DOE OSTI2024

Microstructure and Mechanical Properties of Ni-based Alloys Fabricated by Laser Powder Bed Fusion

The Advanced Materials and Manufacturing Technologies (AMMT) program is aiming at the accelerated incorporation of new materials and manufacturing technologies into nuclear-related systems. Complex Ni-based components fabricated by laser powder bed fusion (LPBF) could enable operating temperatures at T > 700°C in aggressive environments such as molten salts or liquid metals. However, available mechanical properties data relevant to material qualification remains limited, in particular for Ni-based alloys routinely fabricated by LPBF such as IN718 (Ni- 19Cr-18Fe-5Nb-3Mo) and Haynes 282 (Ni-20Cr-10Co-8.5Mo-2.1Ti-1.5Al). Creep testing was conducted on LPBF 718 at 600°C and 650°C and on LPBF 282 at 750°C. finding that the creep strength of the two alloys was close to that of wrought counterparts. with lower ductility at rupture. Heat treatments were tailored to the LPBF-specific microstructure to achieve grain recrystallization and form strengthening γ' precipitates for LPBF 282 and γ' and γ" precipitates for LPBF 718. In-situ data generated during printing and ex-situ X-ray computed tomography (XCT) scans were used to correlate the creep properties of LPBF 282 to the material flaw distribution. In- situ data revealed that spatter particles are the potential causes for flaws formation in LPBF 282. with significant variation between rods based on their location on the build plate. XCT scans revealed the formation of a larger number of creep flaws after testing in the specimens with a higher initial flaw density. which led to a lower ductility for the specimen.

Dryepondt, Sebastien↗
DOE OSTI2024

Complete Optimization of LPBF Ni-Based Alloys Down-Selected from FY23 Candidate Materials Including, Thermodynamic Modeling, Sample Fabrication and Microstructure Characterization

The goal of the Advanced Materials and Manufacturing Technologies (AMMT) program is to accelerate the incorporation of new materials and manufacturing technologies into advanced nuclear-related systems. Although 316H stainless steel fabricated by laser powder bed fusion (LPBF) has already been identified as an alloy that could have a significant effect on various reactor technologies, many other materials and manufacturing techniques are being evaluated. Nickel-based alloys typically offer higher-temperature capabilities compared with advanced stainless steels, and previous reports looked at three Ni-based alloy categories: low-Co alloys with a potential use close to the reactor core; high-temperature, high-strength alloys; and molten salt–compatible alloys. In the first category, alloy 718 was studied in 2023, and creep testing at 600°C and 650°C revealed that the alloy exhibited great creep strength after the appropriate annealing but had low ductility. Advanced characterization was recently conducted to highlight the presence of strengthening γ' and γ" precipitates after creep testing and to show that brittle phases at grain boundaries might explain the low ductility of LPBF 718 compared with wrought 718. For the high-temperature, high-strength alloys, previously purchased powders of alloys 617, 230, and 625 were used to assess the printability of these three solution-strengthened alloys. Hot cracking could not be suppressed for alloy 617 and 230, and it was shown that these cracks, which were elongated along the build direction (BD), had a drastic effect on the ductility of alloy 230 at room temperature when specimens were machined perpendicular to the BD. On the contrary, LPBF printing of crack-free alloy 625 was achieved using similar printing parameters, and the alloy looked like a promising candidate for various reactor technologies. The fabrication of alloy 282 by LPBF, a γ'-strengthened alloy with great creep strength up to 800°C, was performed in 2023, and x-ray computed tomography (XCT) scans of the alloy before and after creep testing at 750°C were carried out to assess the effect of flaws on the alloy’s creep behavior. Correlation between the flaws’ volume fraction, creep ductility, and creep lifetime could be established, and future work on LPBF 625 will take full advantage of in situ printing data and ex situ XCT scans to accelerate the alloy qualification. Finally, single track experiments were performed on the two alloys previously identified as good molten salt–resistant, Ni-based candidates: Hastelloy N and 244. Various laser parameters were considered, and cracking was not observed for either of the two alloys. Wrought 244 offers better creep strength and molten salt compatibility than alloy 625, and future work will aim to establish the alloy LPBF processing window.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Advanced neutron absorber Ni-Cr-Mo-Gd alloys seawater corrosion mechanism and susceptibility study

Previous studies demonstrated the corrosion susceptibility of advanced neutron absorber (ANA) Ni-Cr-Mo-Gd in a seawater environment but remained inconclusive. In this paper, scanning electron microscopy was employed to identify the corrosion phase in Ni-Cr-Mo-Gd, and computational thermodynamic simulation was used to study phase corrosion potentials. Results showed that the Ni 5 Gd second phase, distributed along FCC grain boundaries in Ni-Cr-Mo-Gd, has lower corrosion potential than the substrate. Furthermore, heat treatment and alloy chemistry adjustment would not ameliorate the ANA corrosion susceptibility. Finally, isolating the Ni 5 Gd from the corrosion medium through advanced manufacturing is a viable way to improve the ANA corrosion resistance.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Internal carburization and scale formation on austenitic steels in supercritical carbon dioxide

Direct-fired supercritical CO 2 (sCO 2 ) power cycles are being commercialised to revolutionise fossil energy as a low-emission power source. In order to lower the cost of this technology, less expensive steels are needed in the lower temperature segments of the cycle. However, there are concerns about internal carburisation of steels in sCO 2 . A consistent observation is that thin, Cr-rich oxides appear to reduce C ingress compared to thick Fe-rich oxides formed on 9–12% Cr ferritic-martensitic steels. Advanced austenitic stainless steels (SS) like alloy 709 (20Cr-25Ni) are able to continue to form Cr-rich oxides at 650°C, while a conventional type 316 H SS formed a Fe-rich scale. The C diffusion profiles in SS specimens were quantified at 550°C–650°C using glow discharge optical emission spectroscopy and electron probe microanalysis. Analytical transmission electron microscopy was used to compare the thin protective Cr-rich oxide formed on alloy 709 in sCO 2 at 650°C to that formed in ambient air.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Atmospheric Pressure Plasma Treatment of Magnesium Alloy for Enhanced Coating Adhesion and Corrosion Resistance

Atmospheric pressure plasma (AP) treatment, using an open-air jet of ionized CO 2 , N 2 , or air, was applied to AZ91D Mg alloy surfaces to investigate its effects on primer coating adhesion and corrosion resistance. The CO 2 and air AP treatments formed an O- and C-rich surface layer (Mg-O-C) consisting of agglomerated nanoparticles and pits with a depth of a few microns and increasing the surface roughness by 6–8 times compared with the reference 600 grit-finished surface. Then, three commercial primers, zinc phosphate (ZnP), chromate-containing epoxy, and MIL23377, were applied on the treated surfaces to evaluate the corrosion resistance associated with the coating adhesion. Microscopic analysis demonstrated stronger interlocking between the primer layer and the nano-/microrough Mg-O-C surface compared to the untreated (600 grit-finished) surfaces, indicating improved coating adhesion and corrosion resistance. Crosscut tests of the MIL23377 primer on the CO 2 and air AP-treated surfaces showed the highest level of adhesion, ASTM class 5B. Salt spray corrosion tests showed that after 8 days of exposure, the primer coatings on air AP-treated surfaces had corrosion areas that were more than four times smaller than that of the 600 grit-finished surface. The N 2 AP treatment showed similar adhesion enhancement. The preliminary operation expenses for AP treatment using CO 2 , N 2 , and air were estimated at USD 30.62, USD 35.45, and USD 29.75 (from an air cylinder)/USD 0.66 (from an air compressor) per m 2 , respectively.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Characterization of Fe and Cr Dissolution and Reaction Product Formation in Molten Chloride Salts With and Without Impurities

There is considerable interest in molten chloride salts for several applications including thermal storage and next-generation molten salt reactors (MSRs). Several studies have concluded that Cl salts are highly corrosive to structural materials. Using Oak Ridge National Laboratory’s established methodology, Cl salt compatibility was assessed for candidate Ni-based alloys 230, 600 and 740 H at 600°–800°C in static welded capsules and in flowing thermal convection loop (TCL) salt experiments. Simply drying commercial Cl salt at 550°–650°C and adding~0.05 wt.%Mg was able to produce small specimen mass changes and limited surface attack after 100–1000 h exposures. Intentional additions of H 2 O, NiCl 2 and undried salt were used to better understand the role of impurities and achieve the>50 µm levels of attack reported in other studies. Further, characterisation of Cr depletion and oxide formation in conjunction with pre- and post-test salt chemistry measurements are being used to understand salt compatibility of structural materials.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Experimental and modeling studies of IPDI-based polyurea elastomers – The role of hard segment fraction

Segmented polyureas (PUa) are industrially important class of polymers widely used in coatings, sealant, and adhesive applications. Here, in this paper, we report synthesis, characterization, and modeling of Isophorone Diisocyanate-Diethyl-Toluene-Diamine-Polyether amine (IPDI-DETDA-PO PUa) with varied hard segment contents of 20, 30, and 40 weight percent. For each of the three materials, we study its structure and phase behavior using FTIR, DSC, and TEM, and clearly show the presence of microphase separation between the hard and soft nanodomains. We then measure the linear viscoelastic response of the PUa-s using DMA (frequency sweeps at multiple temperatures). The DMA data are shown to obey the time-temperature superposition. Finally, we develop a new micromechanical model describing the DMA results; the model describes a phase-separated PUa as two “Fractional-order Maxwell gels” branches, connected in parallel, with the first FMG branch representing the “percolated hard phase" and the second one modeling the “filled soft phase". In agreement with the earlier thermodynamic theories, the volume-fraction of the percolated hard phase is related to the hard segment weight-fraction (HSWF), defined as the combined mass of IPDI and DETDA normalized to the total mass of the polymer. The data and model are found to be in a good qualitative and quantitative agreement.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Formation of carbon and oxygen rich surface layer on high purity magnesium by atmospheric carbon dioxide plasma

Carbon and oxygen-rich corrosion barrier layer formed on Mg by a simple and scalable CO 2 atmospheric plasma (CO 2 -AP) process. The reactive CO 2 -AP interacts with the Mg surface and forms a unique layered structure with the top MgCO 3 /MgO-intermixed particulates pillars and the bottom dense layer. The surface features were simultaneously formed on the nano-/micro-structured MgO layer by carbonate molecules, plasma-active CO 2 molecules, and/or other volatile organic compounds on the nano-/micro-structured MgO particle layer. The resulting surfaces after CO 2 -AP were either hydrophobic or hydrophilic and exhibited lower anodic current or high resistance for Mg corrosion. For the hydrophobic surfaces of CO 2 -AP treated Mg, molecular dynamic simulations were performed to understand the origin of hydrophobicity and identified that the amorphous carbon layers formed on the Mg surface are the source. The environmentally benign abundant-gas-based process enables the cost reduction associated with waste treatment, generation of by-product, and supply of raw material.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Corrosion Prevention of Additively Manufactured Aluminum Packing Devices Developed for Process Intensification of CO 2 Capture by Aqueous Amines

Corrosion of additively manufactured (i.e., 3D printed) aluminum packing devices, developed to enhance heat and mass transfer in CO 2 absorption columns using amine-CO 2 scrubbing solutions, is investigated in this paper. The aluminum structures printed by selective laser melting with Al-10Si-0.3Mg feed powder are susceptible to corrosion in aqueous monoethanolamine, both fresh and used CO 2 -saturated solutions. The efficacy of corrosion-protective surface layers of aqueous polyether–ketone–ketone (PEKK) dip coating to provide amine corrosion resistance to the 3D printed aluminum structure is also evaluated. PEKK nanothick layers were coated on the corrugated surface of a 3D printed structure, identical to that of the intensified device, yielding 27 times higher corrosion resistance than the uncoated Al alloy surface. Finally, a systematic long-term electrochemical corrosion analysis revealed that a multilayer PEKK dip coating protocol enables protection of the 3D printed Al alloy surface in various CO 2 –monoethanolamine solutions.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Compatibility of Alumina-Forming Austenitic Steels in Static and Flowing Pb

Alumina-forming austenitic (AFA) steels were evaluated for the lead fast reactor application in static and flowing high-purity Pb. Two AFA composition ranges with different Ni, Mn, Al, Cr and Nb contents were targeted, and Zr foil was used in an attempt to getter O in some capsules. Based on two rounds of capsule testing at 500–800°C, two AFA compositions were selected for evaluation in flowing Pb with a peak temperature of 650°C in a thermal convection loop made of pre-oxidized FeCrAlMo tubing. After exposure for 1000 h, the mass losses for both AFA alloys were generally low, suggesting good compatibility under these conditions without preoxidation.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Quantifying High Temperature Corrosion

Alloys designed for high temperature service can form a variety of surface oxides or scales based on the alloy composition, service temperature, gas environment, surface deposits, etc. The most severe environments, including molten salts and liquid metals can result in significant metal loss, void formation and/or pitting. Standard and evolving practices are discussed for measuring these types of degradationincluding measuring oxide scale thickness, internal oxidation and/or metal loss, correlating them to mass change and reporting the results. Manual and automated methodologies to measure oxide thickness and metal loss are reviewed and compared in order to provide a summary of techniques and identify the best practices for quantifying a variety of materials and damage mechanisms and producing statistically meaningful results. Such techniques create datasets useful for improved understanding of corrosion degradation mechanisms, potentially better predictive models and enhanced data analytics.