Swain, Santosh K.

Publications and source records attributed to Swain, Santosh K..

5 records

DOE OSTI2023

The Effect of Dopant Concentration and Annealing Treatments on N-Type Iodine Doped CdTe

We report properties of highly conducting n-type cadmium telluride single crystals doped with iodine (CdTe:I). These crystals were grown with dopant concentrations in the range of 10^17 cm-3 to 10^19 cm-3 by Modified Vertical Bridgman (MVB) melt growth. Post-growth dopant activation, including Cd annealing, Te annealing, and rapid thermal annealing (RTA), was applied to improve free carrier density. The structural, optical, and electrical properties were analyzed by Glow Discharge Mass Spectroscopy (GDMS), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), Photoluminescence Spectroscopy (PL), optical absorption, Hall measurements, Capacitance-Voltage (CV) measurements, and time-resolved photoluminescence (TRPL). The results indicate that Cd annealing is the most effective activation method to get 100% donor activation (n is approximately 2 x 10^18 cm-3), which is close to the room temperature solubility limit of iodine. This leads to the lowest resistivity and the highest mobility. Moreover, this data suggests a potential role of Cd vacancy-related defects on electrical self-compensation.

annealing↗

DOE OSTI2022

Impact of dopant-induced band tails on optical spectra, charge carrier transport, and dynamics in single-crystal CdTe

Abstract Cadmium telluride (CdTe) semiconductors are used in thin-film photovoltaics, detectors, and other optoelectronic applications. For all technologies, higher efficiency and sensitivity are achieved with reduced charge carrier recombination. In this study, we use state-of-the-art CdTe single crystals and electro-optical measurements to develop a detailed understanding of recombination rate dependence on excitation and temperature in CdTe. We study recombination and carrier dynamics in high-resistivity (undoped) and arsenic (As)-doped CdTe by employing absorption, the Hall effect, time-resolved photoluminescence, and pump-probe in the 80–600 K temperature range. We report extraordinarily long lifetimes (30 µs) at low temperatures in bulk undoped CdTe. Temperature dependencies of carrier density and mobility reveal ionization of the main acceptors and donors as well as dominant scattering by ionized impurities. We also distinguish different recombination defects. In particular, shallow As Te and deep V Cd −As Cd acceptors were responsible for p-type conductivity. AX donors were responsible for electron capture, while nonradiative recombination centers (V Cd −As Te , As 2 precipitates), and native defects (V Cd −Te Cd ) were found to be dominant in p-type and n-type CdTe, respectively. Bimolecular and surface recombination rate temperature dependencies were also revealed, with bimolecular coefficient T −3/2 temperature dependence and 170 meV effective surface barrier, leading to an increase in surface recombination velocity at high temperatures and excitations. The results of this study allowed us to conclude that enhanced crucible rotation growth of As-doped CdTe is advantageous to As activation, leading to longer lifetimes and larger mobilities and open-circuit voltages due to lower absorption and trapping.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Optimization of Source Material for in-situ Arsenic Doping via Vapor Transport Deposition of CdTe Films

In-situ doping of CdTe/CdSeTe films with arsenic is performed using pre-doped source material prepared by high pressure Bridgman (HPB) melt growth. Arsenic level in the source material is varied from 1018-1020 cm-3. Correspondingly, dopant incorporation in the films prepared using vapor transport deposition (VTD) varied from 3x1017 cm-3–1x1018cm-3. In this range, dopant activation is found to inversely correlate with the dopant incorporation, suggesting compensation. The results from this study indicate film properties can be adjusted by source material.

41 EE - Solar Energy Technologies Office (EE-4S)↗

DOE OSTI2020

Defect Study of Group V Doped CdTe By Thermoelectric Effect Spectroscopy

Shallow acceptors in single crystal CdTe induced by Group V (P, As, and Sb) doping are identified by thermoelectric effect spectroscopy (TEES). Understanding defects in Group V doped CdTe is critical to improving and controlling the acceptor density and lifetime in the absorber material which is an important factor determining the open circuit voltage and efficiency in CdTe solar cells.

14 SOLAR ENERGY↗

DOE OSTI2020

Effects of excess Te on flux inclusion formation in the growth of cadmium zinc telluride when forced melt convection is applied

The presence of second phase defects, particularly flux inclusions of tellurium rich composition, are of great concern for charge collection efficiency in cadmium zinc telluride (CZT) and cadmium telluride (CT) material intended for applications such as radiation detection. These inclusions can distort applied electric field lines within the detector as well as act as trapping centers for charge carriers. Reduction and/or elimination of these inclusions is required to achieve appropriate charge collection efficiencies, especially in detectors of thicknesses greater than 5 mm. These so-called flux inclusions are understood to form as a consequence of constitutional undercooling at the crystal growth interface. In this study, a forced melt convection technique was applied in Vertical Bridgman (VB) melt growth of CZT without reducing imposed growth rates of ~2 mm/hr. Several rotation profiles were tested while adjusting the melt composition from 51.62 to 61.75 atomic percent (at%) Te where the Te concentration was initially increased to improve overall material purity. With forced melt convection, the best inclusion distributions were achieved with highly Te rich melt compositions, far beyond the stoichiometric composition range for the CZT system. Average inclusion diameters were reduced to 2 µm while inclusions greater than 5 µm were essentially eliminated. Composition analyses of these ingots revealed near equilibrium concentrations of Te, even with ingots grown from Te concentrations as high as 61.75 at% Te. In this paper, a recipe for the reduction of inclusions in CZT melt growth is put forward and the implications of this method on our understanding of inclusion formation are discussed.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗