DOE OSTI2023

Electrolyte design for Li-ion batteries under extreme operating conditions

The ideal electrolyte for the widely used LiNi 0.8 Mn 0.1 Co 0.1 O 2 (NMC811)||graphite lithium-ion batteries is expected to have the capability of supporting higher voltages (≥4.5 volts), fast charging (≤15 minutes), charging/discharging over a wide temperature range (±60 degrees Celsius) without lithium plating, and non-flammability. No existing electrolyte simultaneously meets all these requirements and electrolyte design is hindered by the absence of an effective guiding principle that addresses the relationships between battery performance, solvation structure and solid-electrolyte-interphase chemistry. Here we report and validate an electrolyte design strategy based on a group of soft solvents that strikes a balance between weak Li+-solvent interactions, sufficient salt dissociation and desired electrochemistry to fulfil all the aforementioned requirements. Remarkably, the 4.5-volt NMC811||graphite coin cells with areal capacities of more than 2.5 milliampere hours per square centimetre retain 75 per cent (54 per cent) of their room-temperature capacity when these cells are charged and discharged at -50 degrees Celsius (-60 degrees Celsius) at a C rate of 0.1C, and the NMC811||graphite pouch cells with lean electrolyte (2.5 grams per ampere hour) achieve stable cycling with an average Coulombic efficiency of more than 99.9 per cent at -30 degrees Celsius. The comprehensive analysis further reveals an impedance matching between the NMC811 cathode and the graphite anode owing to the formation of similar lithium-fluoride-rich interphases, thus effectively avoiding lithium plating at low temperatures. Additionally, this electrolyte design principle can be extended to other alkali-metal-ion batteries operating under extreme conditions.

25 ENERGY STORAGE↗
DOE OSTI2022

Lithium halide cathodes for Li metal batteries

Lithium halides cathodes potentially offer a high energy density at a low cost for rechargeable batteries. However, these cathodes suffer from quick capacity decay in organic electrolytes and the failiure mechanism remains elusive. Here, we report that liquefying the halogen or interhalogen compounds is a prerequisite for achieving high reversibility for the lithium halides cathodes. The gas or solid halogen can be liquefied by using interhalogen compounds with different electronegativity or changing the temperature. As a proof of concept, reversible LiCl conversion-intercalation chemistry in organic electrolyte is demonstrated by using either redox coupling with less electronegative I/Br to form liquid ICl/BrCl or reducing the temperature to -30oC. Further, the LiCl-LiBr-graphite cathodes in 1.6M lithium difluoro(oxalato)borate/1.6M lithium triflate in diglyme electrolytes achieve a high reversible specific capacity of 250 mAh/g at 3.7 V with an energy density being comparable to or higher than transition metal oxide cathodes at a much lower cost.

25 ENERGY STORAGE↗
DOE OSTI2022

Enabling Conversion-Type Iron Fluoride Cathode by Halide-Based Solid Electrolyte

The practical application of low-cost and energy-dense iron fluoride cathodes has been hindered by the first cycle electrochemical irreversibility, cycling instability, and large voltage hysteresis. Here, we report that these challenges may be overcome by the utilization of halide-based solid electrolytes (SEs). The excellent electrochemical stability of halide-based SEs enables a complete conversion and deconversion of FeF 2 which cannot be achieved with sulfide-based SEs. Due to restricted and reversible decomposition of SE, prevention of Fe dissolution, mechanical confinement of active material, as well as improved electrode kinetics, solid-state FeF 2 cathode with halide-based SE demonstrated superior electrochemical performance compared with FeF 2 electrodes in liquid electrolytes, with a high 1st cycle coulombic efficiency (~100 %), high specific capacity (~600 mAh/g), long cycle life (>100 cycles) and high-rate performance (up to 2C). In conclusion, our results suggest solidifying the batteries may be a viable approach to addressing the long-standing key challenges of iron fluoride cathodes.

25 ENERGY STORAGE↗
DOE OSTI2022

High Current-Density-Charging Lithium Metal Batteries Enabled by Double-Layer Protected Lithium Metal Anode

The practical application of lithium (Li) metal anode (LMA) is still hindered by non-uniformity of solid electrolyte interphase (SEI), formation of "dead" Li, and continuous consumption of electrolyte although LMA has an ultrahigh theoretical specific capacity and a very low electrochemical redox potential. Herein, we report a facile protection strategy for LMA using a double layer (DL) coating that consists of a polyethylene oxide (PEO)-based bottom layer which is highly stable with LMA and promotes uniform ion flux, and a cross-linked polymer-based top layer which prevents solvation of PEO layer in electrolytes. Li deposited on DL-coated Li (DL@Li) exhibits a smoother surface and much larger size than that deposited on bare Li. The LiF/Li 2 O enriched SEI layer generated by the salt decomposition on top of DL@Li further suppresses the side reactions between Li and electrolyte. Driven by the abovementioned advantageous features, the DL@Li||LiNi 0.6 Mn 0.2 Co 0.2 O 2 cells demonstrate capacity retention of 92.4% after 220 cycles at a current density of 2.1 mA cm -2 (C/2 rate) and stability at a high charging current density of 6.9 mA cm -2 (1.5C rate). These results indicate that the DL protection is promising to overcome the rate limitation of LMAs and high energy-density Li metal batteries.

25 ENERGY STORAGE↗
DOE OSTI2022

High-Entropy and Superstructure-Stabilized Layered Oxide Cathodes for Sodium-Ion Batteries

Layered transition metal oxides are appealing cathodes for sodium-ion batteries due to their overall advantages in energy density and cost. But their stabilities are usually compromised by the complicated phase transition and the oxygen redox, particularly when operating at high voltages, leading to poor structural stability and substantial capacity loss. Here, in this study, an integrated strategy combing the high-entropy design with the superlattice-stabilization to extend the cycle life and enhance the rate capability of layered cathodes is reported. It is shown that the as-prepared high-entropy Na 2/3 Li 1/6 Fe 1/6 Co 1/6 Ni 1/6 Mn 1/3 O 2 cathode enables a superlattice structure with Li/transition metal ordering and delivers excellent electrochemical performance that is not affected by the presence of phase transition and oxygen redox. It achieves a high reversible capacity (171.2 mAh g –1 at 0.1 C), a high energy density (531 Wh kg –1 ), extended cycling stability (89.3% capacity retention at 1 C for 90 cycles and 63.7% capacity retention at 5 C after 300 cycles), and excellent fast-charging capability (78 mAh g –1 at 10 C). This strategy would inspire more rational designs that can be leveraged to improve the reliability of layered cathodes for secondary-ion batteries.

25 ENERGY STORAGE↗
DOE OSTI2022

Synergy of carbonyl and azo chemistries for wide-temperature-range rechargeable aluminum organic batteries

Rechargeable aluminum organic batteries (RAOBs) are promising for developing cost-effective and sustainable energy storage devices due to the low cost, abundance, and high sustainability of aluminum and organic resources. In this study, we designed and synthesized a redox-active polymer bearing carbonyl and azo groups as a cathode material for RAOBs. The polymeric cathode exhibits a high reversible specific capacity, superior cyclic stability, fast charging capability, and a wide operation temperature range (₋40°C to 100°C). X-ray photoelectron spectroscopy (XPS), pair distribution function (PDF) analysis, and soft X-ray absorption near edge structure (XANES) were employed to gain fundamental insight into the carbonyl and azo chemistries in RAOBs, as well as the cathode electrolyte interphase (CEI) structure. We demonstrated a step-by-step alumination/de-alumination reaction for carbonyl and azo groups in the polymer cathode and unraveled a Al 2 O 3⁻ and AlN-rich CEI, which is critical for the impressive performance of RAOBs.

25 ENERGY STORAGE↗
DOE OSTI2022

Few-Atom Copper Catalyst for the Electrochemical Reduction of CO to Acetate: Synergetic Catalysis between Neighboring Cu Atoms

Single-atom catalysts (SACs) are gaining increasing recognition because of their superior catalytic properties for various reactions. However, the performance of SACs is often limited by the lack of neighboring metal centers to cooperate in catalysis. Herein, a synergetic interaction between neighboring Cu atoms of a few-atom catalyst (FAC) on graphdiyne is found to greatly enhance the production of acetate in CO electroreduction reaction relative to Cu SACs. In a 1.0 M KOH electrolyte, this Cu FAC exhibits an acetate Faradaic efficiency of 53.8±1.5 % and an ultrahigh relative purity of up to 97 wt% for liquid products, and excellent stability of over 23 h continuous electrolysis at -0.8 V versus reversible hydrogen electrode (RHE). Theoretical studies suggest that the intersite catalytic communication between two neighboring metal atoms confined in each pore of GDY facilitates the formation of acetic acid through either stepwise hydrogenation of CH 2 CO* or the direct reaction of H 2 O with CH 2 CO*. Our study demonstrates the unprecedented synergetic catalysis of Cu FAC in promoting the selective CO electroreduction toward acetate production.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Additive engineering for robust interphases to stabilize high-Ni layered structures at ultra-high voltage of 4.8 V

Nickel-rich layered cathode materials promise high energy density for next-generation batteries when coupled with lithium metal anodes. However, the practical capacities accessible are far less than the theoretical values due to their structural instability during cycling, especially when charged at high voltages. Here we demonstrate that stable cycling with an ultra-high cut-off voltage of 4.8 V can be realized by using an appropriate amount of lithium difluorophosphate in a common commercial electrolyte. The Li||LiNi 0.76 Mn 0.14 Co 0.10 O 2 cell retains 97% of the initial capacity (235 mAh g -1 ) after 200 cycles. The cycling stability is ascribed to the robust interphase on the cathode. It is formed by lithium difluorophosphate decomposition, which is facilitated by the catalytic effect of transition metals. The decomposition products (Li 3 PO 4 and LiF) form a protective interphase. This suppresses transition metal dissolution and cathode surface reconstruction. It also facilitates uniform Li distribution within the cathode, effectively mitigating the strain and crack formation.

25 ENERGY STORAGE↗
DOE OSTI2022

Isoxazole-Based Electrolytes for Lithium Metal Protection and Lithium-Sulfurized Polyacrylonitrile (SPAN) Battery Operating at Low Temperature

A new electrolyte system using isoxazole as the salt dissolving solvent has been developed and studied for lithium metal batteries. By using fluoroethylene carbonate (FEC) as an additive and 1,1,2,2-tetrafluoroethyl-2,2,3,3-tetrafluoropropyl ether (TTE) as a diluent for localized high concentration electrolyte (LHCE), isoxazole-based electrolytes were successfully implemented in lithium metal batteries, demonstrating excellent lithium metal protection capability. Utilizing several advanced characterization techniques (including synchrotron-based X-ray absorption spectroscopy and photoelectron spectroscopy), the solid electrolyte interphase (SEI) formed on the Li-metal anode after employing these electrolytes was thoroughly investigated. The high ionic conductivity of isoxazole at low temperature and the low impedance of SEI formed in LHCE significantly improved the low-temperature performance of Li-sulfurized polyacrylonitrile (SPAN) batteries, delivering 273.8 mAh g −1 capacity at −30 °C with 99.85% capacity retention after 50 cycles.

25 ENERGY STORAGE↗
DOE OSTI2022

Mechanistic Insights into the Interplay between Ion Intercalation and Water Electrolysis in Aqueous Batteries

Improving electrolyte stability to suppress water electrolysis represents a basic principle for designing aqueous batteries. Herein, we investigate counterintuitive roles that water electrolysis plays in regulating intercalation chemistry. Using the Na x Fe[Fe(CN) 6 ]∥NaTi 2 (PO 4 ) 3 (x < 1) aqueous battery as a platform, we report that high-voltage overcharging can serve as an electrochemical activation approach to achieving concurrent Na-ion intercalation and an electrolytic oxygen evolution reaction. When the cell capacity is intrinsically limited by deficient cyclable Na ions, the electrolytic water oxidation on the cathode allows for extra Na-ion intercalation from the electrolyte to the NaTi 2 (PO 4 ) 3 anode, leading to a major increase in cyclable Na ions and specific capacity. Furthermore, the parasitic oxygen generation and potential transition-metal dissolution, as proved by our synchrotron and imaging tools, can be significantly mitigated with a simple reassembling approach, which enables stable electrochemical performance and sheds light on manipulating ion intercalation and water electrolysis for battery fast charging and recycling.

25 ENERGY STORAGE↗
DOE OSTI2021

Microwave-Assisted Synthesis of Cu@IrO 2 Core-Shell Nanowires for Low-Temperature Methane Conversion

A facile microwave-assisted synthesis was developed for the tunable fabrication of a novel Cu@IrO 2 core@shell nanowire motif. Experimental parameters, such as (i) reaction time, (ii) the method of addition of the Ir precursor, (iii) capping agent, (iv) reducing agent, as well as (v) the capping agent-to-reducing agent ratio, were subsequently optimized. The viability of other methods based on previously reported literature, such as refluxing, stirring, and physical sonication, was studied and compared with our optimized microwave-assisted protocol in creating our as-prepared materials. It should be noted that the magnitude of the IrO 2 shell could be tailored based on varying the Cu: Ir ratio coupled with judicious variations in the amounts of capping agent and reducing agent. Structural characterization techniques, such as XRD, XPS, and HRTEM (including HRTEM-EDS), were used to analyze our Cu@IrO 2 motifs. Specifically, the shell could be reliably tailored from sizes of 10 nm, 8 nm, 6 nm, and 3.5 nm with corresponding Cu: Ir ratios of 10:1, 15:1, 20:1, and 25:1, respectively. Moreover, the structural integrity of the motifs was probed and found to have been maintained after not only heat treatment but also the post-methane conversion process, indicative of an intrinsically high stability. Both components within the CuO-IrO 2 interface were able to activate methane at temperatures between 400 to 500 K with a reduction of the associated metal cations (Cu 2+ → Cu 1+ ; Ir 4+ → Ir 3+ ) and the deposition of CH x fragments on the surface, as clearly observed in the ambient-pressure XPS results. Thus, on the basis of their stability and chemical activity, these core-shell materials could be very useful for the catalytic conversion of methane into 'higher value" chemicals.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Anionic redox induced anomalous structural transition in Ni-rich cathodes

Ni-rich cathodes have emerged as one of the most promising candidates for power next generation electric vehicles. However, they often suffer from poor capacity retention when charged to high voltages and the origin of this degradation remains elusive. Here, by using high throughput operando neutron diffraction, a universal four-stage structural evolution of Ni-rich cathodes is revealed during the initial cycle for the first time. Particularly, we discovered a universal structural transition in Ni-rich cathodes at ~75% delithiation irrespective of Ni or substituent contents. This transition is hallmarked by the anomalous increase of average TM–O bond lengths, contradicting the conventional wisdom that TM–O bond lengths decrease during charge (oxidation). This anomaly is induced by the direct oxidation of lattice oxygen ions, which is rooted in the drastic decrease of oxygen-to-TM charge transfer gap at high degrees of delithiation. The onset of this anomalous transition matches very well with the onset of oxygen gas release and severe decline of capacity retention in Ni-rich cathodes, suggesting that this bulk structural transition plays an indispensable role in the degradation process. These findings shed light on the elusive degradation mechanism of Ni-rich cathodes, providing valuable clues to stabilize oxidized oxygen ions for stable cycling of layered oxide cathodes at high voltages.

25 ENERGY STORAGE↗