DOE OSTI2022

Light Water Reactor Sustainability Program: Complete the weld campaign on Ni-base irradiated materials using stress improved laser welding including the preliminary weld quality inspections

This report summarizes the most recent welding campaign on irradiated Ni-base alloy 182 and the preliminary weld quality inspections at the Radiochemical Engineering Development Center (REDC). Equipment and capabilities were developed jointly by the U.S. Department of Energy, Office of Nuclear Energy, Light Water Reactor Sustainability Program, the Electric Power Research Institute, Long Term Operations Program (and the Welding and Repair Technology Center), and Oak Ridge National Laboratory. Irradiated nickel alloy 182, with target helium contents of 5 atom parts-per million (appm), 10 appm, and 20 appm, were laser welded in the hot cell successfully. The significant, on-going effort to weld irradiated alloys with high helium concentrations and comprehensively analyze the results will eventually yield validated repair techniques and guidelines for use by the nuclear industry in extending the operational lifetimes of nuclear power plants. This report fulfills the FY 2023 milestone M3LW-22OR0406013, “Complete the weld campaign on Ni base irradiated materials using stress improved laser welding including the preliminary weld quality inspections”.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2022

Microstructure analysis of laser beam weldments performed on neutron-irradiated 304L steel containing 3 and 8 appm helium

We report that AISI 304 L austenitic stainless steel is one of the major structural materials used in light water reactors (LWRs). In the future, 304 L components may require repair, and several welding techniques have been proposed as candidates. In this study, laser beam welding using the low-energy contribution approach was performed in ~2016 on neutron-irradiated AISI 304 L steel with nominal values of 3 and 8 appm helium (He). The goal was to investigate the impact of helium on the irradiated material weldability and evaluate helium-associated damage. The weld and heat-affected zone (HAZ) microstructure was studied using scanning electron microscopy, electron backscatter diffraction, and transmission electron microscopy (TEM). Analysis of the weldment cross-sections did not reveal severe cracking. Still, evidence of incipient helium-associated damage was observed in the HAZ, manifesting as degraded grain boundaries (GBs) “decorated” by pore chains and mostly small (i.e., ≤ 25-30 µm) scattered cracks. The largest observed crack was ~50 µm in length. Helium-associated damage was localized within ~200-300 µm of the weld pool boundary, and the fraction of the compromised GBs, as a rule, was below ~9-11% of the total GB network. TEM analysis showed significant annealing of the radiation-induced defects at distances up to ~300 µm from the weld pool boundary. Inside the HAZ, the cavities (likely, helium bubbles) tended to form at GBs and inclusions, such as manganese sulfide precipitates in the grain interior. Crystallography analysis of the HAZ damage showed that random high-angle boundaries were most susceptible to helium-associated damage. In contrast, low-angle random boundaries and twin boundaries appeared to be strongly resistant to degradation from the combined effects of helium and welding.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Suppression of Helium Induced Cracking in Laser Repair Welding of Highly Irradiated Stainless Steels

Welding repair of irradiated nuclear reactor materials such as austenitic stainless steels used for the reactor internals has been challenging due to irradiation generated helium in the material matrix over an extended period of time. In this study, improved laser welding techniques, including the novel Auxiliary Beam Stress Improved (ABSI) technique that proactively manages the stresses during laser repair welding is investigated to substantially reduce or avoid the occurrence of intergranular helium-induced cracking (HeIC). Here, laser weld cladding, with and without ABSI technique, was applied to deposit weld metal on irradiated stainless steel (Type 304 L) blocks with various helium concentrations up to approximately 20 atomic parts per million (appm). Welded samples were cross-sectioned and analyzed using optical and electron microscopes. It was found that, with the improved laser welding techniques, no macroscopic (millimeter-sized) cracks were observed in any of the samples. Microscopic (less than 50 μm) cracks were present in the heat affected zone. Statistical analysis on the sample with the highest helium concentration (~20 appm) reveals that the ABSI technique could effectively reduce the size and amounts of microscopic cracks.

36 MATERIALS SCIENCE↗

DOE OSTI2019

FRICTION STIR WELDING AND PRELIMINARY CHARACTERIZATION OF IRRADIATED 304 STAINLESS STEEL

The mitigation of helium induced cracking in the heat affected zone (HAZ), a transition metallurgical zone between the weld zone and base metal, during repair welding is a great challenge in nuclear industry. Successful traditional fusion welding repairs are limited to metals with a maximum of a couple of atomic parts per million (appm) helium, and structural materials helium levels in operating nuclear power plants are generally exceed a couple of appm after years of operations. Therefore, fusion welding is very limited in nuclear power plants structural materials repairing. Friction stir welding (FSW) is a solid-state joining technology that reduces the drivers (temperature and tensile residual stress) for helium-induced cracking. This paper will detail initial procedural development of FSW weld trials on irradiated 304L stainless steel (304L SS) coupons utilizing a unique welding facility located at one of Oak Ridge National Laboratory’s hot cell facilities. The successful early results of FSW of an irradiated 304L SS coupon containing high helium are discussed. Helium induced cracking was not observed by scanning electron microscopy in the friction stir weld zone and the metallurgical zones between the weld zone and base metal, i.e. thermal mechanical affected zone (TMAZ) and HAZ. Characterization of the weld, TMAZ and HAZ regions are detailed in this paper.

Tang, Wei↗

DOE OSTI2018

High Performance Computing Tools to Advance Materials Joining Technology

In this project, an in-house HPC finite element code was developed with novel computational schemes that provided fast and high-fidelity simulation capability for welding processes and allied manufacturing processes such as metal additive manufacturing processes. Benchmark comparison confirmed that, for the testing cases studied, the newly developed in-house code resulted in increases in computational speed in the ranges of 100x to 1000x depending on the size and complexity of the testing cases, when compared to today’s commercial welding process simulation tools. As demonstrated by the selected examples in this report, the breakthrough increases in computational simulation speeds achieved by the in-house HPC code means that high fidelity simulations of certain complex welding problems that would require months even years of computational time with today’s commercial code could be solved in two to three days. Similar order of magnitudes of reduction in computational times for metal additive manufacturing process were also achieved.

36 MATERIALS SCIENCE↗