DOE OSTI2022

Vitrification of Hanford Tank 241-AP-101 Waste and Simulant

Hanford tank 241-AP-101 (referred to herein as AP-101) is the second Hanford radioactive tank waste planned to be processed and vitrified. A simulant version of AP 101 waste was formulated from the best-basis inventory (BBI) for the Hanford Tank 241-AP-101 liquid with an assumed target dilution of the waste from the BBI sodium molarity of 8.61 M to the desired 5.5 M Na. After the addition of glass-forming chemicals (GFCs), the simulant melter feed was processed in a non-radioactive, continuous laboratory-scale melter (CLSM) system. The AP-101 simulant melter feed was charged into the CLSM for 6.11 h of processing, which produced 6.55 kg of glass, for an average glass production rate of 2275 kg m 2 d -1 . Since there were no processing issues with the AP-101 simulant melter feed, AP-101 melter feed made with actual waste was then processed in a CLSM system built into a contamination area in a radioactive environment. The melting behavior characteristics appeared similar for both the simulant and waste melter feeds. The AP-101 waste melter feed was charged into the CLSM for 12.14 h of processing, which produced 8.75 kg of glass, for an average glass production rate of 1530 kg m 2 d -1 . During the AP-101 waste melter feed charging, the pump used to move the feed reached a maximum and it is believed that if the pump had a greater capacity, a greater average glass production rate could have been achieved. A constituent of interest present in low quantities in the AP-101 waste is 99 Tc or its non-radioactive surrogate, Re, added to the AP-101 simulant. Analysis for the quantities of 99 Tc and Re in the AP-101 glass product resulted in an average single-pass retention from the melter feed during relative chemical steady state of 55 ± 2 % for 99 Tc and 45 ± 2 % for Re. Compared to the processing of other melter feeds, the retention of 99 Tc in the AP-101 glass was greater than in both AP-107 and AP-105 glass, while the retention of Re in the AP-101 was less than in the AP-107 glass, but greater than in the AP-105 glass. A spike of I was added into the AP-101 melter feed that could be detected above the analysis detection limits. However, the iodine was only detectable above the ~6 ppm limit in one glass pour: the pour immediately following the burn off of the cold cap, where the I level reached ~30 ppm. This event was significant because the glass was poured immediately after burn off and thus it is presumed that the iodine had yet to volatilize from the glass melt while idling. It is recommended to perform future tests with I spikes at greater levels so that it can be detected in additional glass pours to determine if the expected 50 % retention of I used in the Kim et al. glass models can be confirmed. Offgas liquid samples were analyzed for acetonitrile, which was present at greater concentrations in CLSM liquids than in other scaled melter systems. This result was expected based on unique conditions with the CLSM system including a small plenum space leading to low residence time for offgas and the rapidity of offgas cooling upon exiting the CLSM vessel due to the location and environment. About 90 % of the total acetonitrile captured during both the AP-101 simulant and waste CLSM runs was found in the offgas condensate and demister liquids, thus it is recommended that only those liquids be sent for analysis if future testing to study the presence of acetonitrile in offgas products is desired.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2022

Vitrification of Hanford Tank Wastes for Condensate Recycle and Feed Composition Changeover Testing (Rev. 1)

During the vitrification of Hanford Site nuclear waste at the Waste Treatment and Immobilization Plant (WTP), which is a part of the safe and efficient retrieval, treatment, and disposal mission of the U.S. Department of Energy Office of River Protection, the offgas condensate generated from the waste-to-glass conversion is currently planned to be concentrated by evaporation in the Effluent Management Facility (EMF). This concentrated condensate can then be recycled back to the incoming waste and vitrified. To test the recycle process, an apparatus was designed and built to mimic the EMF evaporator and was then used to concentrate a volume of condensate produced during the vitrification of a sample of Hanford tank 241-AP-107 (referred to herein as AP-107) waste in a continuous laboratory-scale melter (CLSM). The concentrated condensate was added to an additional sample of AP-107 waste, to mimic one round of the recycle process, and the combined solution was vitrified, producing a second round of recycle condensate. In the current study, the EMF test apparatus was used to concentrate the second-round recycle condensate under evaporation conditions (at 45 °C and 1.4 psia) designed to emulate EMF operation. The condensate was successfully concentrated by a factor of ~10 while retaining over 95 % of the technetium-99 (99Tc), Cs, and I inventories in the concentrate. Another portion of AP-107 waste was retrieved by Washington River Protection Solutions, LLC (WRPS) and transferred to Pacific Northwest National Laboratory (PNNL), where it was pretreated and then combined with the second-round recycle AP-107 condensate concentrate and glass-forming chemicals (GFCs) to form the two-time recycle AP-107 melter feed, approximating a second round to the recycling action to be performed at the WTP. A portion of AP-105 waste was also retrieved by WRPS and provided to PNNL for pretreatment and combining with GFCs to form AP-105 melter feed. The two-time recycle AP-107 and AP-105 melter feeds were processed consecutively in the CLSM. The CLSM run proceeded for 13.63 hours, producing 9.70 kg of glass for an average glass production rate of 1464 kg m 2 d -1 during the two-time recycle AP-107 feed charging and 1568 kg m 2 d -1 during the AP-105 feed charging. The rate during AP-107 charging was essentially equivalent to the rate when processing no-recycle AP-107 feed and lower than that achieved when processing one-time recycle AP-107 feed. However, all rates were within the potential range of variability when processing melter feeds with similar composition in the CLSM. Likewise, the rate during AP-105 charging was higher than the previous rate processing AP-105, but within the potential CLSM range. The cold-cap characteristics changed from the typically thin AP-107 cold cap to a foamy-edged cold cap as previously seen with AP-105 shortly after transitioning to the AP-105 melter feed. The glass produced during the CLSM run was within 10 % of its target composition for the primary glass components. The CaO and Li 2 O targets varied by more than 1 wt% between the two-time recycle AP-107 and AP-105 glass targets and it took about 2 turnovers of the CLSM glass inventory to reach a relative chemical steady state in the glass for CaO and Li 2 O after the melter feed inputs were switched.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2021

Vitrification of Hanford Tank Wastes for Condensate Recycle and Feed Composition Changeover Testing

During the vitrification of Hanford Site nuclear waste at the Waste Treatment and Immobilization Plant (WTP), which is a part of the safe and efficient retrieval, treatment, and disposal mission of the U.S. Department of Energy Office of River Protection, the offgas condensate generated from the waste-to-glass conversion is currently planned to be concentrated by evaporation in the Effluent Management Facility (EMF). This concentrated condensate can then be recycled back to the incoming waste and vitrified. To test the recycle process, an apparatus was designed and built to mimic the EMF evaporator and was then used to concentrate a volume of condensate produced during the vitrification of a sample of Hanford tank 241-AP-107 (referred to herein as AP-107) waste in a continuous laboratory-scale melter (CLSM). The concentrated condensate was added to an additional sample of AP-107 waste, to mimic one round of the recycle process, and the combined solution was vitrified, producing a second round of recycle condensate. In the current study, the EMF test apparatus was used to concentrate the second-round recycle condensate under evaporation conditions (at 45 °C and 1.4 psia) designed to emulate EMF operation. The condensate was successfully concentrated by a factor of ~10 while retaining over 95 % of the technetium-99 ( 99 Tc), Cs, and I inventories in the concentrate. Another portion of AP-107 waste was retrieved by Washington River Protection Solutions, LLC (WRPS) and transferred to Pacific Northwest National Laboratory (PNNL), where it was pretreated and then combined with the second-round recycle AP-107 condensate concentrate and glass-forming chemicals (GFCs) to form the two-time recycle AP-107 melter feed, approximating a second round to the recycling action to be performed at the WTP. A portion of AP-105 waste was also retrieved by WRPS and provided to PNNL for pretreatment and combining with GFCs to form AP-105 melter feed. The two-time recycle AP-107 and AP-105 melter feeds were processed consecutively in the CLSM. The CLSM run proceeded for 13.63 hours, producing 9.70 kg of glass for an average glass production rate of 1464 kg m 2 d -1 during the two-time recycle AP-107 feed charging and 1568 kg m 2 d -1 during the AP-105 feed charging. The rate during AP-107 charging was essentially equivalent to the rate when processing no-recycle AP-107 feed and lower than that achieved when processing one-time recycle AP-107 feed. However, all rates were within the potential range of variability when processing melter feeds with similar composition in the CLSM. Likewise, the rate during AP-105 charging was higher than the previous rate processing AP-105, but within the potential CLSM range. The cold-cap characteristics changed from the typically thin AP-107 cold cap to a foamy-edged cold cap as previously seen with AP-105 shortly after transitioning to the AP-105 melter feed. The glass produced during the CLSM run was within 10 % of its target composition for the primary glass components. The CaO and Li 2 O targets varied by more than 1 wt% between the two-time recycle AP-107 and AP-105 glass targets and it took about 2 turnovers of the CLSM glass inventory to reach a relative chemical steady state in the glass for CaO and Li 2 O after the melter feed inputs were switched. The 99 Tc and total cesium content in the melter feeds were maintained at concentrations expected to be experienced at the WTP. During the CLSM run, while processing the two-time recycle AP-107 melter feed at a relative chemical steady state, the 99 Tc/Cs ratio was 10, and 34% of 99 Tc and 74% of Cs were retained in the glass. These values were higher than those measured in the CLSM run with one-time recycle AP-107 melter feed. After the transition to processing the AP-105 melter feed, when the production reached a relative chemical steady state, the 99 Tc/Cs ratio was 77 while 44% of 99 Tc was retained in the glass. The C's retention during this time frame reached 200% due to the excess C's in the glass after the target content decreased to 15% of its initial level in the two-time recycle AP-107 melter feed to the lower target in the Ap-105 melter feed. While iodine was below inductively coupled plasma mass spectrometry analytical reporting limits in the melter feed and glass samples, it was detected in quantities above the analytical reporting limits in the liquid and filter samples collected from the CLSM offgas treatment system. The behavior of iodine in the CLSM offgas treatment system followed a similar pattern to those of 99 Tc and Cs.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2020

Vitrification of Hanford Tank 241-AP-107 with Recycled Condensate

During the vitrification of nuclear waste at the Hanford Waste Treatment and Immobilization Plant (WTP) – the primary mission of the U.S. Department of Energy Office of River Protection – the offgas condensate generated from the waste-to-glass conversion is currently planned to be concentrated by evaporation in the Effluent Management Facility (EMF). This concentrated condensate can then be recycled back to the incoming waste and vitrified. To test the recycle process, a test apparatus was designed to mimic the EMF evaporator and used to concentrate a volume of condensate that had been previously produced during the vitrification of Hanford tank 241-AP-107 (referred to herein as AP-107) waste in a continuous laboratory-scale melter (CLSM). The test apparatus successfully concentrated the AP-107 condensate by a factor of 10 while retaining over 90 % of the technetium-99 ( 99 Tc), Cs, and I inventory. A second portion of AP-107 waste was retrieved by Washington River Protection Solutions, LLC, given to Pacific Northwest National Laboratory, and combined with the AP-107 condensate concentrate after undergoing solids filtration and cesium removal by ion exchange. This combination served to approximate the recycling action to be performed at the WTP. After the addition of glass-forming chemicals (GFCs), the combined AP-107 waste and AP-107 condensate concentrate were processed in the CLSM to produce a glass, called AP-107-1R, that was designed to satisfy the WTP baseline requirements (Kim et al. 2012). During the 8.87 hours of processing, 7.27 kg of AP-107-1R glass were produced for an average glass production rate of 1739 kg m 2 d -1 . Compared to the previous run in the CLSM without recycled condensate, the run with the recycle had a greater average glass production rate, but the rate was within the potential range of variability when processing melter feeds with similar composition in the CLSM. The glass produced from the AP-107 recycle run in the CLSM was within 10 % of the target AP-107-1R glass composition with respect to the primary glass components. Analysis of the minor component impurities revealed that their content in the glass product had approached their nominal target after 2 turnovers of the glass inventory in the CLSM while the activity of the minor radionuclides was retained in the glass product. The 99 Tc and total cesium content in the combined AP-107 waste and recycled condensate were maintained at concentrations expected to be experienced at the WTP. During processing in the CLSM, at discrete sampling time periods, the target 99 Tc/Cs mass ratio in the glass formulation varied from 0.9 to 62.9. Across this range, the Cs retention in the glass ranged from 53 to 60 %, while the retention from the entire runtime totaled 68 %, values which align with Cs retention in other scaled melter systems while processing LAW melter feeds at 99 Tc/Cs mass ratios ranging from 1 to 100. The 99 Tc retention in the glass ranged from 22 to 32 %, primarily due to the cold-cap coverage on the glass melt surface, the area covered by reacting melter feed, varying from ~80 % to ~95 % during processing, demonstrating greater volatility of 99 Tc from the glass while more surface was exposed, as expected based on previous 99 Tc volatility studies.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2020

Laboratory-Scale Melter Systems for Simulated and Real AP-107 Tank Waste - 20483

The Hanford Waste Treatment and Immobilization Plant (WTP) will process and stabilize waste that is stored in underground tanks on the Hanford Site. At the WTP, the tank waste will be combined with glass-forming and modifying additives to form an aqueous and solid mixture called melter feed, which will then be vitrified in joule-heated melters. A small-scale melter system, the continuous laboratory-scale melter (CLSM), is designed to operate with a continuous feeding process while periodically pouring glass product and collecting off-gas. Two CLSMs were constructed: one in a non-radioactive environment for processing waste simulants and another in a fume hood capable of handling radioactive material for processing actual Hanford tank waste. The waste sample received for vitrification in the CLSM was from Hanford tank 241-AP-107. Approximately 12 liters of melter-feed slurry was vitrified into 7 kilograms of glass product over the course of 10 hours of charging to the CLSM. The partitioning of technetium-99 in the product streams was used to calculate the technetium-99 recovery and help determine when the vitrification process had reached a steady state. The average single-pass retention of technetium-99 in the glass product was then calculated for the processing of AP-107 waste in the CLSM system. (authors)

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2020

Continuous Laboratory-Scale Melter Runs for System Evaluation

The Waste Treatment and Immobilization Plant (WTP) will process and stabilize waste that is stored in underground tanks on the Hanford Site. Currently, the first phase of the planned WTP startup and operation, called Direct Feed Low-Activity Waste (DFLAW), involves directly feeding only the liquid portion of the waste to electric melters in the WTP Low-Activity Waste (LAW) Vitrification Facility without full pretreatment. A second portion of the tank waste, called high-level waste (HLW), is set to contain most of the radioactivity inventory.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗