Microstructural evaluation of the creep behavior in L-PBF Ni-based superalloys

This presentation at ICAM 2024 Conference focuses on the commonalities and differences in the creep rupture behavior and creep mechanisms for three distinct classes of laser powder-bed fusion (L-PBF) Ni-based superalloys (γ’-precipitate strengthened Haynes® 282®, γ’/γ”/δ-precipitate strengthened Alloy 718, and solid-solution strengthened Alloy 625) as compared to conventionally processed counterparts. A comparison of Larson-Miller parameter plots establishes that these alloys perform statistically within the bounds established for the wrought product, despite having dissimilar microstructural features and other artefacts associated with PBF-LB manufacturing and post-processing heat treatment. To understand the failure and the impact of composition, minor phases, and deformation defects on creep behavior, the fractography has been performed and microstructures have been evaluated in detail with SEM-EDS, EBSD, and HAADF-STEM. The underlying diffusional and dislocation creep mechanisms associated with this microstructural evaluation is discussed. This work is supported by NETL-FWP-1022408 Advanced Turbines.

Sudbrack, Chantal↗
DOE OSTI2024

Characterization of build parameters and microstructure in low heat input WAAM of Ni-based superalloy Haynes 282

Conference paper for 2024 10th International Conference on Advances in Materials, Manufacturing & Repair for Power Plants. Ni-based superalloy Haynes 282 is a prime candidate for advanced power generation systems due to its superior fabricability, weldability, and high-temperature performance. Additive manufacturing offers potential cost and time savings for gas turbine components. Wire-arc direct energy deposition can create large components but often requires post-processing treatments, such as hot isostatic pressing (HIP), to address porosity. This study explores a low heat-input, high deposition rate GMAW process to achieve fully dense Haynes 282 without HIP. Twenty-one blocks were deposited, varying travel and wire feed speeds. Initial analysis (visual inspection, microstructural examination, and CT) revealed the impact of build parameters on internal porosity and defects. Scanning electron microscopy provided insights into structural heterogeneity and microstructural properties. Related journal article can be found at https://doi.org/10.31399/asm.cp.am-epri-2024p0001.

Adam, Benjamin↗
DOE OSTI2024

Rapid Design of Cost-Effective Refractory High Entropy Alloys Strengthened by Precipitation

Funded by the ARPA-E ULTIMATE program, this project aims to develop cost-effective refractory high entropy alloys (RHEAs) for gas turbine blades applications at 1300 degree Celsius and above. The alloy design focuses on carbides precipitation strengthening in a strong and ductile solid solution BCC matrix. The goal is to achieve balanced mechanical properties including room temperature ductility & fracture toughness and high temperature strength and creep resistance, while maintaining comparable oxidation resistance and densities to Ni-base superalloys. To accelerate alloy design, multiscale modeling including CALPHAD and first-principles density functional theory (DFT) calculations and machine learning are performed. Specifically, high throughput phase diagram calculations and screening are carried out using CALPHAD; DFT calculations are performed to predict intrinsic ductility, grain boundary strengthening potential, coefficient of thermal expansion (CTE) and temperature-dependent elastic constants. Temperature dependent yield stress, creep strain and CTE are also predicted using machine learning. Down-selected alloys are synthesized in small buttons of about 250g using arc melting for rapid evaluation on microstructure and mechanical properties before employing plasma arc melting and additive manufacturing for producing large ingots. Preliminary computational and experimental results of this project will be presented and future direction in RHEA development will be discussed.

high temperature materials↗
DOE OSTI2024

Aging heat treatment design for Haynes 282 made by wire-feed additive manufacturing using high-throughput experiments and interpretable machine learning

Wire-feed additive manufacturing (WFAM) produces superalloys with complex thermal cycles and unique microstructures, often requiring optimized heat treatments. To address this challenge, we present a hybrid approach that combines high-throughput experiments, precipitation simulation, and machine learning to design effective aging conditions for the WFAM Haynes 282 superalloy. Our results demonstrate that the γ’ radius is the critical microstructural feature for strengthening Haynes 282 during post-heat treatment compared with the matrix composition and γ’ volume fraction. New aging conditions at 770°C for 50 hours and 730°C for 200 hours were discovered based on the machine learning model and were applied to enhance yield strength, bringing it on par with the wrought counterpart. This approach has significant implications for future AM alloy production, enabling more efficient and effective heat treatment design to achieve desired properties.

CALPHAD↗
NASA NTRS2019

Discerning the Impact of Powder Feedstock Variability on Structure, Property, and Performance of Selective Laser Melted Alloy 718: A Principal Component Analysis (PCA) of Feedstock Variability

Extensive mechanical, chemical and microstructural analyses were conducted on additively manufactured Alloy 718 to characterize powders from multiple vendors to determine the effects of variations observed in the powders had on the consolidated material. With over 190 variables examined, it was necessary to reduce the number of variables and identify the variables and classes of variables that had the greatest effect. Principle Component Analysis (PCA) was used to reduce the number of variable to effectively 12 while identifying several classes of variables as most important.

Ellis, David↗
NASA NTRS2018

Impact of Powder Variability on the Microstructure and Mechanical Behavior of Selective Laser Melted (SLM) Alloy 718

Nickel Alloy 718 has found wide use in high-temperature aerospace applications (up to 700°C), due to a combination of good mechanical properties, environmental resistance, and workability at moderate cost. These properties have led Alloy 718 to early adoption by selective laser melting (SLM) additive manufacturing. This presentation will share results from a comprehensive industry survey of 718 powder feedstock for SLM. The survey focuses on the impact of variability in powder characteristics on build quality, microstructure, tensile and high cycle fatigue in the as-fabricated and machined surface conditions. The investigation includes sixteen powder lots from eight suppliers that are produced by gas atomization or rotary atomization in argon or nitrogen. This research was previously presented and published at the 9th International Symposium on Superalloy 718 & Derivatives and was funded by NASA Space Launch System Liquid Engine Office with the Human Exploration Operations Mission Directorate.

Sudbrack, Chantal↗
NASA NTRS2018

Fatigue Characteristics of Additively Manufactured Aerospace Materials

This presentation documents the fatigue properties of three additive manufactured (AM) metallic systems (Ti-6-4, GRC op-84, and Alloy 718) used by NASA in various aerospace applications. These alloys were produced using the powder bed method, with the titanium alloy using an electron beam melting (EBM) and the other two alloys using selective laser melting systems (SLM). For each material a large matrix of fatigue tests were conducted and the fatigue characteristics compared to their conventionally manufactured counterparts. Build orientations and resulting microstructures are discussed with respect to the tested mechanical properties.

Lerch, Brad↗
NASA NTRS2017

Coatings for Oxidation and Hot Corrosion Protection of Disk Alloys

Increasing temperatures in aero gas turbines is resulting in oxidation and hot corrosion attack of turbine disks. Since disks are sensitive to low cycle fatigue (LCF), any environmental attack, and especially hot corrosion pitting, can potentially seriously degrade the life of the disk. Application of metallic coatings are one means of protecting disk alloys from this environmental attack. However, simply the presence of a metallic coating, even without environmental exposure, can degrade the LCF life of a disk alloy. Therefore, coatings must be designed which are not only resistant to oxidation and corrosion attack, but must not significantly degrade the LCF life of the alloy. Three different Ni-Cr coating compositions (29, 35.5, 45wt. Cr) were applied at two thicknesses by Plasma Enhanced Magnetron Sputtering (PEMS) to two similar Ni-based disk alloys. One coating also received a thin ZrO2 overcoat. The coated samples were also given a short oxidation exposure in a low PO2 environment to encourage chromia scale formation. Without further environmental exposure, the LCF life of the coated samples, evaluated at 760C, was less than that of uncoated samples. Hence, application of the coating alone degraded the LCF life of the disk alloy. Since shot peening is commonly employed to improve LCF life, the effect of shot peening the coated and uncoated surface was also evaluated. For all cases, shot peening improved the LCF life of the coated samples. Coated and uncoated samples were shot peened and given environmental exposures consisting of 500 hrs of oxidation followed by 50 hrs of hot corrosion, both at 760C). The high-Cr coating showed the best LCF life after the environmental exposures. Results of the LCF testing and post-test characterization of the various coatings will be presented and future research directions discussed.

LCF life↗
NASA NTRS2014

Fabrication of Turbine Disk Materials by Additive Manufacturing

Precipitation-strengthened, nickel-based superalloys are widely used in the aerospace and energy industries due to their excellent environmental resistance and outstanding mechanical properties under extreme conditions. Powder-bed additive manufacturing (AM) technologies offer the potential to revolutionize the processing of superalloy turbine components by eliminating the need for extensive inventory or expensive legacy tooling. Like selective laser melting (SLM), electron beam melting (EBM) constructs three-dimensional dense components layer-by-layer by melting and solidification of atomized, pre-alloyed powder feedstock within 50-200 micron layers. While SLM has been more widely used for AM of nickel alloys like 718, EBM offers several distinct advantages, such as less retained residual stress, lower risk of contamination, and faster build rates with multiple-electron-beam configurations. These advantages are particularly attractive for turbine disks, for which excessive residual stress and contamination can shorten disk life during high-temperature operation. In this presentation, we will discuss the feasibility of fabricating disk superalloy components using EBM AM. Originally developed using powder metallurgy forging processing, disk superalloys contain a higher refractory content and precipitate volume fraction than alloy 718, thus making them more prone to thermal cracking during AM. This and other challenges to produce homogeneous builds with desired properties will be presented. In particular, the quality of lab-scale samples fabricated via a design of experiments, in which the beam current, build temperature, and beam velocity were varied, will be summarized. The relationship between processing parameters, microstructure, grain orientation, and mechanical response will be discussed.

oxidation↗