Tan, Xiaoyan

Publications and source records attributed to Tan, Xiaoyan.

10 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Ba 4 RuMn 2 O 10 : A Noncentrosymmetric Polar Crystal Structure with Disordered Trimers

Phase-pure polycrystalline Ba 4 RuMn 2 O 10 was prepared and determined to adopt the noncentrosymmetric polar crystal structure (space group Cmc2 1 ) based on results of second harmonic generation, convergent beam electron diffraction, and Rietveld refinements using powder neutron diffraction data. The crystal structure features zigzag chains of corner-shared trimers, which contain three distorted face-sharing octahedra. The three metal sites in the trimers are occupied by disordered Ru/Mn with three different ratios: Ru1:Mn1 = 0.202(8):0.798(8), Ru2:Mn2 = 0.27(1):0.73(1), and Ru3:Mn3 = 0.40(1):0.60(1), successfully lowering the symmetry and inducing the polar crystal structure from the centrosymmetric parent compounds Ba 4 T 3 O 10 (T = Mn, Ru; space group Cmca). The valence state of Ru/Mn is confirmed to be +4 according to X-ray absorption near-edge spectroscopy. Ba 4 RuMn 2 O 10 is a narrow bandgap (~0.6 eV) semiconductor exhibiting spin-glass behavior with strong magnetic frustration and antiferromagnetic interactions.

36 MATERIALS SCIENCE↗
DOE OSTI2023

IrGe 4 : A Predicted Weyl-Metal with a Chiral Crystal Structure

Polycrystalline IrGe4 was synthesized by annealing elements at 800 °C for 240 h, and the composition was confirmed by energy-dispersive X-ray spectroscopy. IrGe 4 adopts a chiral crystal structure (space group P3 1 21) instead of a polar crystal structure (P3 1 ), which was corroborated by the convergent-beam electron diffraction and Rietveld refinements using synchrotron powder X-ray diffraction data. The crystal structure features layers of IrGe 8 polyhedra along the b axis, and the layers are connected by edge- and corner-sharing. Each layer consists of corner-shared [Ir 3 Ge 20 ] trimers, which are formed by three IrGe 8 polyhedra connected by edge-sharing. Temperature-dependent resistivity indicates metallic behavior. The magnetoresistance increases with increasing applied magnetic field, and the nonsaturating magnetoresistance reaches 11.5% at 9 T and 10 K. The Hall resistivity suggests that holes are the majority carrier type, with a carrier concentration of 4.02 × 10 21 cm –3 at 300 K. In conclusion, electronic band structures calculated by density functional theory reveal a Weyl point with a chiral charge of +3 above the Fermi level.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

CoTe 2 : A Quantum Critical Dirac Metal with Strong Spin Fluctuations

Abstract Quantum critical points separating weak ferromagnetic and paramagnetic phases trigger many novel phenomena. Dynamical spin fluctuations not only suppress the long‐range order, but can also lead to unusual transport and even superconductivity. Combining quantum criticality with topological electronic properties presents a rare and unique opportunity. Here, by means of ab initio calculations and magnetic, thermal, and transport measurements, it is shown that the orthorhombic CoTe 2 is close to ferromagnetism, which appears suppressed by spin fluctuations. Calculations and transport measurements reveal nodal Dirac lines, making it a rare combination of proximity to quantum criticality and Dirac topology.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Multifunctional Cu 2 TSiS 4 (T = Mn and Fe): Polar Semiconducting Antiferromagnets with Nonlinear Optical Properties

In this work, Cu 2 TSiS 4 (T = Mn and Fe) polycrystalline and single-crystal materials were prepared with high-temperature solid-state and chemical vapor transport methods, respectively. The polar crystal structure (space group Pmn2 1 ) consists of chains of corner-sharing and distorted CuS 4 , Mn/FeS 4 , and SiS 4 tetrahedra, which is confirmed by Rietveld refinement using neutron powder diffraction data, X-ray single-crystal refinement, electron diffraction, energy-dispersive X-ray spectroscopy, and second harmonic generation (SHG) techniques. Magnetic measurements indicate that both compounds order antiferromagnetically at 8 and 14 K, respectively, which is supported by the temperature-dependent (100–2 K) neutron powder diffraction data. Additional magnetic reflections observed at 2 K can be modeled by magnetic propagation vectors k = (1/2,0,1/2) and k = (1/2,1/2,1/2) for Cu 2 MnSiS 4 and Cu 2 FeSiS 4 , respectively. The refined antiferromagnetic structure reveals that the Mn/Fe spins are canted away from the ac plane by about 14°, with the total magnetic moments of Mn and Fe being 4.1(1) and 2.9(1) μ B , respectively. Both compounds exhibit an SHG response with relatively modest second-order nonlinear susceptibilities. Density functional theory calculations are used to describe the electronic band structures.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

LiMo 8 O 10 : Polar Crystal Structure with Infinite Edge-Sharing Molybdenum Octahedra

Here, polycrystalline LiMo 8 O 10 was prepared in a sealed Mo crucible at 1380 °C for 48 h using the conventional high-temperature solid-state method. The polar tetragonal crystal structure (space group I4 1 md) is confirmed based on the Rietveld refinement of powder neutron diffraction and 7 Li/ 6 Li solid-state NMR. The crystal structure features infinite chains of Mo 4 O 5 (i.e., Mo 2 Mo 4/2 O 6/2 O 6/3 ) as a repeat unit containing edge-sharing Mo 6 octahedra with strong Mo–Mo metal bonding along the chain. X-ray absorption near-edge spectroscopy of the Mo-L 3 edge is consistent with the formal Mo valence/configuration. Magnetic measurements reveal that LiMo 8 O 10 is paramagnetic down to 1.8 K. Temperature-dependent resistivity [ρ(T)] measurement indicates a semiconducting behavior that can be fitted with Mott’s variable range hopping conduction mechanism in the temperature range of 215 and 45 K. The ρ(T) curve exhibits an exponential increase below 5 K with a large ratio of ρ 1.8 /ρ 300 = 435. LiMo 8 O 10 shows a negative field-dependent magnetoresistance between 2 and 25 K. Heat capacity measurement fitted with the modified Debye model yields the Debye temperature of 365 K.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Iridate Li8IrO 6 : An Antiferromagnetic Insulator

In this work, a polycrystalline iridate Li 8 IrO 6 material was prepared via heating Li 2 O and IrO 2 starting materials in a sealed quartz tube at 650 °C for 48 h. The structure was determined from Rietveld refinement of room-temperature powder neutron diffraction data. Li 8 IrO 6 adopts the nonpolar space group $R\bar{3}$ with Li atoms occupying the tetrahedral and octahedral sites, which is supported by the electron diffraction and solid-state 7Li NMR. This results in a crystal structure consisting of LiO 4 tetrahedral layers alternating with mixed IrO 6 and LiO 6 octahedral layers along the crystallographic c -axis. The +4 oxidation state of Ir 4+ was confirmed by near-edge X-ray absorption spectroscopy. An in situ synchrotron X-ray diffraction study of Li 8 IrO 6 indicates that the sample is stable up to 1000 °C and exhibits no structural transitions. Magnetic measurements suggest long-range antiferromagnetic ordering with a Néel temperature (TN) of 4 K, which is corroborated by heat capacity measurements. The localized effective moment $μ_{\text{eff}}$ (Ir) = 1.73 $μ_{\text{B}}$ and insulating character indicate that Li 8 IrO 6 is a correlated insulator. First-principles calculations support the nonpolar crystal structure and reveal the insulating behavior both in paramagnetic and antiferromagnetic states.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Ambient and High Pressure CuNiSb 2 : Metal-Ordered and Metal-Disordered NiAs-Type Derivative Pnictides

The mineral Zlatogorite, CuNiSb 2 , was synthesized in the laboratory for the first time by annealing elements at ambient pressure (CuNiSb 2 -AP). Rietveld refinement of synchrotron powder X-ray diffraction data indicates that CuNiSb 2 -AP crystallizes in the NiAs-derived structure ( P 3 m 1, #164) with Cu and Ni ordering. The structure consists of alternate NiSb 6 and CuSb 6 octahedral layers via face-sharing. The formation of such structure instead of metal disordered NiAs-type structure ( P 6 3 / mm c, #194) is validated by the lower energy of the ordered phase by first-principle calculations. Interatomic crystal orbital Hamilton population, electron localization function, and charge density analysis reveal strong Ni-Sb, Cu-Sb, and Cu-Ni bonding and long weak Sb-Sb interactions in CuNiSb 2 -AP. The magnetic measurement indicates that CuNiSb 2 -AP is Pauli paramagnetic. First-principle calculations and experimental electrical resistivity measurements reveal that CuNiSb 2 -AP is a metal. The low Seebeck coefficient and large thermal conductivity suggest that CuNiSb 2 is not a potential thermoelectric material. Single crystals were grown by chemical vapor transport. The high pressure sample (CuNiSb 2 -8 GPa) was prepared by pressing CuNiSb 2 -AP at 700 °C and 8 GPa. However, the structures of single crystal and CuNiSb 2 -8 GPa are best fit with a disordered metal structure in the P 3 m 1 space group, corroborated by transmission electron microscopy.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2020

High-Pressure, High-Temperature Synthesis and Characterization of Polar and Magnetic LuCrWO 6

We report a new polar and magnetic oxide, LuCrWO 6 , was synthesized under high pressure (6 GPa) and high temperature (1673 K). LuCrWO 6 is isostructural with the previously reported polar YCrWO 6 (SG: Pna21, no. 33). The ordering of CrO 6 and WO 6 octahedra in the edge-shared dimers induce the polar structure. The effective size of rare earth, Ln cation does not seem to affect the symmetry of LnCrWO 6 . Second harmonic generation measurements of LuCrWO 6 confirmed the noncentrosymmetric character and strong piezoelectric domains are observed from piezoresponse force microscopy at room temperature. LuCrWO 6 exhibits antiferromagnetic behavior, T N , of ~18 K with a Weiss temperature of -30.7 K.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗