Sutton, Austin T. | Search NASA

DOE OSTI2024

Spot pattern welding scanning strategy for sensor embedding and residual stress reduction in laser-foil-printing additive manufacturing

Here, this paper aims to present spot pattern welding (SPW) as a scanning strategy for laser-foil-printing (LFP) additive manufacturing (AM) in place of the previously used continuous pattern welding (CPW) (line-raster scanning). The SPW strategy involves generating a sequence of overlapping spot welds on the metal foil, allowing the laser to form dense and uniform weld beads. This in turn reduces thermal gradients, promotes material consolidation and helps mitigate process-related risks such as thermal cracking, porosity, keyholing and Marangoni effects. 304L stainless steel (SS) feedstock is used to fabricate test specimens using the LFP system. Imaging techniques are used to examine the melt pool dimensions and layer bonding. In addition, the parts are evaluated for residual stresses, mechanical strength and grain size. Compared to CPW, SPW provides a more reliable heating/cooling relationship that is less dependent on part geometry. The overlapping spot welds distribute heat more evenly, minimizing the risk of elevated temperatures during the AM process. In addition, the resulting dense and uniform weld beads contribute to lower residual stresses in the printed part. To the best of the authors’ knowledge, this is the first study to thoroughly investigate SPW as a scanning strategy using the LFP process. In general, SPW presents a promising strategy for securing embedded sensors into LFP parts while minimizing residual stresses.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Modeling powder spreadability in powder-based processes using the discrete element method

Powder-bed fusion (PBF) processes refer to a subset of Additive Manufacturing (AM) techniques where powder is spread on the build-plate before melting (by a laser or electron beam). While PBF processes are attractive due to their ability for realizing complex structures that are either difficult or impossible to create through conventional means, the parts fabricated with these techniques can exhibit defects such as pores, inclusions, and excessive surface roughness. To minimize these defects, much research has been dedicated towards process maturation by optimizing laser or electron beam parameters. However, these developmental efforts typically do not address the recoating process where achieving dense and uniform layers of powder is a necessity for ensuring process repeatability and part quality. While the recoating process can be studied through experimentation, the dynamics of particle movement are difficult to analyze experimentally. Therefore, here, in this study, powder spreading in PBF was simulated through the Discrete Element Method (DEM) to elucidate the mechanisms that control powder-bed quality. Utilizing the Buckingham Pi theorem, a dimensionless metric referred to as the spreading index is developed that combines powder-bed density, roughness, and particle size to assess the quality of powder layers. The formulated spreading index is then related to several dimensionless quantities that provide insight into the mechanisms dominating powder spreading in PBF. The DEM simulations conducted in this work focused on the scenario where powder is spread onto an existing powder bed and revealed that a reduction in the recoating velocity causes an increase in the spreading index while little to no impact on the spreading index was observed when varying layer thickness from 30 μm to 75 μm.Particle size effects on the powder-bed quality were also investigated.

36 MATERIALS SCIENCE↗