The presence of Ru metal modifies the behavior of deuterium bound to pyridinic nitrogen in doped graphene-like materials
We used a combination of x-ray photoelectron spectroscopy (XPS) and density functional theory (DFT) to investigate how the presence of a ruthenium (Ru) metal substrate modifies the N-D bond strength of the pyridinic nitrogen species in nitrogen (N)-doped graphene (Gr) on Ru(0001) compared to metal-free highly-oriented pyrolytic graphite (HOPG) substrate. The N-dopants were introduced through low-energy N+/N2+ irradiation. N is embedded in the carbon materials in two predominant configurations: as graphitic N (GN: N substituted in the hexagonal C lattice) and pyridinic N (PN: substitutional N adjacent to a C vacancy). XPS data showed that upon atomic deuterium (D) exposure at 220 K, the PN peak shifted to a higher binding energy by +1.2 eV for HOPG and +1.0 eV for N-doped graphene on Ru(0001), while the GN peak remained unchanged, indicating that the D atoms bound solely to pyridinic N. 85% of PN sites on HOPG can be saturated with D atoms, whereas only ~30% of pyridinic N sites are able to bind D atoms in N-doped Gr/Ru(0001). Our DFT analysis shows that this difference is due to the coordination of PN to Ru atoms, which necessitates bond cleavage of the N-Ru interaction prior to D atom adsorption. D begins desorbing from N-HOPG at ~573 K and is fully desorbed by ~973 K, whereas desorption from N-doped graphene on Ru(0001) begins at ~290 K, with complete desorption observed at ~700 K, indicating that the Ru metal weakens the N-D bond strength. We also studied a high-surface-area, layered, and porous N-doped carbon material, internally labeled NC900, which was synthesized by pyrolysis of glucose and graphitic carbon nitride (g-C3N4) at 1173 K. D exposure caused a +1.1 eV PN peak shift in NC900, with no change in the GN peak. Moreover, the NC900 exhibited the same desorption behavior as HOPG, demonstrating that well-defined model systems can effectively capture the behavior of more complex N-doped carbon materials.