Hard carbon with an opened pore structure for enhanced sodium storage performance

The pore structure of hard carbon has a significant impact on its Na + storage capacity. Herein, a waste wood-derived hard carbon with opened pores (OP-HC) was fabricated with polyvinyl pyrrolidone (PVP) as an additive. Ex situ SAXS and HR-TEM testing results indicate that OP-HC with opened pores and enlarged d 002 interlayer spacing facilitates the reversible (de)sodiation of Na + ions. In situ TEM and XRD testing results demonstrate that OP-HC shows excellent structure stability during the (de)sodiation process. Thus, OP-HC delivers a high reversible charge capacity of 350.7 mA h g −1 at 0.05 C and an ultra-high initial Coulombic efficiency (ICE) of 94.9%. Moreover, OP-HC exhibits excellent cycling stability, and the assembled 18650 full cell with an OP-HC anode can achieve a high capacity retention of 94.5% after 400 cycles at 1.0 A. Furthermore, the excellent electrochemical performance and deep insights into OP-HC with opened pores and increased d 002 interlayer spacing offer a new strategy to design high-performance HC anodes for SIBs.

You, Shunzhang↗

DOE OSTI2023

Implanting Transition Metal into Li 2 O-Based Cathode Prelithiation Agent for High-Energy-Density and Long-Life Li-Ion Batteries

Compensating the irreversible loss of limited active lithium (Li) is essentially important for improving the energy-density and cycle-life of practical Li-ion battery full-cell, especially after employing high-capacity but low initial coulombic efficiency anode candidates. Introducing prelithiation agent can provide additional Li source for such compensation. Herein, we precisely implant trace Co (extracted from transition metal oxide) into the Li site of Li 2 O, obtaining (Li 0.66 Co 0.11$\square$0.23 ) 2 O (CLO) cathode prelithiation agent. Further, the synergistic formation of Li vacancies and Co-derived catalysis efficiently enhance the inherent conductivity and weaken the Li-O interaction of Li 2 O, which facilitates its anionic oxidation to peroxo/superoxo species and gaseous O 2 , achieving 1642.7 mAh/g ~Li2O prelithiation capacity (≈980 mAh/g for prelithiation agent). Coupled 6.5 wt % CLO-based prelithiation agent with LiCoO 2 cathode, substantial additional Li source stored within CLO is efficiently released to compensate the Li consumption on the SiO/C anode, achieving 270 Wh/kg pouch-type full-cell with 92 % capacity retention after 1000 cycles.

25 ENERGY STORAGE↗