Taylor, P. Craig

Publications and source records attributed to Taylor, P. Craig.

8 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Crystalline Si Surface Passivation with Nafion for Bulk Defects Detection with Electron Paramagnetic Resonance

Here, in monocrystalline Si (c-Si) solar cells, identification and mitigation of bulk defects are crucial to achieving a high photoconversion efficiency. To spectroscopically detect defects in the c-Si bulk, it is desirable to passivate the surface defects. Passivation of the c-Si surface with dielectrics such as Al 2 O 3 and SiNx requires deposition at elevated temperatures, which can influence defects in the bulk. Herein, we report on the passivation of different Czochralski (Cz) Si wafer surfaces by an organic copolymer, Nafion. We test the efficacy of the surface passivation at temperatures ranging from 6 to 473 K to detect bulk defects using electron paramagnetic resonance (EPR) spectroscopy. By comparing with state-of-the-art passivation layers, including Al 2 O 3 and liquid HF/HCl, we found that at room temperature, Nafion can provide comparable passivation of n-type Cz Si with an implied open-circuit voltage (iV oc ) of 713 mV and a recombination current prefactor J o of 5 fA/cm 2 . For p-type Cz Si, we obtained an iV oc of 682 mV with a J o of 22.4 fA/cm 2 . Scanning electron microscopy and photoluminescence reveal that Nafion can also be used to passivate the surface of c-Si solar cell fragments scribed from a solar cell module by using a laser. Consistent with previous studies, analysis of the EPR spectroscopy data confirms that the H-terminated surface is necessary, and fixed negative charge in Nafion is responsible for the field-effect passivation. While the surface passivation quality was maintained for almost 24 h, which is sufficient for spectroscopic measurements, the passivation degraded over longer durations, which can be attributed to surface SiO x growth. These results show that Nafion is a promising room-temperature surface passivation technique to study bulk defects in c-Si.

14 SOLAR ENERGY↗
DOE OSTI2023

Defect Characterization of Monocrystalline Silicon Solar Cells with Polysilicon Passivated Contact Using Electrically-Detected Magnetic Resonance (EDMR) Spectroscopy

As the c-Si based solar cell efficiencies are approaching over 26%, it is becoming critical to characterize the low concentrations of the defects – as low as 10^10-10^11 cm-3 (for e.g., iron contamination in high-lifetime Ga-doped wafers3 and n-type wafers), and further reduce them. Also, atomistic level understanding of the mechanisms of the low concentration process-induced-defects and reliability limiting defects (such as light and elevated temperature induced degradation, surface passivation degradation) is needed to design the mitigation strategies. The conventional characterization techniques are limited due to their detection limitations. Some of the techniques based on lifetime spectroscopies can still be used for low concentration characterization however, they are based on estimations and theoretical models and hence, indirect and cannot fully reveal information about the microscopic mechanism of the defects. Thus, we present the application of an ultrasensitive magnetic resonance-based technique for the direct spectroscopic detection of the defects in Si PV - electrically detected magnetic resonance (EDMR). In this work, we aim to focus on establishing a process flow for fabrication of minicells with (miniature replica of the larger-area cells) and setting up the routine for EDMR measurements on them with the EDMR instrumentation capability at NREL. For the EDMR measurements, sample size is limited by the dimensions of sample holder tube (width less than 3.2 mm, active area - 20 mm). Thus, we have designed c-Si based minicells with polysilicon (poly-Si) passivated contacts same as the larger-area cells that we fabricate in our group at NREL. We also modified our minicell process flow for fabricating the textured minicells for preserving the texture during processing and taking care of the laser-ablation edge damage which can significantly affect the performance of such small devices. We have achieved comparable performance on these newly fabricated minicells as that of our 4 cm2 devices with same structure (comparable VOC, JSC, FF). We also conducted EDMR measurements on the minicells and observed a distinct EDMR signal at g-value ~2.005 at temperatures 30K and above, as shown in Fig. 2. We associate this signal to the presence of silicon dangling bonds based on the g-value. We also observed an EDMR signal at g-value ~1.998 at temperature ~5K. The origin of this signal is still being investigated. Thus, we show the proof of concept of minicells and EDMR measurements with which we now aim to study some of the unknown defects in silicon solar cell devices.

EDMR↗
DOE OSTI2023

Understanding Microscopic Mechanisms of LeTID and LID and their Unifying Features by Electron Paramagnetic Resonance

LID degradation involves not only creation of ~ 10^12 cm^-3 recombination centers, but also ~ 10^16 cm^-3 shallow negative-U traps. In Ga-doped Si, LID EPR defects don't appear, but some traps are still created. LeTID: Si DB and H-hyperfine EPR signatures. We postulate that the defect responsible for LeTID is a partially hydrogenated (multivacancy) with a Si dangling bond and H in the vicinity. O involvement is possible yet unclear. We prove that H is related to the structure of the LeTID defect with isotope experiments and its EPR signal is comparable and linear with the Si DB signal upon LeTID degradation. Working on simulating these results with DFT to obtain more detailed defect structure.

Cz Si↗
DOE OSTI2022

Spectroscopic Investigation of Shallow Hole Traps in Ga- and B-doped Czochralski Silicon: Insight into Light-Induced Degradation

We report the minority carrier lifetime in B-doped Czochralski (Cz) Si declines upon carrier injection due to light-induced degradation (LID), which is attributed to the formation of a recombination-active boron-oxygen complex. Ga-doped Cz Si does not undergo LID. Previously, we showed that B-doped Cz Si undergoes a transition from paramagnetic to diamagnetic due to LID. Herein, we show that Ga-doped Cz Si remains paramagnetic upon carrier injection. This suggests that either the shallow hole traps that are formed in B-doped Cz Si are absent in Ga-doped Cz Si, or the negative-U centers in Ga-doped Cz Si do not transform into a recombination-active configuration, because the shallow acceptor trap state is shallower than the Ga acceptor level in the forbidden gap. In contrast to B-doped Cz Si, the defect signatures in Ga-doped Cz Si do not change upon light exposure, as detected by both electron paramagnetic resonance and deep-level transient spectroscopy.

14 SOLAR ENERGY↗
DOE OSTI2021

Electron Paramagentic Resonance Investigation of Mechanism of Light- and Elevated-Temperature-Induced Degradation in Ga-doped Cz Si

We report on the electron paramagnetic resonance (EPR) spectra recorded at 6 K for Ga-doped Czochralski (Cz) Si in the initial stages of light- and elevated-temperature-induced degradation (LeTID). We show that the narrow-range EPR spectrum depends on the duration of simultaneous heat and light exposure. After prolonged LeTID, the EPR intensity increases at ~334 mT. The EPR signature at ~334 mT is characteristic of Si dangling bonds, and the increase in the dangling bond density can be attributed to the bulk and not the surface. Additionally, we show that the inverse of the minority carrier lifetime in Ga-doped Cz Si samples, measured by quasi-steady-state photoconductance (QSSPC) decay, correlates with the increase in the intensity of the Si dangling bond signal measured by EPR. Based on these observations, we put forth a hypothesis connecting H to LeTID and the corresponding defect structure.

Cz Si↗
DOE OSTI2021

Atomic structure of light-induced efficiency-degrading defects in boron-doped Czochralski silicon solar cells

Boron-doped Czochralski (Cz) Si is the most commonly used semiconductor in the fabrication of solar cells. The minority carrier lifetime of boron-doped Cz Si decreases upon exposure to light due to B–O-related defects, which reduce the performance of ~10 9 solar modules worldwide. Using electron paramagnetic resonance (EPR), we have identified the spin-active paramagnetic signatures of this phenomenon and gained insights into its microscopic mechanism. We found a distinct defect signature, which diminished when the degraded sample was annealed. The second signature, a broad magnetic field spectrum, due to the unionized B acceptors, was present in the annealed state but vanished upon light exposure. These observations show that, on degradation, nearly all the ~10 16 cm –3 B atoms in Cz Si complexed with interstitial O atoms, whereas only ~10 12 cm –3 of these complexes created defects that were recombination-active. The formation rate of these recombination-active defects correlated with the decay of the minority carrier lifetime. Furthermore, the line shape parameters linked these defects to both B and O impurities in Cz Si.

14 SOLAR ENERGY↗
DOE OSTI2021

Spectroscopic Investigation of Light-Induced Degradation Paramagnetic Defect in Czochralski Silicon

We report on the electron paramagnetic resonance (EPR) spectra of Cz and FZ Si in different stages of light-induced degradation. Firstly, we show that the paramagnetic signal at low temperature (10K) is dependent on the state of light-induced degradation performed at room temperature and on the sample doping. The light-degraded state in p-Cz Si shows strong, sharp paramagnetic defect signatures compared to samples in the annealed state. When an excitation light is applied during the EPR measurement, additional structures appear in the spectra. In contrast, the wide EPR active signature related to boron interaction with lattice, is present in the annealed state but diminishes after light exposure. Finally, we show that the degraded paramagnetic signal returns when annealed samples are exposed to ambient light. We suggest that these changes in the electron paramagnetic resonance spectra is related to the boron-oxygen defect that causes light-induced degradation.

41 EE - Solar Energy Technologies Office (EE-4S)↗