Nanotomographic observation and statistical analysis of overcharging induced cracks in LiCoO 2 single crystalline particles
Particle fracture represents an important mode of battery electrode degradation. Extensive cracking occurs in the layered oxide cathodes of lithium-ion rechargeable batteries when they are charged beyond safe operational voltages. In this paper, we analyze the morphology and distribution of cracks in over 100 overcharged LiCoO 2 (LCO) single-crystalline particles imaged via X-ray nanotomography. Herein, we observe a strong particle size dependence in both nucleation and growth of cracks, with percentage of cracked particles, crack size, and crack surface area per unit volume all increasing significantly with particle volume. Increasing the cutoff voltage above 4.6V is found to trigger much more pronounced crack growth, which we attribute to the large misfit stress caused by the H1-3 to O1 phase transition. This study offers valuable statistical insights into the fracture behavior of layered oxide cathodes and reveals the importance of particle size control on electromechanical degradation of battery electrodes.
A stable cathode-solid electrolyte composite for high-voltage, long-cycle-life solid-state sodium-ion batteries
Rechargeable solid-state sodium-ion batteries (SSSBs) hold great promise for safer and more energy-dense energy storage. However, the poor electrochemical stability between current sulfide-based solid electrolytes and high-voltage oxide cathodes has limited their long-term cycling performance and practicality. Here, we report the discovery of the ion conductor Na 3-x Y 1-x Zr x Cl 6 (NYZC) that is both electrochemically stable (up to 3.8 V vs. Na/Na + ) and chemically compatible with oxide cathodes. Its high ionic conductivity of 6.6 × 10 –5 S cm –1 at ambient temperature, several orders of magnitude higher than oxide coatings, is attributed to abundant Na vacancies and cooperative MCl 6 rotation, resulting in an extremely low interfacial impedance. A SSSB comprising a NaCrO 2 + NYZC composite cathode, Na 3 PS 4 electrolyte, and Na-Sn anode exhibits an exceptional first-cycle Coulombic efficiency of 97.1% at room emperature and can cycle over 1000 cycles with 89.3% capacity retention at 40 °C. These findings highlight the immense potential of halides for SSSB applications.