Superconductivity in WBe 2
WBe 2 , which occurs in space group 194, with hexagonal symmetry P6 3 /mmc, is prepared by arc-melting at temperatures above 2200 C, where Be vapor loss is significant. This study is motivated by recent work on MoB 2 and WB 2 , both superconductors (T c =32 and 17 K respectively) under high (∼70 GPa) pressure. In order to avoid the known Be-rich superconducting phases (WBe 13 and WBe 22 ) in the complex phase diagram, both known to be superconducting at 4.1 K, the sample was prepared with a slight (∼5 %) excess of W. The resultant sample, prepared using high purity (99.999 %) Be, is essentially single phase WBe 2 , with some spread in its superconducting properties due to the known homogeneity range. (WBe 2 forms in space group 194 between approximately W 1.02 Be 1.98 and W 0.88 Be 2.12 .) Characterization was carried out with x-ray diffraction, electrical resistivity, ρ, in zero and applied magnetic fields, and specific heat. The resistivity in zero and applied fields and specific heat data indicate that our sample of WBe 2 is a bulk superconductor at ambient pressure with a T c onset in ρ at 1.05 K, and T c (ρ→0) at ∼0.86 K. Furthermore, there is no signature of superconductivity in ρ at 4.1 K, indicating successful avoidance of WBe 13 and WBe 22 . The ρ data in field indicate an upper critical field of approximately 400 gauss.