Revisiting metal fluorides as lithium-ion battery cathodes
Metal fluorides, promising lithium-ion battery cathode materials, have been classified as conversion materials due to the reconstructive phase transitions widely presumed to occur upon lithiation. We challenge this view by studying FeF 3 using X-ray total scattering and electron diffraction techniques that measure structure over multiple length scales coupled with density functional theory calculations, and by revisiting prior experimental studies of FeF 2 and CuF 2 . Metal fluoride lithiation is instead dominated by diffusion-controlled displacement mechanisms, and a clear topological relationship between the metal fluoride F- sublattices and that of LiF is established. Initial lithiation of FeF3 forms FeF2 on the particle's surface, along with a cation-ordered and stacking-disordered phase, A-Li x Fe y F 3 , which is structurally related to alpha-/beta-LiMn 2+ Fe 3+ F 6 and which topotactically transforms to B- and then C-Li x Fe y F 3 , before forming LiF and Fe. Lithiation of FeF 2 and CuF 2 results in a buffer phase between FeF 2 /CuF 2 and LiF. Overall, the resulting principles will aid future developments of a wider range of isomorphic metal fluorides.