Publications and source records attributed to Sulejmanovic, Dino.

15 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Electrochemically Assisted Single Crystal Growth of Reduced Preyssler Polyoxometalates Decorated with M 2+ ( M = Co, Ni) and Cubane–Like Ni 4 O 4 Units

Polyoxometalates (POMs) are of great interest to the scientific community, and their reduction and nucleation have been well–established by multi–step techniques. The present study develops an electrochemical approach for simultaneous reduction and nucleation of polyoxometalate–containing solids. Herein we report crystal growth of reduced Preyssler polyoxotungstate–based (anionic formula [NaP 5 W 30 O 110 ] 14– ) new crystalline solids made of Preyssler anions interlinked by Co 2+ and Ni 2+ ions. Crystal nucleation and in situ reduction were achieved at room temperature using a two silver wire electrode setup in various aqueous solutions under constant applied potentials. The POM material was deposited on the cathode, and its structure was characterized by X–ray diffraction techniques. The primary structure type observed involves POMs decorated by disordered Co 2+ /Ni 2+ octahedra and fused into 1–D pillars by additional Co 2+ /Ni 2+ octahedra. Additionally, a secondary phase was observed in the Ni–based reactions, where reduced Preyssler anions are decorated by Ni 4 O 4 cubane–like units. To understand the electrochemical process, polarization curves of the electrolyte solutions are presented, suggesting an applied potential best suited for crystal growth. The work highlights the effectiveness of an electrochemical pathway where nucleation and simultaneous reduction of POMs can make novel reduced POM solids.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2024

Materials Assessment for FLiBe Fusion Blankets

This evaluation was prepared at the request of DOE-FES and expands on an earlier evaluation prepared by Wilson, Wiffen and Keiser in 2015 (attached as Appendices A and B). Additional useful information for materials in fission molten salt reactor systems that use FLiBe can be found in a prior NRC report [Busby 2019]. The purpose of this report is to review the considerations that will determine the fusion blanket structural materials that will be suitable for use in a FLiBe breeder-coolant fusion power plant (FPP). Identifying a fusion-relevant structural material that is sufficiently compatible with FLiBe is a key issue to be addressed. The constraints and trade-offs made in structural materials selection include the usual power generation requirements such as mechanical properties, fabricability and durability, which assumes reasonable compatibility with the working fluid. For an FPP, additional constraints include neutron economy (breeding ratio), resistance to irradiation damage and low activation (i.e. waste disposal) characteristics.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Density Measurements of Molten LiF–BeF 2 and LiF–BeF 2 –LaF 3 Salt Mixtures by Neutron Radiography

The densities of eutectic (LiF) 2 –BeF 2 and mixtures of this salt (FLiBe) with LaF 3 were measured by dilatometry and by neutron attenuation from 673 K to 1,073 K. Because LaF 3 has a limited solubility in FLiBe, it was necessary to determine the amount of LaF 3 in solution before the density could be determined. The FLiBe density determination was favorably benchmarked against the literature data. A simple comparison was not available for the LaF 3 –FLiBe mixtures, so extrapolation of published data was necessary based on analysis using the Molten Salt Thermal Properties Database-Thermochemistry, or MSTDB-TC, developed by the US Department of Energy. Solubilities for LaF 3 in FLiBe ranged from 1 to 4 mol % over 673 to 1,073 K. The salt system was heated and cooled over 24 h to evaluate potential changes in composition and hysteresis during the measurement. Changes in the meniscus were observed, and these were included in the correction for density determinations. Salt surface tension may have led to supersaturation of LaF 3 in the salt because the solubility curve was nonlinear with respect to the inverse temperature, as would be expected for an ideal system. Surface tension measurements are currently underway to test this hypothesis.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

Graphite-Salt Interactions: Summary of FY23 Activities

This report summarizes the research activities related to graphite–molten salt interactions during FY 2023. It includes results of FLiNaK infiltration experiments under various operating conditions, such as different temperatures, pressures, and times, to understand the effect of each condition on a variety of nuclear-grade graphites. Six graphite grades with various origins and properties were selected for the intrusion experiments using molten FLiNaK. The effect of intrusion pressure, temperature, and time were evaluated by measuring weight uptake, and the extent of penetration was studied using neutron tomography (n-CT). In addition, the wetting behavior of molten FLiNaK on a graphite surface was studied by measuring the contact angle on various grades of graphite. The results obtained by n-CT and contact angle measurements will help advance the understanding of factors that control the salt penetration in graphite and their relationship with intrinsic structural properties of the various graphite grades.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Characterization and Electrochemical Analysis of Acidic Condensate-Induced Corrosion on Aluminized Coating on Steel in Residential Heaters

Condensing furnace residential heaters are starting to replace outdated and less efficient non-condensing units in homes across the US. However, the burning of natural gas in these new units produces acidic gases, which can form acid droplets (H 2 SO 4 , HNO 3 , H 2 CO 3 , etc.) that are corrosive to low-grade heat exchanger metallic materials. Type-1 aluminized steel has been used in industrial applications, such as marine, heating, and automobile parts, due to its resistance to oxidation at elevated temperature. Many components of the condensing furnaces, including heat exchangers, are made from type-1 aluminized steel. We investigated the interaction of type-1 aluminized steel substrates with two acidic condensate liquids by 500 h corrosion exposures as well as short-term electrochemical impedance measurements. SEM plan and cross-sectional view images revealed damage to the Al-Si rich layer and exposure of the steel substrate. The non-uniform damage in the Al-Si rich layer was likely attributed to a pitting corrosion mechanism and induced by high acidity of the condensate liquid. Electrochemical impedance measurements in an acidic condensate revealed lower corrosion resistance of the aluminized steel surface with a weld line, identifying welded sections as preferential corrosion initiation sites.

36 MATERIALS SCIENCE↗
DOE OSTI2023

The Dissolution of Cr and Fe at 850°C in FLiNaK and FLiBe

Understanding the solubility of common alloying elements, such as Cr and Fe, in fluoride salts, can provide valuable insights into the degradation process of alloys in these salts and assist in modeling the attack observed in static and flowing conditions. Previous isothermal dissolution experiments at 550°-750°C in FLiNaK showed little effect of time or temperature on the amount of dissolution, which was not expected. Therefore, the purpose of this milestone was to extend those observations to 850°C where Ni-based alloys have been developed with 100+X better creep strength than the historic Hastelloy N alloy developed for molten salt reactors more than 50 years ago. Exposures were conducted in the same commercial FLiNaK and FLiBe salts used in the lower temperature exposures.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Measuring the Dissolution of Cr and Fe at 550°-750°C in FLiNaK and FLiBe

Assessing the compatibility of 316H stainless steel with molten fluoride salts has been identified as a key research topic for molten salt reactor development. Current developers are interested in 316H stainless steel due to its ready availability and ASME code qualification. Previous studies of 316H stainless steel compatibility in molten fluoride salts have shown general agreement that Cr is selectively removed from the alloy during the exposures in molten salts. However, the extent of Cr dissolution depends on the initial purity of the salt and Fe also readily dissolves in the salt. In order to model dissolution, it is necessary to understand how time and temperature affect the dissolution rates of the alloying elements which may lead to saturation of these elements in the salt. To study the dissolution of 316H, Cr and Fe specimens were exposed in FLiNaK and LiFBeF2 (FLiBe) salt at three different temperatures (550°-750°C) and three different durations (100-2000 h) in isothermal capsule experiments.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Be 2 C synthesis, properties, and ion-beam irradiation damage characterization

This technical report is in submission of completion of the Level 2 milestone number M2AT 23OR1101022, titled “Be 2 C synthesis, properties, and ion-beam irradiation damage characterization,” for the AT-23OR110102 “Beryllium Carbide as moderator for MSRs—ORNL” WBS number 2.04.11.01 within the larger Advanced Reactor Technologies program at Oak Ridge National Laboratory. This effort is an initial study of the viability of Be 2 C as a future neutron moderator for molten salt reactors and other high-temperature reactors. The research was awarded funding in September 2022, and this Level 2 milestone presents the work that completed by the end of July 2023. This work is a collaboration between Oak Ridge National Laboratory and the University of Michigan. This report discusses the status of this effort and planned work before the final reporting.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2023

Evaluation of Corrosion Behavior of Various Fe- and Ni-Based Alloys in Molten Li 2 BeF 4 (FLiBe)

Reliable performance of structural alloys is essential for the successful implementation of Generation-IV fluoride salt–cooled high-temperature reactors (FHRs). Most FHR designs are considering molten salt (2LiF-BeF 2 ), or FLiBe, as a primary coolant or fuel carrier. The main corrosion mechanism for alloys exposed to molten fluoride salts is the selective dealloying of active alloying elements. Alloy composition has a significant effect on their high-temperature mechanical properties, but also affects their corrosion behavior. Although Hastelloy-N and its variants show good corrosion resistance compared to higher Cr-containing Ni- or Fe-based alloys, the mechanical properties of these alloys degrade quickly at temperatures above ~600°C. Twelve Ni-based or Fe-based alloys were selected due to their high temperature stability or their low Cr alloy composition and tested for their corrosion behavior in FLiBe. The results show that the mode and the extent of alloy degradation by selective dissolution mechanism corelates well with the overall alloy composition, and not just the concentration of active elements. It was found that there was good correlation between weight loss of the tested alloys and the ratio of major active elements (Cr, Mn) to that of the more noble alloying elements (Ni, Mo).

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2023

A neutron tomography study to visualize fluoride salt (FLiNaK) intrusion in nuclear-grade graphite

Manufactured graphite is a preferred material for in-core components of molten salt reactors and fluoride salt-cooled high-temperature reactors, which are in permanent contact with liquid salts. However, owing to the porous nature of nuclear graphite, under certain conditions, molten salts may intrude graphite's pores and affect graphite's properties and functionality. Therefore, a better understanding of molten salt intrusion (distribution across sample cross section and penetration depth) is needed to assess its effects. Here, in this work, we have demonstrated the use of neutron imaging (computed tomography) in the evaluation of salt penetration and distribution of a wide range of graphite grades with diverse microstructures that have been subjected to FLiNaK (LiF–NaF–KF) intrusion at 750 °C and 5 bar pressure for 12 h. Because of the great neutron attenuation contrast from scattering and adsorption between Li (from FLiNaK) and the graphite matrix, we have obtained direct visualization of FLiNaK salt distribution in the salt-impregnated graphites for the first time. Three-dimensional reconstructed images and cross-sectional concentration profiles demonstrate that salt penetration and density distribution are greatly dependent on the microstructural properties of the graphite grade.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2023

Characterization of Fe and Cr Dissolution and Reaction Product Formation in Molten Chloride Salts With and Without Impurities

There is considerable interest in molten chloride salts for several applications including thermal storage and next-generation molten salt reactors (MSRs). Several studies have concluded that Cl salts are highly corrosive to structural materials. Using Oak Ridge National Laboratory’s established methodology, Cl salt compatibility was assessed for candidate Ni-based alloys 230, 600 and 740 H at 600°–800°C in static welded capsules and in flowing thermal convection loop (TCL) salt experiments. Simply drying commercial Cl salt at 550°–650°C and adding~0.05 wt.%Mg was able to produce small specimen mass changes and limited surface attack after 100–1000 h exposures. Intentional additions of H 2 O, NiCl 2 and undried salt were used to better understand the role of impurities and achieve the>50 µm levels of attack reported in other studies. Further, characterisation of Cr depletion and oxide formation in conjunction with pre- and post-test salt chemistry measurements are being used to understand salt compatibility of structural materials.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Tribocorrosion of stainless steel sliding against graphite in FLiNaK molten salt

The molten salt reactor (MSR) concept recently gained renewed interest in developing Generation IV nuclear reactors. One MSR design uses fluoride molten salts to cool tri-structural isotropic particle fuel encapsulated by a carbon matrix into spherical pebbles, which would inevitably contact the reactor's stainless steel container wall during salt circulation. Characterizing this interaction is crucial for reactor safety. Here, in this work, we report the tribocorrosion behavior of graphite sliding against Type 316H stainless steel lubricated by a FLiNaK (LiF:NaF:KF; 46.5:11.5:42 mol %) molten salt in an argon environment. Accelerated wear loss was observed at a higher temperature because of a lower molten salt viscosity and a higher corrosion rate. The graphite had a more rapid material loss at a higher sliding speed than stainless steel because of its higher vulnerability to vibration-induced microfracture. The salt-starved condition caused more material loss than either the no-salt or the salt-flooded condition because neither a graphite transfer film nor stable boundary lubrication could be established at salt starvation. An interesting dual-layer surface film was discovered on the stainless steel worn surface: a chromium-rich top film and a nickel-accumulated but chromium-depleted interlayer. The film composition and structure provide fundamental insights to the mechanochemical interactions between stainless steel and graphite in a molten salt environment.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2023

Corrosion Testing Trade Study on Testing Methods in Molten Salts

In assessing molten salt compatibility with structural materials, static testing is often reported because it is easy to conduct. However, in order to assess mass transfer, where material dissolves in the salt in the hot section and may precipitate out of the liquid in colder regions, a flowing salt experiment in a temperature gradient is needed. While a forced convection or pumped loop produces prototypic flowing conditions, it also is a multi-million dollar investment. Among the less expensive dynamic testing options, the thermal convection loop (TCL) was favored during the 1960’s development of molten salt reactor technology. Because the workforce and core facilities are currently available to conduct TCL experiments, it is the least expensive strategy to evaluate candidate structural alloys in flowing molten salt conditions.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Performance of Structural Alloys in Bio-oil Production, Upgrading, and Storage Systems

Selection of corrosion-resistant, cost-effective structural materials for the process and containment vessels required for the production, upgrading, and storage of biomass-derived oils has been the subject of study in our laboratory for many years. The wide variety of biomass resources and the many liquefaction techniques and processing conditions result in products with a broad range of properties and compositions. Here, this paper will address the materials issues in three distinct areas. In production, materials are exposed to temperatures that range from 350 to 550 °C depending upon the process. Generally, austenitic stainless steels have performed reasonably well, although thicker oxide scales and intergranular attack have sometimes been observed. For storage and transport of the bio-oil products, temperatures experienced by the containment materials are not expected to exceed 50 °C. Our studies have shown that most raw bio-oils contain significant concentrations of organic acids, and low-molecular-weight organic acids were quite corrosive to carbon and low alloy steels. For some applications, subsequent processing is required, which includes hydrotreating or co-processing with a petroleum-derived liquid. These processes utilize a catalyst that requires periodic retreatment with a sulfidizing gas, and the exposure to this gas at elevated temperatures can cause appreciable corrosion to the more common austenitic stainless steels. The materials considered most cost-effective and sufficiently corrosion-resistant for each of these environments were identified.

36 MATERIALS SCIENCE↗