NASA NTRS1988

Evaluation of mixed solvent electrolytes for ambient temperature secondary lithium cells

The ethylene carbonate/2-methyltetrahydrofuran (EC/2-MeTHF) mixed-solvent electrolyte has been experimentally found to possess many desirable electrolyte characteristics for ambient-temperature secondary Li-TiS2 cell applications. As many as 300 cycles have been demonstrated, and a cycling efficiency figure-of-merit of 38.5 percent, for 10-percent EC/90-percent MeTHF mixed-solvent electrolyte in experimental Li-TiS2 cells. The improved performance of this electrolyte is attributable to the formation of a beneficial passivating film on the Li electrode by interaction with the EC.

Shen, D. H.↗

NASA NTRS1987

Development of ambient temperature secondary lithium cells

JPL is developing ambient temperature secondary lithium cells for future spacecraft applications. Prior studies on experimental laboratory type Li-TiS2 cells yielded promising results in terms of cycle life and rate capability. To further assess the performance of this cell, 5 Ah engineering model cells were developed. Initially baseline cells were designed and fabricated. Each cell had 15 cathodes and 16 anodes and the ratio of anode to cathode capacity is 6:1. A solution of 1.5 molar LiAsF6 in 2Me-THF was used as the electrolyte. Cells were evaluated for their cycle life at C/1 and C/5 discharge rates and 100 percent depth of discharge. The cells were cycled between voltage limits 1.7 and 2.8 volts. The rate of charge in all cases is C/10. The results obtained indicate that cells can operate at C/10 to C/2 discharge rates and have an initial energy density of 70 Wh/kg. Cells delivered more than 100 cycles at C/2 discharge rate. The details of cell design, the test program, and the results obtained are described.

Subbarao, S.↗

NASA NTRS1987

Chemical analysis of charged Li/SO(sub)2 cells

The initial focus of the program was to confirm that charging can indeed result in explosions and constitute a significant safety problem. Results of this initial effort clearly demonstrated that cells do indeed explode on charge and that charging does indeed constitute a real and severe safety problem. The results of the effort to identify the chemical reactions involved in and responsible for the observed behavior are described.

Subbarao, S.↗

NASA NTRS1986

Test results of JPL LiSOCl sub 2 cells

In the development of high rate Li-SO-Cl2 cells for various applications, the goal is to achieve 300 watt-hours per kilogram at the C/2 (5 amp) rate in a D cell configuration. The JPL role is to develop the understanding of the performance, life, and safety limiting characteristics in the cell and to transfer the technology to a manufacturer to produce a safe, high quality product in a reproducible manner. The approach taken to achieve the goals is divided into four subject areas: cathode processes and characteristics; chemical reactions and safety; cell design and assembly; and performance and abuse testing. The progress made in each of these areas is discussed.

Halpert, G.↗

NASA NTRS1986

Evaluation of advanced high rate Li-SOCl2 cells

Under NASA sponsorship, JPL is developing advanced, high rate Li-SOCl2 cells for future space missions. As part of this effort, Li-SOCl2 cells of various designs were examined for performance and safety. The cells differed from one another in several aspects, such as: nature of carbon cathode, catalysts, cell configuration, case polarity, and safety devices. Performance evaluation included constant-current discharge over a range of currents and temperatures. Abuse-testing consisted of shortcircuiting, charging, and over-discharge. Energy densities greater than 300 Wh/Kg at the C/2 rate were found for some designs. A cell design featuring a high-surface-area carbon cathode was found to deliver nearly 500 Wh/Kg at moderate discharge rates. Temperature influenced the performance significantly.

Deligiannis, F.↗

NASA NTRS1985

Safety of Li-SOCl2 cells

The safety of lithium thionyl chloride cells has been a concern of JPL for some time in the development of these cells for NASA's use. Because the safety problems are complex and several issues are interrelated it was decided that it would be best to put together an organized review of the safety issues, which are reviewed here. Hazards are classified in three categories: (1) cell leakage, a problem dealing with construction or materials; (2) venting of toxic gases through seals and welds, considered a mild hazard in which electrolyte and gas is released; and (3) violent rupture or controlled rupture of cells with the possibility of explosion of the materials inside. These hazards and their effects are detailed along with possible ways of dealing with them.

Subbarao, S.↗

NASA NTRS1985

An update of the JPL program to develop Li-SOCl2 cells

The goal of producing spiral wound D cell was met. The cell design and electrodes, particularly the carbon cathodes were produced in-house. Also all parts were assembled, the welding performed, the electrolyte aided and the cells sealed in-house. The lithium capacity (theoretical) was 19.3 Ah and that of the SOCl2 in the 1.8 m LiAlCl4 electrolyte, 16.4 Ah (a greater excess of SOCl2 is necessary for safe high rate operation). The electrode surface area was 452 sq cm. The carbon electrode comprised Shawinigen Black/Teflon -30 (90/10 by weight) mixture 0.020 inches thick on an expanded metal screen prepared in the JPL laboratory. There were two tab connections to the cathode. The 0.0078 inch thick lithium foil was rolled into an expanded nickel screen. The separator was Mead 934-5 fiberglass material.

Halpert, S.↗

NASA NTRS1984

Characterization of Glass Fiber Separator Material for Lithium Batteries

Characterization studies were carried out on a glass fiber paper that is currently employed as a separator material for some LiSOCl2 primary cells. The material is of the non-woven type made from microfilaments of E-type glass and contains an ethyl acrylate binder. Results from extraction studies and tensile testing revealed that the binder content and tensile strength of the paper were significantly less than values specified by the manufacturer. Scanning electron micrographs revealed the presence of clusters of impurities many of which were high in iron content. Results of emission spectroscopy revealed high overall levels of iron and leaching, followed by atomic absorption measurements, revealed that essentially all of this iron is soluble in SOCl2.

Subbarao, S.↗