The effect of oxygen pressure on volatility and morphology of LaB6 single crystal cathodes

The effect of oxygen pressure on the volatility and morphology of single crystal LaB6 cathodes, heated to different temperatures, was investigated. At a temperature of 1600 K, an increase of oxygen pressure from 1 x 10 to the -8th torr to 1 x 10 to the -6th torr has led to a 100-fold enhancement in cathode volatility. The enhancement effect of oxygen pressure diminished with increasing temperature: at a cathode operating temperature of 1900 K, the volatility enhancement due to the same oxygen pressure was negligible. It was shown that the faceting frequently observed during evaporation of conically shaped emitters is due to a crystallograpic anisotropy of the oxidation rate of LaB6. No facet formation occurs during evaporation at oxygen pressures below -110 to the -8th torr.

Davis, P. R.↗
NASA NTRS1984

Evaluation of single crystal LaB6 cathodes for use in a high frequency backward wave oscillator tube

The results of thermionic emission and evaporation studies of single crystal LaB6 cathodes are given. A comparison between the (100), (210) and (310) crystal planes shows the (310) and (210) planes to possess a work function approx 0.2 eV lower than (100). This translates into a significant increase in current density, J, at a specified temperature. Comparison with a state-of-the-art impregnated dispenser cathode shows that LaB6 (310) is a superior cathode in nearly all respects except operating temperature at j 10 A/sq cm. The 1600 K thermionic and room temperature retarding potential work functions for LaB6 (310) are 2.42 and 2.50 respectively.

Swanson, L. W.↗
NASA NTRS1980

Fabrication and surface characterization of composite refractory compounds suitable for thermionic converters

Thermal faceting was observed for the high index planes of LaB6. The (100), (110), and (111) planes were found to be the most thermodynamically stable faces in vacuum in a study of electrode materials for thermionic emitters. The properties of adsorbed carbon, cesium, and cesium-oxygen layers were investigated on LaB6 single crystal surfaces as well as on Zr/0/W(100) and W(100). Cesium was found to increase electron reflection near the collision threshold on LaB6(100) and W(100) and to decrease the reflection on Zr/0/W(100). This difference may be explained by the unusually high threshold reflection coefficient of Zr/0/W without adsorbed cesium.

Davis, P. R.↗
NASA NTRS1980

The adsorption of cesium on lanthanum hexaboride surfaces

The adsorption/desorption characteristics of cesium on clean and oxygen-covered LaB6 (100) surfaces were studied using various surface analysis techniques. On the initially clean surface (phi = 2.77 eV), adsorption produces a minimum work function of 1.96 eV and a saturation work function of 2.07 eV. For the oxygen-saturated surface, the cesium adsorption curve shows no minimum, the lowest work function (1.35 eV) occurring at cesium saturation. The utility of LaB6 (100) as an emitter or collector in thermionic converter applications (particularly for space nuclear electric propulsion) is evaluated.

Davis, P. R.↗
NASA NTRS1979

Fabrication and surface characterization of composite refractory compounds suitable for thermionic converters

The techniques of fabricating and characterizing the surface properties of electrode materials were investigated. The basic surface properties of these materials were studied with respect to their utilization as thermionic energy converter electrodes. Emphasis was placed on those factors (e.g, cesium disorption kinetic and mechanisms of low work function production) which are of primary concern to thermionic converter performance.

Davis, P. R.↗
NASA NTRS1976

Fabrication and surface characterization of composite refractory compounds suitable for thermionic converters

Procedures for fabricating high purity single crystals of LaB6 and SmB6 have been developed. Auger spectroscopy shows that a clean surface can be obtained by thermal heating at 1700 K; such a clean surface gives a value of B/La of 2.3 to 2.6 for the (100) face. The measured thermionic and FERP work functions of the (100) face of LaB6 are 2.47 and 2.28 eV, respectively. The electron reflection coefficient for LaB6(100) increases near zero primary energy to 0.5. Flash thermal desorption of an oxygen dosed surface showed that B2O3 is the desorption product at 1600 to 1700 K. A work function increase of 1.6 eV was observed on oxygen adsorption on LaB6(100). Thermal desorption of Co occurs at approximately 1300 K. A reduction of the work function to 1.39 eV was observed on adsorption of a partial monolayer of Cs on LaB6(100). The evaporation of LaB6 occurs as atomic La and B with a value of B/La of 6 to 3 in the temperature range 1700 to 2000 K. The activation energies of desorption for La and B are 6.3 + or - 0.3 and 6.8 + or - 0.3 eV, respectively.

Swanson, L. W.↗
NASA NTRS1975

A field-ionization neutral detector - FIND

The field ionization neutral detector FIND operates according to the following principle: Neutral atoms are attracted toward the field ionization tips since they are polarized by the electric field of the tips. The atoms are singly ionized and repelled by the positive potential of the tips toward the detector situated behind a grid at ground potential. The ions deposit in the detector their kinetic energies, typically 26 keV, corresponding to the potential difference between the ionization region and the detector. Laboratory results show that FIND can have the resolution, sensitivities and durability required to perform in situ measurements of neutral H and He fluxes in interplanetary space, cometary halos and exospheres.

Curtis, C. C.↗
NASA NTRS1973

Work function measurements by the field emission retarding potential method.

Description of the theoretical foundation of the field electron retarding potential method, and review of its experimental application to the measurement of single crystal face work functions. The results obtained from several substrates are discussed. An interesting and useful fallout from the experimental approach described is the ability to accurately measure the elastic and inelastic reflection coefficient for impinging electrons to near zero-volt energy.

Strayer, R. W.↗
NASA NTRS1972

Measurement of single crystal surface parameters

The sticking coefficient and thermal desorption spectra of Cs from the (110) plane of W was investigated. A sticking coefficient of unity for the monolayer region was measured for T 250 K. Several distinct binding states were observed in the thermal desorption spectrum. Work function and electron reflection measurements were made on the (110) and (100) crystal faces of Mo. Both LEED and Auger were used to determine the orientation and cleanliness of the crystal surfaces. The work function values obtained for the (110) and (100) planes of Mo were 4.92 and 4.18 eV respectively.

Swanson, L. W.↗
NASA NTRS1971

Work function measurements by the field emission retarding potential method

Using the field emission retarding potential method true work functions have been measured for the following monocrystalline substrates: W(110), W(111), W(100), Nb(100), Ni(100), Cu(100), Ir(110) and Ir(111). The electron elastic and inelastic reflection coefficients from several of these surfaces have also been examined near zero primary beam energy.

Swanson, L. W.↗
NASA NTRS1969

Detection of molecular infrared spectra

Total energy distribution measurements of field emitted electrons detect molecular infrared spectra of adsorbed molecules. Tunneling electron gives up energy to excite various modes of adsorbed molecule. These electrons, when energy-analyzed, show up on the collector and exhibit the spectra of various modes excited by tunneling electrons.

Swanson, L. W.↗