Szymanski, Dennis

Publications and source records attributed to Szymanski, Dennis.

4 records

DOE OSTI2022

Schottky contacts to N-polar GaN with SiN interlayer for elevated temperature operation

In this Letter, we unveil the high-temperature limits of N-polar GaN Schottky contacts enhanced by a low-pressure chemical vapor deposited (LPCVD) SiN interlayer. Compared to conventional Schottky diodes, the insertion of a 5 nm SiN lossy dielectric interlayer in-between Ni and N-polar GaN increases the turn-on voltage (V ON ) from 0.4 to 0.9 V and the barrier height ($\phi_B$) from 0.4 to 0.8 eV. This modification also reduces the leakage current at zero bias significantly: at room temperature, the leakage current in the conventional Schottky diode is >103 larger than that observed in the device with the SiN interlayer, while at 200 °C, this ratio increases to 105. Thus, the rectification ratio (ION/IOFF) at ±1.5 V reduces to less than one at 250 °C for the conventional Schottky diode, whereas for SiN-coated diodes, rectification continues until 500 °C. The I–V characteristics of the diode with an SiN interlayer can be recovered after exposure to 400 °C or lower. Contact degradation occurs at 500 °C, although devices are not destroyed yet. Here, we report N-polar GaN Schottky contact operation up to 500 °C using an LPCVD SiN interlayer.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗

DOE OSTI2021

On the characteristics of N-polar GaN Schottky barrier contacts with LPCVD SiN interlayers

In this work, we study the behavior of N-polar GaN Schottky diodes with low-pressure chemical vapor deposited (LPCVD) SiN interlayers and unveil the important role of an amphoteric miniband formed in this interlayer due to a previously identified and dominating Si dangling bond defect. Through analysis of temperature-dependent current–voltage (I–V–T), capacitance–voltage (C–V), and x-ray photoelectron spectroscopy measurements, we observe that when nickel is deposited on LPCVD SiN pretreated with hydrofluoric acid, the SiN/GaN interface is responsible for determining the overall system's barrier height. By contrast, contact formation on oxidized LPCVD SiN leads to a metal/SiN-dominant barrier. We, consequently, propose band diagrams that account for an amphoteric miniband in LPCVD SiN, leading to a new understanding of LPCVD SiN as a lossy dielectric with surface barrier-dependent behavior.

42 ENGINEERING↗

DOE OSTI2021

High Mg activation in implanted GaN by high temperature and ultrahigh pressure annealing

Not provided.We demonstrate high p-type conductivity and hole concentrations >10 18 cm -3 in Mg-implanted GaN. The implantation was performed at room temperature and by post-implantation annealing at 1 GPa of N 2 and in a temperature range of 1200–1400 °C. The high pressure thermodynamically stabilized the GaN surface without the need of a capping layer. We introduce a “diffusion budget,” related to the diffusion length, as a convenient engineering parameter for comparing samples annealed at different temperatures and for different times. Although damage recovery, as measured by XRD, was achieved at relatively low diffusion budgets, these samples did not show p-type conductivity. Further analyses showed heavy compensation by the implantation-induced defects. Higher diffusion budgets resulted in a low Mg ionization energy (~115 meV) and almost complete Mg activation. For even higher diffusion budgets, we observed significant loss of Mg to the surface and a commensurate reduction in the hole conductivity. High compensation at low diffusion budgets and loss of Mg at high diffusion budgets present a unique challenge for shallow implants. A direct control of the formation of compensating defects arising from the implantation damage may be necessary to achieve both hole conductivity and low Mg diffusion.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Chemical treatment effects on Schottky contacts to metalorganic chemical vapor deposited n-type N-polar GaN

In this article, we investigate the effect of different chemical treatments, such as solvents, bases, and acids, on the surface properties and electrical behavior of Schottky diodes fabricated on metalorganic chemical vapor deposition-grown, n-type, N-polar GaN. The I–V and C–V barrier heights of the as-grown Schottky diodes are found to be 0.40 eV and 0.60 eV, respectively, with an ideality factor n = 1.07. It is found that the solvent treatments neither change the surface nor the electrical performance of the Schottky diodes, as expected. However, the treatments by the alkaline photolithography developer and acid—the latter of which is often used to clean the surface of Ga-polar GaN films prior to metal contact deposition—degrade the performance of N-polar GaN. These base and acid treatments severely roughen the surface by creating triangular/hexagonal crystallographic facets. The I–V and C–V barrier heights of these base- and acid-treated diodes are increased to 0.63 eV and 1.00 eV, respectively, with ideality factor values n < 1.2. X-ray photoelectron spectroscopy studies indicate that base- and acid-treated surfaces have lower oxygen content as compared to the as-grown sample surface. It is understood that the increment in the barrier height for base- and acid-treated diodes could be due to the change in polarity, from N-polar to semi-polar/non-polar, on these crystallographic features. All these results demonstrate that, unlike for Ga-polar GaN, the N-polar GaN surface is highly reactive to bases and acids.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗