DOE OSTI2024

Radiation Modeling of Z1: Validation of a Novel Radioisotope System

This paper presents the development of a radiation model for a novel strontium-90 (Sr-90) radioisotope heat source developed by Zeno Power Systems (Zeno), which demonstrates a groundbreaking fuel and shielding design that significantly reduces weight compared to traditional concepts. A Monte Carlo N-Particle (MCNP) model has been created to assess the effectiveness of this fuel and shielding design, however validation of the MCNP model is desired. Zeno has developed a prototype device (Z1) to aid in this model validation effort. This project is a collaborative effort between Zeno, the University of Dayton Research Institute (UDRI) and Pacific Northwest National Laboratory (PNNL), where the Z1 prototype was constructed and characterized.

RTG↗

DOE OSTI2023

Visualizing Uranium Crystallization from Melt: Experiment-Informed Phase Field Modeling and Machine Learning

The focus of this project was to observe and simulate the solidification of uranium metal at the crystallographic level from its molten state. Melting experiments were conducted at two different scales to observe microstructural evolution using either a laboratory-scale induction furnace (hundreds of grams of metal) or a microscope heating stage (hundreds of milligrams of metal), respectively. Experimental parameters and characterization data were then used to inform a phase field model of gamma-U crystal growth as dendrites with or without secondary phase impurities in the form of uranium carbide particles. Finally, training datasets were generated by the phase field model as inputs to a neural network, developed with the aim of providing a faster, cheaper surrogate model for microstructural simulations within a given parameter space. Progress is reported herein for each of these task areas. Ultimately, 1) an optical microscope heating stage capability has been stood-up for uranium metal solidification studies, 2) a phase field model was advanced to simulate multiple uranium grains growing in the presence of carbide impurity particles and 3) a neural network was constructed and optimized to predict the microstructure features of individually growing uranium crystals.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Casting and Characterization of U-50Zr

Uranium alloyed with 50 wt% zirconium (U-50Zr) is a proposed light water reactor (LWR) nuclear fuel by Lightbridge Corporation (LTBR). The proposed method for making the U-50Zr alloy is to arc-melt master alloys and then remelt in a vacuum induction melter (VIM) to consolidate the material and cast into an intermediate shape. After casting, the material will eventually need to be formed into a desired fuel shape. The work discussed in this report resulted from a joint effort between Ltbr and Pacific Northwest National Laboratory (PNN) to investigate a 500g – 1kg scale casting process to produce the U-50Zr alloy in the desired δ-UZr 2 phase and characterize the impurities and microstructure that result from the casting process. Master alloys were fabricated in an arc melter, then five castings were carried out in a VIM with multiple inert coating and crucible materials to find an appropriate combination. Both ZrO 2 and graphite crucibles were used and different combinations of Y 2 O 3 , CaZrO 3 , and TiC to identify which would contain the molten metal with the least reaction. On each casting, the C, O, N, H impurities were analyzed as well as the phase by x-ray diffraction and microstructure. Of the five castings, two resulted in majority of δ-UZr 2 phase-pure material and had impurity levels within acceptable ranges. The two most successful castings utilized a graphite crucible with a TiC undercoating and a Y 2 O 3 overcoat. The O and N levels were below 1000 ppm and the C content was variable but did not result in measurable carbide formation. The highest success casting resulted in an average of 282 ppm C, 567 ppm O, 217 ppm N and 79 ppm H. This casting's crucible and inert coating material was repeated with slightly different casting parameters and resulted in higher C numbers but similar phase identification. The differences between each casting are discussed and recommendations are made for future experiments to better decide on a casting process to go forward with.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

Electropolishing of a Full-Sized U-10Mo Plate

Electropolishing is used to remove material from the surface of a metal using electric potential and current. U-10Mo fuel is produced from a low enriched uranium plate alloyed with 10% molybdenum (U-10Mo). Electropolishing is being considered in two steps of the process of fabricating this U-10Mo fuel. First, it could be used as a means initially improving the surface finish of the cast plate while removing smut from the casting process from the surface prior to homogenization. Second, it could be used again after homogenization to remove oxidation and continue to improve the surface finish prior to hot rolling. The purpose of this work is to demonstrate the process on full-size ingots and optimize the process. A depleted uranium U-10Mo plate was electropolished three times: the first two times were prior to homogenization and the third after a homogenization step. The first two polishes decreased the overall roughness, as measured by laser confocal microscopy. After each polish, a smoother and shinier blue-gold surface was left on the plate. Upon homogenization, the surface had a more matte appearance and the surface roughness increased back to the pre-homogenization values obtained prior to the initial polish. After electropolishing the homogenized pieces, the changes in surface roughness increased, as measured by laser confocal microscopy. The final polishing step was not long enough to return the surface roughness to pre-homogenization conditions, implying less polishing is needed before the homogenization versus afterwards. Heat generation during the polish was addressed by circulating the electrolyte solution through an external heat exchanger; however, solubility and anodization challenges require further study.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗