Stewart, David Murdock

DOE OSTI2024

Simultaneous Solid Electrolyte Deposition and Cathode Lithiation for Thin Film Batteries and Lithium Iontronic Devices

Here we show that the deposition of the solid-state electrolyte LiPON onto films of V 2 O 5 leads to their uniform lithiation of up to 2.2 Li per V 2 O 5 , without affecting the Li concentration in the LiPON and its ionic conductivity. Our results indicate that Li incorporation occurs during LiPON deposition, in contrast to earlier mechanisms proposed to explain postdeposition Li transfer between LiPON and LiCoO 2 . We use our discovery to demonstrate symmetric thin film batteries with a capacity of >270 mAh/g, at a rate of 20C, and 1600 cycles with only 8.4% loss in capacity. We also show how autolithiation can simplify fabrication of Li iontronic transistors attractive for emerging neuromorphic computing applications. Our discovery that LiPON deposition results in autolithiation of the underlying insertion oxide has the potential to substantially simplify and enhance the fabrication process for thin film solid state Li ion batteries and emerging lithium iontronic neuromorphic computing devices.

25 ENERGY STORAGE↗

DOE OSTI2023

In Situ Raman Mapping of Si Island Electrodes and Stress Modeling as a Function of Lithiation and Size

Si is known for cracking and delamination during electrochemical cycling of a battery due to the large volume change associated with Li insertion and extraction. However, it has been found experimentally that patterned Si island electrodes that are 200 nm thick and less than 7 μm wide can deform in a purely elastic manner. Inspired by this, we performed in situ Raman stress characterization of model poly-crystalline Si island electrodes using an electrochemical cell coupled with an immersion objective lens and designed for a short working distance. A 5 μm wide Si island electrode showed a parabolic stress profile during lithiation, while for a 15 μm Si island electrode, a stress plateau in the center of the electrode was observed. A continuum model with coupled electro-chemo-mechanical (ECM) physics was established to understand the stress measurement. A qualitative agreement was reached between modeling and experimental data, and the critical size effect could be explained by the Li diffusive flux as governed by competition between the Li concentration and hydrostatic stress gradients. Below the critical size, the stress gradient drives Li toward the edges, where the electrode volume is free to expand, while above the critical size, the stress plateau inhibits Li diffusion to the edge and forces destructive stress relief by cracking. Furthermore, this work represents a promising methodology for in situ characterization of ECM coupling in battery electrodes, with suggestions provided for further improvement.

25 ENERGY STORAGE↗