NASA NTRS1980

Preliminary design of graphite composite wing panels for commercial transport aircraft

Subjectively assessed practical and producible graphite/epoxy designs were subjected to a multilevel screening procedure which considered structural functions, efficiency, manufacturing and producibility, costs, maintainability, and inspectability. As each progressive screening level was reviewed, more definitive information on the structural efficiency (weight), manufacturing, and inspection procedures was established to support the design selection. The configuration features that enhance producibility of the final selected design can be used as a generic base for application to other wing panel designs. The selected panel design showed a weight saving of 25 percent over a conventional aluminum design meeting the same design requirements. The estimated cost reduction in manufacturing was 20 percent, based on 200 aircraft and projected 1985 automated composites manufacturing capability. The panel design background information developed will be used in the follow-on tasks to ensure that future panel development represents practical and producible design approaches to graphite/epoxy wing surface panels.

Byers, B. A.↗
NASA NTRS1980

The 737 graphite composite flight spoiler flight service evaluation

The flight service experience of 111 graphite-epoxy spoilers on 737 transport aircraft and related ground based enviromental exposure of graphite-epoxy material specimens is reported. Spoilers were installed on 28 aircraft representing seven major airlines operating throughout the world. Over 1,188,367 spoiler flight hours and 1,786,837 spoiler landings were accumulated by this fleet. Tests of removed spoilers and ground-based exposure specimens after the fifth year of service indicate modest changes in composite strength properties. Two incidents of trailing edge delamination with subsequent core corrosion were observed. Based on visual, ultrasonic, and destructive testing, there has been no evidence of moisture migration into the honeycomb core and no core corrosion.

Hoffman, D. J.↗
NASA NTRS1977

The 737 graphite composite flight spoiler flight service evaluation

The flight service experience of 110 graphite epoxy spoilers on 737 transport aircraft was reviewed as well as ground based environmental exposure of graphite epoxy material specimens for the period from April 1976 through April 1977. Several spoilers were installed on each of 27 aircraft representing seven major airlines operating throughout the world. A flight service evaluation program of at least 5 years is under way. As of April 30, 1977, a total of 766,938 spoiler flight hours and 1,168,090 spoiler landings were accumulated by the fleet. Based on visual ultrasonic, and destructive testing, there was no evidence of moisture migration into the honeycomb core and no core corrosion. Tests of removed spoilers and of ground based exposure specimens after the third year of service continue to indicate modest changes in composite strength properties.

Stoecklin, R. L.↗
NASA NTRS1976

Development, manufacturing, and test of graphite-epoxy composite spoilers for flight service on 737 transport aircraft

A total of 114 spoiler units were fabricated in a production shop environment, utilizing three graphite epoxy material systems. Production planning paper was generated for each spoiler unit to completely document each production step of each spoiler unit. The graphite epoxy skins were laid up on production tooling using both mechanical and hand layup techniques. Inspection techniques utilized MRB type assessment in the abscence of quality requirements. Each completed spoiler was subjected to ultrasonic inspection utilizing a multicolor recording system that documented each inspection result. In addition, one static test spoiler was sectioned after the test to examine the adhesive filleting to the honeycomb core. Visual examination of the cured adhesives showed excellent results.

Stoecklin, R. L.↗
NASA NTRS1976

The 737 graphite composite flight spoiler flight service evaluation

The flight-service experience of 110 graphite-epoxy spoilers on 737 transport aircraft and related ground-based environmental exposure of graphite-epoxy material specimens is reported. Spoilers were installed on each of 27 aircraft representing seven major airlines operating throughout the world. Based on visual, ultrasonic, and destructive testing, there is no evidence of moisture migration into the honeycomb core and no core corrosion. Tests of removed spoilers and of ground-based exposure specimens after the second year of service indicate modest changes in composite strength.

Stoecklin, R. L.↗
NASA NTRS1975

The 737 graphite composite flight spoiler flight service evaluation

The flight service experience of 108 graphite-epoxy spoilers on 737 transport aircraft, and related ground-based environmental exposure of graphite-epoxy material specimens were evaluated. Four spoilers were installed on each of 27 aircraft for a 5-year study. As of February 28, 1975, a total of 294,280 spoiler flight-hours and 460,686 spoiler landings were accumulated. Based on visual, ultrasonic, and destructive testing, no moisture migration into the honeycomb core and no core corrosion has occurred. Tests of removed spoilers and of ground-based exposure specimens after the first year of service indicate no significant changes in composite strength.

Stoecklin, R. L.↗