Detection of a Cobalt-Containing Interphase at the Li 6 PS 5 Cl-NMC111 Interface by In Situ μ XANES and EIS

Sulfide electrolyte all-solid-state lithium batteries (ASLBs) with uncoated Li-Ni x Mn y Co 1–x–y O 2 (NMC) cathodes suffer from a large capacity loss during initial cycling and an increase in cell impedance. Decomposition reactions are known to occur at the Li 6 PS 5 Cl-NMC111 interface due to incompatibility between the two materials. If a stabilizing coating is applied to the NMC, it delivers full capacity during initial charge. However, the loss in capacity during discharge still occurs. The interface was studied by μ XANES and through EIS analysis. A chemically-formed interphase was detected by μ XANES, evident from reduction of Co at an uncoated NMC particle surface. This interphase was produced by decomposition at rest. To study the effect of the interphase on electrochemically active surface area, piecewise in situ EIS was performed and the data was modeled using a transmission line model (TLM). The charge transfer resistance R CT was used to estimate the volume specific active surface area (a act ). The median value for a act was 296 cm –1 , a factor of 7.5 lower than the theoretical value of 2216 cm –1 . This provided evidence of a lower electrochemically active surface area in the ASLB.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Understanding Electrochemical Reaction Mechanisms of Sulfur in All‐Solid‐State Batteries through Operando and Theoretical Studies **

Abstract Due to its outstanding safety and high energy density, all‐solid‐state lithium‐sulfur batteries (ASLSBs) are considered as a potential future energy storage technology. The electrochemical reaction pathway in ASLSBs with inorganic solid‐state electrolytes is different from Li‐S batteries with liquid electrolytes, but the mechanism remains unclear. By combining operando Raman spectroscopy and ex situ X‐ray absorption spectroscopy, we investigated the reaction mechanism of sulfur (S 8 ) in ASLSBs. Our results revealed that no Li 2 S 8, Li 2 S 6, and Li 2 S 4 were formed, yet Li 2 S 2 was detected. Furthermore, first‐principles structural calculations were employed to disclose the formation energy of solid state Li 2 S n (1≤ n ≤8), in which Li 2 S 2 was a metastable phase, consistent with experimental observations. Meanwhile, partial S 8 and Li 2 S 2 remained at the full lithiation stage, suggesting incomplete reaction due to sluggish reaction kinetics in ASLSBs.

Cao, Daxian↗

DOE OSTI2023

Understanding Electrochemical Reaction Mechanisms of Sulfur in All‐Solid‐State Batteries through Operando and Theoretical Studies **

25 ENERGY STORAGE↗

DOE OSTI2023

Manufacturing Water‐Based Low‐Tortuosity Electrodes for Fast‐Charge through Pattern Integrated Stamping

Achieving high energy density and fast charging of lithium‐ion batteries can accelerate the promotion of electric vehicles. However, the increased mass loading causes poor charge transfer, impedes the electrochemical reaction kinetics, and limits the battery charging rate. Herein, this work demonstrated a novel pattern integrated stamping process for creating channels in the electrode, which benefits ion transport and increases the rate performance of the electrode. Meanwhile, the pressure applied during the stamping process improved the contact between electrode and current collector and also enhanced the mechanical stability of the electrode. Compared to the conventional bar‐coated electrode with the same thickness of 155 μm (delivered a discharge capacity of 16 mAh g −1 at the rate of 3 C), the stamped low‐tortuosity LiFePO 4 electrode delivered 101 mAh g −1 capacity. Additionally, water was employed as a solvent in this study. Owing to its eco‐friendliness, high scalability, and minimal waste generation, this novel stamping technique inspire a new method for the industrial‐level efficient roll to roll fabrication of fast‐charge electrodes.

25 ENERGY STORAGE↗

DOE OSTI2023

Lithiation Gradients and Tortuosity Factors in Thick NMC111-Argyrodite Solid-State Cathodes

Achieving high energy density in all-solid-state lithium batteries will require the design of thick cathodes, and these will need to operate reversibly under normal use conditions. We use high-energy depth-profiling X-ray diffraction to measure the localized lithium content of Li 1-x Ni 1/3 Mn 1/3 Co 1/3 O 2 (NMC111) through the thickness of 110 μm thick composite cathodes. The composite cathodes consisted of NMC111 of varying mass loadings mixed with argyrodite solid electrolyte Li 6 PS 5 Cl (LPSC). During cycling at C/10, substantial lithiation gradients developed, and varying the NMC111 loading altered the nature of these gradients. Microstructural analysis and cathode modeling showed this was due to high tortuosities in the cathodes. This was particularly true in the solid electrolyte phase, which experienced a marked increase in tortuosity factor during the initial charge. Our results demonstrate that current distributions are observed in sulfide-based composites and that these will be an important consideration for practical design of all-solid-state batteries.

25 ENERGY STORAGE↗

DOE OSTI2023

High Ion Conductive and Selective Membrane Achieved through Dual Ion Conducting Mechanisms

Conventional ion-selective membranes, that is ion-exchange and porous membranes, are unable to perform high conductivity and selectivity simultaneously due to the contradictions between their ion selecting and conducting mechanisms. Here, in this work, a bifunctional ion-selective layer is developed via the combination of nanoporous boron nitride (PBN) and ion exchange groups from Nafion to achieve high ion conductivity through dual ion conducting mechanisms as well as high ion selectivity. A template-free method is adopted to synthesize flake-like PBN, which is further enmeshed with Nafion resin to form the bifunctional layer coated onto a porous polyetherimide membrane. The double-layer membrane exhibits excellent ion selectivity (1.49 × 10 8 mS cm –3 min), which is 22 times greater than that of the pristine porous polyetherimide membrane, with outstanding ion conductivity (64 mS cm –1 ). In a vanadium flow battery, the double-layer membrane achieves a high Coulombic efficiency of 97% and outstanding energy efficiency of 91% at 40 mA cm –2 with a stable cycling performance for over 700 cycles at 100 mA cm –2 . PBN with ion exchange groups may therefore offer a potential solution to the limitation between ion selectivity and conductivity in ion-selective membranes.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Opening twisted polymer chains for simultaneously high printability and battery fast-charge

Fast-charging is key to the widespread adoption of battery-based electric vehicles. However, improving fast-charging through architecture optimization is expensive. To reduce costs and expand to commercialization, we applied roll-to-roll screen printing technology to create channels and decrease the tortuosity of electrodes. For the first time, this work successfully opened twisted polymer chains within high-solid-content inks to improve their screen printability and battery performance of as-printed electrodes. With LiNi 0.6 Mn 0.2 Co 0.2 O 2 as active materials, the 60% solid content ink presents superior screen printability after opening the twisted binder chains. As-printed electrode exhibits 33% higher charge capacity at 6 C than printed electrode with chains twisted ink at mass loading of 6.5 mg/cm 2 . Furthermore, coarse-grained molecular dynamics simulations are performed to study the underlying mechanism systematically. In conclusion, the new ink preparation procedure provides a scalable, effective strategy for manufacturing screen-printable battery ink and promotes screen-printed electrode technology.

25 ENERGY STORAGE↗

DOE OSTI2022

Molecular Engineering of Biorefining Lignin Waste for Solid-State Electrolyte

Lignin is the second most abundant renewable biopolymer on Earth but also a waste in both the paper industry and lignocellulosic biorefineries. Recently, lignin valorization has been extensively sought after to return economics, enhance carbon efficiency, and improve the bioeconomy, but the commercial value and size compatibility still hinder its applications. In this study, we developed a facile strategy to apply lignin waste into a solid-state electrolyte (SSE), which represents a safe next generation energy storage. Here, lignin was grafted with polyethylene glycol (PEG), an efficient lithium-ion (Li + ) conductive polymer, to enable its ion conduction. The synthesized PEG-g-lignin was mixed with poly(vinylidene fluoride)-co-hexafluoropropylene (PVDF-HFP) and PEG-g-lignin-based bis(trifluoromethanesulfonyl)imide (LiTFSI) to prepare a solid polymer electrolyte (SPE), which has an ionic conductivity of 2.5 × 10 –5 S/cm at 25 °C. This result was further enhanced to 6.5 × 10 –5 S/cm by adding an ion-conductive ceramic of Li 6.4 La 3 Ga 0.2 Zr 2 O 12 (LLGZO), which is referred to as composite polymer electrolyte (CPE). These data represent the highest ones among reported polymer-based SSE. A mechanistic study by using 2D HSQC NMR revealed that PEG-g-lignin has increased ether type β–O–4 linkages that can promote the interchain hopping of Li+ between lignin polymer chains, and 31 P NMR revealed that the lignin phenolic end can be associated by Li + . Moreover, the abundant aromatic moieties and methoxyl in PEG-g-lignin also enhanced Li + association and improved its ionic conductivity. The superior ionic conductivity of PEG-g-lignin-based SSE can enable massive applications of this biorefining waste in all-solid-state lithium batteries (ASSLBs), which has potential to promote the energy sector by promoting the bioeconomy and enhancing the renewability and sustainability of future energy storage.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2022

Long–Cycling Sulfide–Based All–Solid–State Batteries Enabled by Electrochemo–Mechanically Stable Electrodes

Anode significantly determines the energy density of all-solid-state Lithium batteries (ASLBs). Silicon (Si) and Lithium (Li) metal are two of the most attractive anodes because of their ultrahigh theoretical capacities. However, most investigations focus on Li metal; the great potential of Si is underrated. This study investigates Si anode's stability, processability, and cost in ASLBs and compares them with Li metal. Moreover, the single-crystal LiNi 0.8 Co 0.1 Mn 0.1 O 2 is stabilized with a lithium silicate (Li 2 SiO x ) through a scalable sol-gel method. ASLBs with a cell-level energy density of 285 Wh kg -1 are obtained through sandwiching Si anode, thin sulfide solid-state electrolyte membrane, and interface stabilized LiNi 0.8 Co 0.1 Mn 0.1 O 2 . The full cell delivered a high capacity of 145 mAh g -1 at C/3 and maintained stability for 1000 cycles. This work inspires commercializing the ASLBs on a large scale with exciting manufacturing lines for large-scale, safe, and economical energy storage.

25 ENERGY STORAGE↗