding methods. The combination of seed materials was found to be critical for the selection of emission signatures characteristic for the material recession which can be isolated in the final emission spectra.

Winter, Michael↗

NASA NTRS2017

Progress Report on PICA Activities in Support of New Frontiers Missions

Phenolic Impregnated Carbon Ablator (PICA) is a TPS material that has been used in a number of previous flight missions (Stardust, MSL) and is planned for a number of future missions (OSIRIS-Rex and Mars 2020) so it has substantial flight heritage, is applicable to a wide range of missions, and is often baselined as the TPS in future NASA proposal activities. As is common with a number of TPS materials, PICA faces a supply chain issue with the rayon precursor from which the carbon fibers used in the PICA preform are derived. PICA uses a non-woven form of the rayon, which once carbonized, is used in the low-density carbon FiberForm (carbon tile) preform utilized in PICA. Current PICA uses a NASA-qualified non-domestic rayon supplier (Sniace), however the qualified supplier is no longer manufacturing the rayon materials. This activity will address PICA sustainability, by initially carbonizing the remaining stockpile of Sniace rayon precursor. A additional FiberForm manufacturing task from alternate rayon sources is also in progress.

thermal protection↗

NASA NTRS2016

Development of Advanced Conformal Ablative TPS Fabricated from Rayon- and PAN-Based Carbon Felts

The conformal ablative TPS first developed under NASA's Hypersonics Project in the early 2000's demonstrated very low through the thickness conductivity compared to state-ofthe- art PICA. However, in initial arcjet testing of Conformal-1, surface recession rates were 2x higher than PICA. Because commercial carbon felts are currently available as very thin substrates, this was a concern if conformal TPS were to be considered for a mission that required thicker material. Discussed in this paper are the results of the development of an Advanced Conformal TPS derived from thicker, higher density carbon felt. Two substrate systems were evaluated, the first material was a needled rayon-based carbon felt and the other a needled PAN-based carbon felt. Both substrates were impregnated with phenolic resin following the PICA/CPICA process to add a low density phenolic matrix to the system prior to aerothermal screening at the LaRC HyMETS facility and larger scale testing in the NASA ARC Interaction Heating Facility (IHF) at heating fluxes ranging from 250-1700 W/cm2.

Arcjet Testing↗

NASA NTRS2016

Characterization of Candidate Materials for Remote Recession Measurements of Ablative Heat Shield Materials

A method of remotely measuring surface recession of a material sample in a plasma flow through emission spectroscopy of the post shock layer was characterized through experiments in the NASA Langley HYMETS arc jet facility. Different methods for delivering the seed products into the Phenolic Impregnated Carbon Ablator (PICA) material samples were investigated. Three samples were produced by seeding the PICA material with combinations of Al, Si, HfO2, VB2, Al2O3, SiO2, TiC, HfC, NaCl, and MgCl2 through infusing seed materials into a core of PICA, or through encapsulating seed material in an epoxy disk, mechanically bonding the disk to a PICA sample. The PICA samples seeded with the candidate tracers were then tested at surface temperatures near 2400 K under low pressure air plasma. The emission of Al, Ti, V, Na, and Mg in the post-shock layer was observed in the UV with a high resolution imaging spectrometer viewing the whole stagnation line from the side, and from UV to NIR with a fiber-coupled miniaturized spectrometer observing the sample surface in the wavelength range from 200 nm to 1,100 nm from the front through a collimator. Al, Na, and Mg were found to be emitting in the post-shock spectra even before the recession reached the seeding depth - therefore possibly characterizing the pyrolysis process rather than the recession itself. The appearance of Ti and V emission in the spectra was well correlated with the actual recession which was monitored through a video of the front surface of the sample. The applicability of a seed material as an indicator for recession appears to be related to the melting temperature of the seed material. Future parametric studies will be carried out in low power plasma facilities at the University of Kentucky.

Butler, Bradley D.↗

NASA NTRS2014

Remote Recession Sensing of Ablative Heat Shield Materials

Tests were performed to demonstrate the feasibility of a new method of measuring surface recession of a material sample during arc-jet testing in the NASA Ames mARC subscale developmental facility. The measurement principle was inspired through tracer elements such as Ca and Na which were seen in the spectra taken during the airborne observation campaign of the Stardust re-entry and which could be clearly observed standing out against the emission spectra emitted by postshock layer and glowing surface of the re-entry capsule. The measurement principle involves seeding of the heat shield materials at a defined depth with tracer elements which show strong and characteristic emission lines in the post shock plasma. Once the material recession reaches the seeding depth, these elements get into the hot plasma and show up in the emission spectra. The methodology was successfully demonstrated during arc-jet testing of phenolic impregnated carbonablator (PICA) material which was seeded in depth with a mixture of NaCl and MgCl in powder form. In the emission spectroscopy data, the emission lines of Mg and Na showed up about 1.5 seconds after probe insertion into the arc-jet plasma and vanished after another 2.5 seconds when recessionhad consumed the seeding material. From these data, a recession rate of about 1 mm/s is estimated.The heat flux during the test was measured to be 2575 W/sq cm on a hemispherical heat flux probewhich corresponds to a heat flux of 1036 W/sq cm on the rectangular test articles. An estimate for a lower limit of the surface temperature of 2800K during the test was obtained by fitting Planck radiation to the continuum spectra emitted by the PICA sample. Typical recession rates of PICA during testing in the large arc-jet facilities at similar test conditions are reported to be on the order of 0.05 to 0.1 cm/s which agrees well with the recession rates of 0.05-0.06 cm/s estimated from the emission spectroscopy data. Further tests under better controlled conditions are suggested to quantify this measurement method. Through a different choice of seeding materials with lower melting point, an extension of the measurement principle to monitor char depth seems feasible but was not yet demonstrated. Possible applications besides ground testing are recession and possibly char depth measurements during real re-entry. Detection through emission spectroscopy could be accomplished through ground based or airborne observation as performed during the Stardust and Hayabusa re-entries, or through on-board spectrometers. A suitable mission would be the re-entryof the OSIRIS-REX mission planned for late 2023. The measured data are presented and interpreted, the results and details of future applications are discussed.

instrumentation↗

NASA NTRS2014

Remote Recession Sensing of Ablative Heat Shield Materials

Material recession and charring are two major processes determining the performance of ablative heat shield materials. Even in ground testing, the characterization of these two mechanisms relies on measurements of material thickness before and after testing, thus providing only information integrated over the test time. For recession measurements, optical methods such as imaging the sample surface during testing are under investigation but require high alignment and instrument effort, therefore being not established as a standard measurement method. For char depth measurements, the most common method so far consists in investigation of sectioned samples after testing or in the case of Stardust where core extractions were performed to determine char information. In flight, no reliable recession measurements are available, except total recession after recovering the heat shield on ground. Developments of mechanical recession sensors have been started but require substantial on board instrumentation adding mass and complexity. In this work, preliminary experiments to evaluate the feasibility of remote sensing of material recession and possibly char depth through optically observing the emission signatures of seeding materials in the post shock plasma is investigated. It is shown that this method can provide time resolved recession measurements without the necessity of accurate alignment procedures of the optical set-up and without any instrumentation on board of a spacecraft. Furthermore, recession data can be obtained without recovering flight hardware which would be a huge benefit for inexpensive heat shield material testing on board of small re-entry probes, e.g. on new micro-satellite re-entry probes as a possible future application of Cubesats or RBR

instrumentation↗

NASA NTRS2013

Woven Thermal Protection System Based Heat-shield for Extreme Entry Environments Technology (HEEET)

NASA's future robotic missions utilizing an entry system into Venus and the outer planets, namely, Saturn, Uranus, Neptune, result in extremely high entry conditions that exceed the capabilities of state of the art low to mid density ablators such as PICA or Avcoat. Therefore mission planners typically assume the use of a fully dense carbon phenolic heat shield similar to what was flown on Pioneer Venus and Galileo. Carbon phenolic is a robust TPS material however its high density and relatively high thermal conductivity constrain mission planners to steep entries, with high heat fluxes and pressures and short entry durations, in order for CP to be feasible from a mass perspective. The high entry conditions pose challenges for certification in existing ground based test facilities and the longer‐term sustainability of CP will continue to pose challenges. In 2012 the Game Changing Development Program (GCDP) in NASA's Space Technology Mission Directorate funded NASA ARC to investigate the feasibility of a Woven Thermal Protection System (WTPS) to meet the needs of NASA's most challenging entry missions. This project was highly successful demonstrating that a Woven TPS solution compares favorably to CP in performance in simulated reentry environments and provides the opportunity to manufacture graded materials that should result in overall reduced mass solutions and enable a much broader set of missions than does CP. Building off the success of the WTPS project GCDP has funded a follow on project to further mature and scale up the WTPS concept for insertion into future NASA robotic missions. The matured WTPS will address the CP concerns associated with ground based test limitations and sustainability. This presentation will briefly discuss results from the WTPS Project and the plans for WTPS maturation into a heat‐shield for extreme entry environment.

Ellerby, Donald↗

NASA NTRS2012

Development of Matrix Microstructures in UHTC Composites

One of the major issues hindering the use of ultra high temperature ceramics for aerospace applications is low fracture toughness. There is considerable interest in developing fiber-reinforced composites to improve fracture toughness. Considerable knowledge has been gained in controlling and improving the microstructure of monolithic UHTCs, and this paper addresses the question of transferring that knowledge to composites. Some model composites have been made and the microstructures of the matrix developed has been explored and compared to the microstructure of monolithic materials in the hafnium diboride/silicon carbide family. Both 2D and 3D weaves have been impregnated and processed.

Johnson, Sylvia↗

NASA NTRS2011

Microstructure of Matrix in UHTC Composites

Approaches to controlling the microstructure of Ultra High Temperature Ceramics (UHTCs) are described.. One matrix material has been infiltrated into carbon weaves to make composite materials. The microstructure of these composites is described.

Johnson, Sylvia↗

NASA NTRS2011

PICA Variants with Improved Mechanical Properties

Phenolic Impregnated Carbon Ablator (PICA) is a member of the family of Lightweight Ceramic Ablators (LCAs) and was developed at NASA Ames Research Center as a thermal protection system (TPS) material for the Stardust mission probe that entered the Earth s atmosphere faster than any other probe or vehicle to date. PICA, carbon fiberform base and phenolic polymer, shows excellent thermal insulative properties at heating rates from about 250 W/sq cm to 1000 W/sq cm. The density of standard PICA - 0.26 g/cu cm to 0.28 g/cu cm - can be changed by changing the concentration of the phenolic resin. By adding polymers to the phenolic resin before curing it is possible to significantly improve the mechanical properties of PICA without significantly increasing the density.

Thornton, Jeremy↗

NASA NTRS2001

Processing and Properties Of Refractory Zirconium Diboride Composites For Use In High Temperature Applications

The Thermal Protection Materials and Systems Branch at NASA Ames Research Center is involved in the development of a class of refractory oxidation-resistant diboride composites termed Ultra High Temperature Ceramics or UHTCs. These composites have good high temperature properties making them candidate materials for thermal protection system (TPS) applications. The current research focuses on improving processing methods to develop more reliable composites with enhanced thermal and mechanical properties. This presentation will concentrate on the processing of ZrB2/SiC composites. Some preliminary mechanical properties and oxidation data will also be presented.

Stackpoole, Margaret↗