Engineering topics
Publications and source records attributed to Stadie, Nicholas P..
A halide-free route to the synthesis of graphitic BC 3 was discovered via decomposition temperature matching: benzene (C 6 H 6 ) as the carbon precursor and the borohydride anion (BH 4 − ) as the boron precursor.
In this work, we utilized an ultramicroporous metal–organic framework (MOF) named [Ni 3 (pzdc) 2 (ade) 2 (H 2 O) 4 ]·2.18H 2 O (where H 3 pzdc represents pyrazole-3,5-dicarboxylic acid and ade represents adenine) for hydrogen (H 2 ) adsorption. Upon activation, [Ni 3 (pzdc) 2 (ade) 2 ] was obtained, and in situ carbon monoxide loading by transmission infrared spectroscopy revealed the generation of open Ni(II) sites. The MOF displayed a Brunauer–Emmett–Teller (BET) surface area of 160 m 2 /g and a pore size of 0.67 nm. Hydrogen adsorption measurements conducted on this MOF at 77 K showed a steep increase in uptake (up to 1.93 mmol/g at 0.04 bar) at low pressure, reaching a H 2 uptake saturation at 2.11 mmol/g at ~0.15 bar. The affinity of this MOF for H 2 was determined to be 9.7 ± 1.0 kJ/mol. In situ H 2 loading experiments supported by molecular simulations confirmed that H 2 does not bind to the open Ni(II) sites of [Ni 3 (pzdc) 2 (ade) 2 ], and the high affinity of the MOF for H 2 is attributed to the interplay of pore size, shape, and functionality.
Despite great efforts to achieve ideal atomistic packing of carbon in the pore networks of even the largest pore zeolites, templating inaccuracies are ubiquitous in all presently synthesized zeolite-templated carbon (ZTC) materials. Idealized models suggest that the long-sought schwarzite-like structures could in principle be obtained by zeolite templating if the appropriate zeolite template were chosen (e.g., faujasite for D surface schwarzites) and if perfect template fidelity (insertion of a pristine layer of pure carbon directly on the surface of the zeolite) could be achieved. A requirement to achieve such structures is increased carbon density within the zeolite. We report the investigation of a series of alkali metal cation-exchanged zeolites to determine how the periodic trends in the group 1 elements influence zeolite templating, with a specific focus on the metric of structural packing density (SPD) as resolved by ex situ thermogravimetry. In a survey based on controlled synthesis temperature, time, and flow conditions, an increasing SPD was observed with decreasing cation size, an effect that is consistent with the increasing strength of cation-π interactions. Furthermore, this effect could be promising for future work to increase the SPD of ZTCs for the synthesis of closed-tube, schwarzite-like carbonaceous solids.
Zeolite-templated carbon (ZTC) is a unique porous carbonaceous material whose structure is ordered at the nanometre scale, enabling a representative periodic description at the atomistic level. Utilizing an existing, well-defined reference model for ZTCs, a structural library of varying compositions was developed by refinement using density-functional tight-binding (DFTB) potentials parameterized for materials science applications. We first determined the quantum chemical-refined structures of models with CH, CHO, CHON, CHOB, and CHOBN compositions with various degrees of heteroatom substitution. These structural models comprise the characteristic morphological features of highly porous carbon materials, such as open-blade surfaces, edges, saddles, and closed-strut formations, spanning a range of curvatures and characteristic sizes. Second, we carried out alternating compression and expansion of the CHO model unit cell to determine the lowest energy structure as well as to obtain its bulk modulus in order to demonstrate a close connection between macroscopic observations and atomic-scale structures. Further, the agreement between experimental measurements and the computational model is remarkable and demonstrates the power of approximate density functional theory as a cost-effective computational tool with chemical accuracy for the investigation of structure/property relationships in real-world carbon-based solids.
Incorporation of heteroatoms in carbon materials is commonly expected to influence their physical or chemical properties. Furthermore, contrary to previous results for methane adsorption, no technologically significant effect was identified for the hydrogen physisorption energies (measured 4.1–4.6 kJ mol –1 and calculated q st = –ΔH ads = 4.1 ± 0.7 kJ mol –1 using a comprehensive set of levels of theory) as a function of B- and N-substitution of a mid-plane C-site on open carbon surfaces.
Experimental and theoretical studies disagree on the energetics of methane adsorption on carbon materials. However, this information is critical for the rational design and optimization of the structure and composition of adsorbents for natural gas storage. The delicate nature of dispersion interactions, polarization of both the adsorbent and the adsorbate, interplay between H-bonding and tetrel bonding, and induced dipole/Coulomb interactions inherent to methane physisorption require computational treatment at the highest possible level of theory. In this study, we employed the smallest reasonable computational model, a maquette of porous carbon surfaces with a central site for substitution and methane binding. The most accurate predictions of methane adsorption energetics were achieved by electron-correlated molecular orbital theory CCSD(T) and hybrid density functional theory MN15 calculations employing a saturated, all-electron basis set. Here, the characteristic geometry of methane adsorption on a carbon surface (“lander approach”) arises due to bonding interactions of the adsorbent π-system with the proximal H–C bonds of methane, in addition to tetrel bonding between the antibonding orbital of the distal C–H bond and the central atom of the maquette (C, B, or N). The polarization of the electron density, structural deformations, and the comprehensive energetic analysis clearly indicate a ∼3 kJ mol –1 preference for methane binding on the N-substituted maquette. The B-substituted maquette showed a comparable or lower binding energy than the unsubstituted, pure C model, depending on the level of theory employed. The calculated thermodynamic results indicate a strategy for incorporating electron-enriched substitutions (e.g., N) into carbon materials as a way to increase methane storage capacity over electron-deficient (e.g., B) modifications. The thermochemical analysis was revised for establishing a conceptual agreement between the experimental isosteric heat of adsorption and the binding enthalpies from statistical thermodynamics principles.
Sorption enhanced methanol production makes use of the equilibrium shift of the CO 2 hydrogenation reaction towards the desired products. However, the increased complexity of the catalyst system leads to additional reactions and thus side products such as dimethyl ether, and complicates the analysis of the reaction mechanism. On the other hand, the unusually high concentration of intermediates and products in the sorbent facilitates the use of inelastic neutron scattering (INS) spectroscopy. Despite being a post-mortem method, the INS data revealed the change of the reaction path during sorption catalysis. Concretely, the experiments indicate that the varying water partial pressure due to the adsorption saturation of the zeolite sorbent influences the progress of the reaction steps in which water is involved. Experiments with model catalysts support the INS findings.
Physical adsorption remains a promising method for achieving fast, reversible hydrogen storage at both ambient and cryogenic conditions. Research in this area has recently shifted to focus primarily on the volumetric (H 2 stored/delivered per volume) gains achieved within an adsorptive storage system over that of pure H 2 compression; however, the methodology for estimating a volumetric stored or delivered amount requires several assumptions related to the ultimate packing of the adsorbent material into an actual storage system volume. In this work, we critically review the different assumptions commonly employed, and thereby categorize and compare the volumetric storage and delivery across numerous different porous materials including benchmark metal-organic frameworks, porous carbons, and zeolites. In several cases, there is a significant gain in both storage and delivery by the addition of an adsorbent to the high-pressure H 2 storage system over that of pure compression, even at room temperature. Lightweight, low-density materials remain the optimal adsorbents at low temperature, while higher density, open metal-containing frameworks are necessary for high-density room temperature storage and delivery.
In this work, bulk turbostratic graphitic carbon of varying levels of disorder and chemical compositions has been synthesized by a direct synthesis method in the temperature range of 750–1100 °C, with a focus on boron incorporation within the graphitic lattice. The atomistic and electronic/vibrational structures were characterized by X-ray diffraction, energy-dispersive X-ray spectroscopy, Auger electron spectroscopy, X-ray absorption spectroscopy, and Raman spectroscopy. The phonon dispersion relation of graphitic carbon was found to be uniquely sensitive to substitutional boron doping, which perturbs the phonon structure while leaving the lattice structure unchanged. The dispersion relation of the D peak measured by Raman spectroscopy can be used to uniquely identify bulk graphitic materials containing a large content of ordered trigonal planar g-BC 3 units, which are of high interest in applications ranging from hydrogen storage to lithium-ion batteries.