NASA NTRS2001

Promoted Combustion of Metals in a High-Pressure, Flowing Oxygen Environment

Traditional promoted combustion testing has used 0.125 inch diameter samples that are ignited in a pressurized, oxygen-enriched environment. Many years of testing this sample size have yielded useful data regarding threshold pressure, or the minimum oxygen pressure required to support self-sustained combustion. However, when a material is tested in a flowing system, the threshold pressure changes. White Sands Test Facility has developed a test system to burn samples in flowing gaseous oxygen. Current sample configurations are 0.5 inch diameter rods and 1.25 inch diameter pipes with pressures ranging up to 2000 psi and gas velocities reaching 200 ft/s. This paper describes the test apparatus, modifications made as the result of a fire, and a description of the tests currently being performed.

Maes, M. J.↗

NASA NTRS1992

Material compatibility evaluation for liquid oxygen turbopump fluid foil bearings

Three series of tests were carried out on three polymer-coated Inconel substrate materials, Teflon S, polyimide bonded graphite fluoride (PBGF), and Teflon, which are considered for use in fluid foil bearings for a liquid oxygen turbopump. All the candidate materials passed the liquid oxygen frictional heating test. During the gaseous oxygen frictional heating test, all coatings wore off before ignition occured. Both Teflon S and PBGF coated foils passed 100 start/stop cycles against chrome-plated Inconel 718 shaft in the direct foil bearing lift-off simulation test in liquid oxygen.

Stoltzfus, J. M.↗

NASA NTRS1986

Ignition of metals and alloys in gaseous oxygen by frictional heating

The ignition of metals and alloys have been investigated by rotating the end of a hollow cylinder against an identical stationary cylinder on a common axis (frictional heating) in gaseous oxygen. A ranking criterion that measures the resistance of metals and alloys to ignition is discussed. It consists of the power per unit area required for ignition conveniently expressed as the product of contact pressure P and average linear velocity ALV. Data are presented that demonstrate that materials that are high in nickel and copper require greater P-ALV products for ignition (more resistant to ignition) than materials that are high in iron. Aluminum and titanium alloys are shown to require the lowest P-ALV products for ignition. The effects of varying surface velocity, contact pressure, coefficient of friction, and oxygen pressure on P-ALV products required for ignition are discussed. The results indicate that P-ALV product required for ignition increases as surface velocity increases, as contact pressure decreases, and as the coefficient of friction decreases. Increasing oxygen pressure will cause the P-ALV product required for ignition to decrease at low pressures and increase at high pressures. In some cases, the relative ranking of materials based on P-ALV products will also change as conditions are varied. The data presented in this paper are from a development program to determine the merits of using such a dynamic test method for ranking materials for oxygen service. The results to date have indicated that more testing is required before this method can be made into a standard test. The data presented do show some of the major parameters affecting the ignition of materials when exposed to frictional heating. The repeatability of the data at any set of conditions have not been thoroughly investigated.

Benz, F. J.↗

NASA NTRS1985

An experimental data base for material selection and design of high-speed, high-pressure, oxygen turbomachinery

New technologies for space-based, reusable, throttleable, cryogenic, orbit transfer propulsion are being evaluated. A variable-thrust (200 to 3000 lbF), 2000 psi chamber pressure, LO2/LH2 engine has been selected to demonstrate the 20-hour, 500-restart life goal, and a specific impulse of 480 lbF-sec/lbM. The advanced design uses warm oxygen to power a fully integrated turbopump that delivers 4500 psi LO2. The selected engine cycle provides the following advantages over conventional expander cycle designs which use H2 to drive the LH2 and LO2 pumps; higher engine operating pressures and performance in a smaller envelope, lower turbine operating temperatures, elimination of interpropellant seals and purges, and an extended throttling range. The design approach and results of testing to characterize materials for use in high-pressure gaseous oxygen are discussed. Test methods include particle impact testing in a sonic-flow, hot GO2 streams and forced, high-speed friction rubbing testing. Materials are exposed to oxygen and nitrogen atmospheres at pressures of 100, 1000, and 3000 psi to identify separately the gas cooling effects from the metal oxidation effects at the rubbing surface. The selection of candidate design materials is based on an analytical parameter defined as the burn factor. Typical materials tested include carbon steel, stainless steel, nickel, copper, and monel alloys.

Schoenman, L.↗

NASA NTRS1983