Selenium-doped copper oxide nanoarrays: Robust electrocatalyst for the oxygen evolution reaction with ultralow overpotential
The oxygen evolution reaction (OER) is the key anodic reaction in electrochemical water splitting. OER is a four-electron process with sluggish reaction kinetics. RuO 2 and IrO 2 are the benchmark catalysts for OER. Thus, finding a low-cost, earth-abundant, and stable electrocatalyst for OER is a big challenge. Here in this work, we report OER over Se-CuO/CF nanoarrays with an ultralow overpotential of 440 mV (at 50 mA/cm 2 current density). Se-CuO/CF nanoarray has a TOF of 0.05 s -1 at 300 mV. The catalyst showed consistent OER performance upto1000 cycles run over a period of 10 h. The OER performance of Se-CuO/CF nanoarrays was compared with RuO 2 /CF catalyst and the overpotential for RuO 2 /CF nanoarray was only 10 mV lower than Se-CuO/CF 50 mA/cm 2 current density. Se-CuO/CF nanoarray showed 50 mV lower overpotential than the state of the art RuO 2 /CF catalyst at a current density of 100 mA/cm 2 . The Tafel slope of Se-CuO/CF is 21 mV/decade lower compared to RuO 2 /CF suggesting faster reaction kinetics of Se-CuO/CF. The electrochemical surface area and the conductivity were increased upon doping Se into CuO/CF nanoarrays which can be attributed to enhanced OER performance of the Se-CuO/CF nanoarrays.
Enhanced Catalytic Activity of a Vanadium-Doped Mesoporous Octahedral Molecular Sieve-2 (K-OMS-2) toward Hydrogen Evolution Reaction
Hydrogen evolution reaction (HER) is the cathodic reaction in electrochemical water splitting that produces H 2 in a renewable pathway, primarily to be used in fuel cells. K-OMS-2, a manganese octahedral molecular sieve, has the potential to replace Pt as a catalyst for HER due to its redox and electrochemical properties, which can be further improved by doping metal cations into the K-OMS-2 framework. In this work, we synthesized 1, 5, and 10% vanadium- (V) doped mesoporous K-OMS-2 under mild acidic reaction conditions. Here, the mesoporous nature of the samples was confirmed by BET analysis. X-ray photoelectron spectroscopy confirmed that Mn has 2+, 3 +, and 4+ oxidation states, and V is present as V 4+ in V-K-OMS-2 samples. HER performance of 1% V-K-OMS-2 in an acidic medium shows the best activity with -0.32 V overpotential. The overpotential was lowered by 0.56 V upon doping 1% V into the K-OMS-2 framework. The 1% V-K-OMS-2 material has a Tafel slope of 129 mV/decay and an electrochemically active surface area (ECSA) of 127.5 cm 2 ECSA .