Hygrothermal aging and recycling effects on mechanical and thermal properties of recyclable thermoplastic glass fiber composites

Abstract Glass fiber‐reinforced polymer composites are widely used in marine applications, including renewable energy devices and submarines, due to their strength‐to‐weight ratios and corrosion resistance. As sustainability becomes more important, recyclable thermoplastic composites are gaining attention in marine energy applications. These materials face harsh conditions such as high chloride water, UV radiation, pressurization, and thermal cycling, which can affect their durability and recyclability. This study examines the impact of hygrothermal aging on the recyclability of an Elium glass fiber (GF) composite. Samples were mechanically ground for recycling, and mechanical and thermal properties were compared between aged and unaged samples. After seawater aging, the tensile strength and modulus of the unaged composite dropped by 25% and 13% respectively, due to water ingress along the fiber‐matrix interface. The recycled composite showed reduced flexural strength as the long fiber composite was converted into short fibers during the process. Differential scanning calorimetry (DSC) revealed no change in glass transition temperature after aging. Weight loss (25%) was attributed to the thermal stability of the glass fibers. Dynamic mechanical analysis (DMA) showed that the storage modulus increased with aging, and fracture analysis confirmed a mixed mode of failure for aged composites. Highlights Hygrothermal aging lowers mechanical performance of Elium® GF composites. Failure mechanism tends to be matrix cracking and interface bonding. Glass transition temperature is not reduced by hygrothermal aging. Fractured composite was successfully recycled via thermoforming. Flexural strength of the recycled composite is lower.

17 WIND ENERGY↗
DOE OSTI2024

SSTDR and FDR Detection of Un-Energized and Energized Cable Anomalies Including Thermal Degradation Using Machine Learning

Historically, cables are initially qualified for nuclear power plant use for 40 years. As plants extend their operating license to 60 and 80 years, continued use of these cables must shift to a performance-based approach since it is cost prohibitive to completely replace cables that are likely still capable of performing their design function. A variety of cable tests are available and are commonly applied during outages when the cables can be taken out of service. Frequency domain reflectometry (FDR) is one of these test methods that is being more broadly accepted and used because it not only detects anomalies along the cable with a low-voltage signal that does not stress the cable insulation, but the technique also locates the anomalies. This supports follow-up local inspection and local repair or partial replacement of a damaged cable segment. Currently, FDR testing is only applied to cables that are taken out of service since the test instrument would be damaged by operational voltages. A related technology that has found some acceptance in the aircraft and rail industry is spread spectrum time domain reflectometry (SSTDR). This technology has been implemented with a custom commercial instrument by LiveWire Innovation that is designed to operate on live cables up to 1000 volts and with a bandwidth of 48 MHz. Initial evaluation by the Pacific Northwest National Laboratory (PNNL) of the Live Wire system indicated that a broader bandwidth (BW) SSTDR may be better for many kinds of flaws. This led PNNL to develop an SSTDR laboratory instrument suitable for tests up to 500 MHz bandwidth. Testing on energized cables is also desirable for online monitoring systems so an inductive clamshell coupler was developed that allows energized cables to be tested up to at least 5 kV and likely higher voltage levels. Dielectric spectroscopy and tan delta testing plus various laboratory destructive tests were included in this data acquisition campaign directed to feed a machine learning (ML) study. With these kinds of developments, online energized cable tests may be possible with industrial adoption of such hardware advances but it will be completely impractical to have highly skilled data analysts continually examine these complex signals for indications of damage or compromised conditions. If online testing is to be implemented in new test hardware, it must be accompanied by software that can interpret the signals and alert plant operators of changing or degraded conditions. The thermally aged, shielded cable investigated here was separately treated for ML analysis. Visual analysis of electrical data showed generally increasing peaks where the cable entered and exited the oven. These peaks were not exactly aligned with expected locations, but these differences were attributed to velocity of propagation calibration errors. Only supervised ML was applied to the thermally aged data as this data was only available shortly before the committed publication date of this report. The supervised ML was structured to divide the 0 to 70-day responses as ‘normal’ from 0 to 35 days or ‘anomalous’ from 36 to 70 days, based on cable tensile elongation at break (EAB) insulation characterization. Using 80% of the data for training and 20% for testing, the supervised ML predicted normal versus anomalous was 70% accurate. Important conclusions include: • Accuracy to predict the presence of cable damage is improved from the 2023 effort by more training data. Weighted accuracies for comparisons among the instruments ranged from 67 to 89 % for unsupervised ML and 71 to 99% for supervised ML. • Based on the synthetic data tests, the unsupervised models are more generalizable to unseen anomalies. The Multi-Layer Perceptron classifier (MLP) model reported as high as 99.7% accuracy on the test data, but this dropped to 58.3% when tested on the synthetic data. In contrast, the unsupervised Pointwise model only achieved 89.7% accuracy on the experimental data but reported 78.3% accuracy on the synthetic data. • The best anomaly indicators are higher frequency (400 MHz BW) FDR data. Other tests may be interesting but for this study, this was the best predicter.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗
DOE OSTI2024

Thermal aging effects on crosslinked polyethylene cable insulation with decabromodiphenyl ether flame retardant alternative

Decabromodiphenyl ether (decaBDE) has been extensively used as a flame retardant in several applications, including nuclear electrical cable insulation. However, decaBDE has been identified as a persistent, bioaccumulative and toxic (PBT) substance, leading to regulatory scrutiny. The Environmental Protection Agency (EPA) published a regulation on January 6, 2021, aimed at phasing out the manufacturing, processing, and distribution of decaBDE. This rule set a compliance deadline of March 8, 2021, for the manufacture and processing of decaBDE, and an extended deadline of January 6, 2023, for specific applications including wire and cable insulation in nuclear power generation facilities. In response to such regulations, RSCC, a major supplier of safety-related electrical cables and associated products to the U.S. nuclear industry updated the formula of their crosslinked polyethylene (XLPE) insulation to replace the historically used decaBDE flame retardant with an acceptable alternative. This change from the previous decaBDE-containing XLPE prompted interest in comparative performance of the two material formulations, especially with respect to characteristics relevant to safety-related function such as thermal and radiation resistance. RSCC graciously provided samples of wire insulated with the decaBDE-containing XLPE formulation and corresponding wire insulated with XLPE of the new formulation, containing a decaBDE alternative. In this work we compare characteristics of the two formulations and a previously produced commercial version of the RSCC decaBDE-containing XLPE insulation subjected to thermal aging at 150 °C and 165 °C. The comparison was focused on mechanical durability, thermal stability in the oxidative environment, and chemical structures. Briefly, • Tensile elongation at break (EAB) results showed loss of mechanical elasticity with longer aging time, as expected. Aging time dependence of EAB did not differ between the decaBDE-containing and decaBDE-alternative samples. • Subtle differences between the two materials can be detected from Fourier-transform infrared spectroscopy (FTIR) absorbance spectra in the range below 1700 cm -1 , are assumed to be related to decomposition of flame retardant additives during thermal aging. • The oxidation induction time (OIT) data seemed to show that the unaged decaBDE-containing XLPE material is more thermally stable than the unaged decaBDE-alternative material, but the discrepancy in OIT decreased with aging time and the OIT values of the two materials became similar starting with the 4 th day of aging at 165 °C. This thermal aging investigation confirmed that the mechanical durability, a key property monitored for cable qualification, was not significantly affected by the modification of the formulation with a decaBDE alternative flame-retardant system in the investigated thermal aging conditions. Further studies on the same sets of materials exposed to thermal and gamma radiation aging would further inform comparison of the materials safety-related function.

36 MATERIALS SCIENCE↗
DOE OSTI2024

SSTDR and FDR Detection of Un-Energized and Energized Cable Anomalies Including Thermal Degradation Using Machine Learning

Historically, cables are initially qualified for nuclear power plant use for 40 years. As plants extend their operating license to 60 and 80 years, continued use of these cables must shift to a performance-based approach since it is cost prohibitive to completely replace cables that are likely still capable of performing their design function. A variety of cable tests are available and are commonly applied during outages when the cables can be taken out of service. Frequency domain reflectometry (FDR) is one of these test methods that is being more broadly accepted and used because it not only detects anomalies along the cable with a low-voltage signal that does not stress the cable insulation, but the technique also locates the anomalies. This supports follow-up local inspection and local repair or partial replacement of a damaged cable segment. Currently, FDR testing is only applied to cables that are taken out of service since the test instrument would be damaged by operational voltages.