Engineering topics
Publications and source records attributed to Storm, R. S..
The physical properties of sintered alpha silicon carbide are reviewed, including the effect of oxidation at high temperatures. Net shape fabricated components are described which have undergone extensive testing in heat engine applications. Properties of an SiC/TiB2 composite material, which has significantly improved fracture toughness, are presented.
Processing methods of sintered alpha SiC for engine applications are developed in a cost effective manner, using a submicron sized powder blended with sintering aids (boron and carbon). The processes for forming a green powder compact, such as dry pressing, cold isostatic pressing and green machining, slip casting, aqueous extrusion, plastic extrusion, and injection molding, are described. Dry pressing is the simplest route to component fabrication, and is carried out at approximately 10,000 psi pressure, while in the cold isostatic method the pressure could go as high as 20,000 psi. Surfactants are added to control settling rates and casting characteristics in the slip casting. The aqueous extrusion process is accomplished by a hydraulic ram forcing the aqueous mixture through a die. The plastic forming processes of extrusion and injection molding offer the potential of greater diversity in shape capacity. The physical properties of sintered alpha SiC (hardness, Young's modulus, shear modulus, and thermal diffusivity) are extensively tested. Corrosion resistance test results of silicon carbide are included.
The development status of component technology in an automotive gas turbine Ceramic Applications in Turbine Engines program is discussed, with attention to such materials and processes having a low cost, net shape fabrication potential as sintered alpha-SiC that has been fashioned by means of injection molding, slip casting, and isostatic pressing. The gas turbine elements produced include a gasifier turbine rotor, a turbine wheel, a connecting duct, a combustor baffle, and a transition duct.
Net shape techniques have been used in the production of rotating and static vehicular engine high-temperature components composed of sintered Alpha-SiC (SASC). Injection-molded rotors have been cold spin tested, as well as a slip-cast combustor assembly hot rig. SASC pistons and cylinder liners have also been constructed for an opposed piston, two-cycle diesel test rig while test results are presented. An uncooled, minimum-friction internal combustion engine with multi-fuel capability due to its elevated combustion temperatures appears to be achievable in the near term by means of SASC techniques. The flexural strength of SASC at 1500 C is 446 MPa, identical to that at room temperature, and excellent strength retention has been demonstrated after 3500 hours of cyclic exposure.
Development of Alpha Silicon Carbide components by net shape fabrication techniques has continued in conjunction with several turbine engine programs. Progress in injection molding of simple parts has been extended to much larger components. Turbine rotors fabricated by a one piece molding have been successfully spin tested above design speeds. Static components weighing up to 4.5 kg and 33 cc in diameter have also been produced using this technique. Use of sintering fixtures significantly improves dimensional control. A new Si-SiC composite material has also been developed with average strengths up to 1000 MPa (150 ksi) at 1200 C.
Fabrication of a sintered alpha silicon carbide turbine blade by injection molding is described. An extensive process variation matrix was carried out to define the optimum fabrication conditions. Variation of molding parameters had a significant impact on yield. Turbine blades were produced in a reasonable yield which met a rigid quality and dimensional specification. Application of injection molding technology to more complex components such as integral rotors is also described.