Publications and source records attributed to Taysom, Brandon S..
Shear Enhanced Eccentric Roiling (ShEER) is a novel sheet manufacturing technique that aims to superimpose and control hydrostatic and deviatoric stress paths during rolling. In this research, we attempt to use ShEER to form and enhance the properties of low-ductility highly anisotropic materials such as magnesium.
Titanium and its alloys are used in the aviation and automobile industries due to their remarkable strength to weight ratio, but, commonly, machining loss is high with ~90 wt.% of the material being converted to scrap. Recycling post-consumer Ti scrap directly into solid bulk products is a potential solution for repurposing valuable material. Further, reducing or even eliminating fresh Ti sponge during recycling might lead to lower energy and greenhouse gas emissions. In this study, a solid-phase process known as friction extrusion was utilized to recycle Ti-6Al-4V machining chips into solid wires which could be used as feedstock in additive manufacturing. The friction consolidation technique was first used to convert chips with varying degrees of oxygen content into solid billets for its use as feedstock material in subsequent friction extrusion. The extrudates were fabricated above the beta transition temperature, which was achieved by selecting rotation rate and feed rate, to process the billets near 1000°C using a tungsten-lanthana extrusion die. This work presents the first occurrence of friction extruded titanium alloy wires. The effect of friction extrusion on microstructural features, tensile properties, and texture are reported. Overall, the friction extrusion method is capable of recycling Ti-6Al-4V scrap directly into extruded wire.
Conservation of critical materials is an increasing area of focus in the Unites States. In 2023, aluminum was added to the US Department of Energy Final Critical Materials List which has spurred public and private research into sustainable management of these resources. Additionally, efficiency in manufacturing and conservation of natural resources are growing concerns with targets to lower global carbon emissions, as primary aluminum alloy production is energy intensive, requiring 14 MWh of electricity plus 0.4 tonnes of CO2 per tonne of Al. Due to these factors, is essential that more sustainable manufacturing methods for aluminum alloys are developed going forward. To this end, much research is ongoing on the topic of more efficient utilization and recovery. However, most of this research still requires primary aluminum in the production process. Here, it will be attempted to bypass the use of primary aluminum and produce useful material recycled from 100% post-consumer scrap. Even considering recent developments in recycling of Al scrap, there is still a large amount of post-consumer scrap that is underutilized due to high impurity content, and that amount will increase significantly as more and more aluminum alloys are utilized in vehicles. This “scrap wave” is expected to cover 80% of the demand for automotive aluminum alloys by 2050 . A challenge to be addressed before the coming scrap wave can be fully utilized is that the tolerance of manufacturing techniques to impurities or off-spec alloy compositions must be increased. Particularly, in 5000-and 6000-series alloys (the most common wrought alloys in durable products), excess iron, copper, and silicon create brittle intermetallics during casting that remain in the extruded microstructure which limit the formability, ductility, and corrosion resistance of the alloy. Concerningly, many of the highest-volume post-consumer aluminum scrap streams such as automotive shredder scrap contain a mix of alloys including both wrought and cast alloys. Their compositions can vary widely depending on geography and the time of year. Because they are mixed, they often contain high content of multiple alloying elements such as Si and Cu in higher concentrations than are found in typical wrought alloys. They may also be contaminated with non-Al alloys from fasteners that get mixed in and often have high content of unwanted elements such as Fe. As a method for utilizing these underused scrap streams that are high in tramp elements, an emerging extrusion technology is being developed at the Pacific Northwest National Laboratory (PNNL) that aims to upcycle 100% post-consumer aluminum scrap directly into extruded components without the addition of primary aluminum . This new technology, called Shear Assisted Processing and Extrusion (ShAPE), is enabling a shift away from today’s recycling paradigm by reaching deeper into lower-value scrap streams, using shredder scrap as the extrusion billet material. Sometimes referred to as Twitch or Tweak, these scrap streams result from shredding and sorting of automobiles, building materials, appliances, and consumer goods. ShAPE combines the linear axis of conventional extrusion with a rotating extrusion die. This rotating die applies large strain to the material during extrusion, which breaks up large impurity-containing intermetallic particles, reducing their deleterious effects. This has been demonstrated for 6063 machining scrap spiked with excess Fe, and Twitch scrap high in Fe, Si and Cu where strength and ductility were retained for both feedstock compositions. Additionally, the extreme plastic deformation during ShAPE enables extrusion of billets with high Si that are too brittle for processing by conventional extrusion. By using 100% post-consumer shedder scrap as feedstock, ShAPE has the potential to slash embodied energy and carbon in extruded components by >80% compared to conventional extrusion of primary aluminum alloys.
Bimetallic tubes are used when a component requires more than one performance requirement, for instance, strength/creep resistance and oxidation/corrosion resistance. Shear-assisted processing and extrusion (ShAPE) can be used to fabricate extrudates that are comparable or superior in performance relative to conventionally manufactured extrudates. For the first time, ShAPE has been successfully employed in producing bimetallic Al tubing consisting of 6061 and 7075 Al alloys. Both light and electron microscopy techniques were used to investigate the integrity of the tubes, especially the interface between the core and cladding of the bimetallic tubes. Void-free bimetallic tubes were produced using ShAPE. Quantification of tube integrity was carried out with tensile testing under as-extruded and post-aged conditions. All the bimetallic tubes in the as-extruded samples exhibited uniform elongation above 5% with good tensile strength. Key insights such as material flow during bimetallic tube extrusion were obtained from the characterization of remnant billet and simulation results from a smoothed particle hydrodynamics model.
In this work, we use the thermoelectricity to directly measure the temperature at different radial positions within instrumented Al1100 billets during friction extrusion. Site-specific and uninterrupted temperature measurements were possible by measuring the local voltages at several thermoelectric junctions consisting of aluminum-nickel pairs during extrusion. Measurements were conducted for a constant die rotation speed of 150 RPM and different extrusion feed rates of 2, 8, 32, and 80 mm.min-1. X-ray computed tomography was used to locate the positions of the thermoelectric junctions inside the processed billet, thus allowing for site-specific microstructural characterization at the precise measurement points. Smooth particle hydrodynamic modeling allowed to determine the thermal, strain, and strain rate fields developing during FE. The applicability and limitations of this temperature measurement approach are discussed as a function of the peak extrusion and torsion stresses relative to the matrix of extrusion feed rates.
Shear Assisted Processing and Extrusion (ShAPE) was used to fabricate aluminum 6063 tubing directly from secondary scrap. Trimmings from an automotive manufacturing facility were cast into billets spiked with iron (0.3 wt% Fe) to explore the tolerance of ShAPE to Fe contamination. Billets were extruded in the unhomogenized condition to form tubing with an outer diameter of 12 mm and wall thickness of 2 mm. Tensile properties reached 0.2% YS = 206 MPa, UTS = 238 MPa, and U.E. = 16.3% in the T6 temper. Performance exceeds the ASTM minimum standard and is on par with ASM typical values for conventional extrusion of primary aluminum billets in the fully homogenized condition. Microstructural characterization shows extensive refinement of grain size along with dispersion and refinement of Fe-Al-Si intermetallic phases. This study suggests that ShAPE extrusion may offer a lower carbon manufacturing pathway through direct recycling of secondary aluminum scrap and elimination of the billet homogenization step.
Shear Assisted Processing and Extrusion (ShAPE), a severe plastic deformation technique that is fast and scalable, was used to produce thin-wall tubing from alloy 6082 (Al-0.8Mg-0.9Si-0.7Mn) with in-situ solutionization during processing quickly followed by quenching. Quench medium and input material heat treatment were varied and natural aging behavior (T1 heat treatment) was evaluated using tensile testing. As-cast input material was found to have higher strength early in post-ShAPE natural aging and homogenized input material was found to have strengthening during natural aging. Compared to air quenching, water quenching gave greater strength both early in and after natural aging. These observations along with microscopy suggest that: 1. air quenching was too slow; 2. as-cast material was not fully solutionized but plastic deformation broke up the coarse intermetallic particles, which provided strengthening; and 3. homogenized material was solutionized well, which led to good natural aging behavior.
In this report aluminum alloy 2024 (AA2024) tubes were extruded using the shear assisted processing and extrusion (ShAPE) method. As a ubiquitous aerospace alloy, AA2024 has reached a high degree of maturity with respect to manufacturing processes, alloy chemistry and heat treatment to maximize material strength. Therefore, over the eight decades since the introduction of this alloy, the mechanical properties have plateaued, and the extrusion speed has reached a 3.5 m/min ceiling using conventional extrusion. The ShAPE technique enabled an extrusion speed of AA2024 up to 7.4 m/min at 480 °C which is surpassing the extrudability chart of this alloy. Variation of the standard T3510 and T8510 post extrusion heat treatments were applied to improve the mechanical performance of the ShAPE extruded AA2024 tube. The ultimate tensile strength and yield strength of AA2024-T8510 ShAPE extruded tube are 522.0 ± 3.3 MPa and 510.7 ± 3.3 MPa, which are respectively 18% and 32% higher than ASM-typical and ASTM minimum values. The elongation at break of ShAPE extruded AA2024-T8510 tubes is two times higher than the ASM-typical and ASTM-minimum values. This improved ductility is attributed to the refinement of grain size and secondary phases as well as due to the uniform dispersion of sub-micron strengthening precipitates formed during the ShAPE process.
Cladded tubes are generally used where two distinct properties are required at the outer and inner part of a tube, for instance, strength and corrosion resistance. In this investigation, shear assisted processing and extrusion (ShAPE) was employed to fabricate bi-metallic tubes from 1100 and 7075, and 1100 and 2024 dissimilar Al alloy combinations. Surface defect-free bi-metallic tubes were fabricated via the ShAPE process. Detailed microstructural characterization of the interface and various locations of the cladded tubes were carried out using light and scanning electron microscopy techniques. A defect-free, metallurgically bonded interface between the cladded layer and high strength Al (7075 and 2024 Al) was observed. Furthermore, hardness and tensile properties of the cladded ShAPE tubes were examined in the as-extruded conditions.
Extrusion of unhomogenized castings of 7075 aluminum (Al) alloy has been accomplished using shear assisted processing and extrusion (ShAPE). The simultaneous plastic deformation and heat generation during ShAPE rapidly fracture and dissolve interdendritic and intragranular secondary phases of Al-Zn-Mg-Cu, accomplishing homogenization in seconds rather than many hours in a furnace prior to extrusion. ShAPE thereby eliminates the energy-intensive and time-consuming homogenization step required to prepare as-cast microstructures for conventional extrusion. Concurrently, extensive grain refinement occurs due to gradient activation of dynamic recrystallization during ShAPE, which facilitates a threefold increase in extrusion speed compared to the conventional extrusion method. Evident enhancement of the mechanical properties of ShAPE+T6 samples is achieved, compared to the ASTM standard values for conventional extrusion products. The microstructural evolution pathway, involving the processes of grain refinement and secondary particle dissolution, is explained using scanning and transmission electron microscopy.
Shear assisted processing and extrusion (ShAPE) was used to extrude aluminum alloy 7075 tubing at speeds up to 12.2 m/min. This is in comparison to 2.0 m/min which is generally the limit for conventionally extruded 7075. The increased speed is primarily attributed to more extensive shear deformation, compared to conventional extrusion, which results in a high density of low angle grain boundaries that facilitate continued deformation and delay the onset of surface tearing. Mechanical testing after heat treating to the T6 condition gave an ultimate tensile strength of 565.3 ± 4.6 MPa, yield strength of 495.7 ± 8.7 MPa, and elongation of 16.8 ± 0.8%. Strength values exceed the ASTM minimum standard and are on par with ASM typical values, while elongation was substantially improved compared to 7 and 11% for the ASTM and ASM values respectively. Finally, it was observed that low temperature extrusion at 341 °C and 40 rpm gave superior material properties in the T6 condition compared to high temperature extrusion at 441 °C and 120 rpm due to variances in nanoscale second phase size and distribution.
Friction welding (FW) enables joining of dissimilar metals parts up to the limits of their strength. CostE and NFA are two high-temperature steel alloys used in land-based power generation. These alloys were joined with FW, and the effect of process parameters on post-welded structure and tensile strength was studied. Weld energy primarily determined the heat-affected zone (HAZ) thickness in both alloys. The highest joint efficiencies – up to 96% – resulted from contact strengthening of thin NFA HAZ regions, but too thin of a HAZ resulted in an unreliable joint. Conversely, thick HAZ regions consistently lowered the weld strength. Optimal welding conditions occur with sufficient energy to create a full bond but not so much to notably lower weld strength.
Conventional extrusion of aluminum alloy 7075 is limited to 1-2 meters per minute in order to avoid surface tearing and cracking. An emerging technique called Shear Assisted Processing and Extrusion (ShAPE) was used to extrude aluminum alloy 7075 tubing at a speed of 7.4 meters per minute without inducing surface defects. The faster extrusion speed is attributed to the unique flow characteristics inherent to the ShAPE process compared to conventional extrusion. Tubes with an inner diameter of 10 mm, outer diameter of 12 mm, and length of 2 meters were extruded at temperatures ranging from 340°C to 466°C. Tensile testing was performed per ASTM B557-15 with strain measured using digital image correlation. An ultimate tensile strength of 565 ± 4.6 MPa, yield strength of 496 ± 8.7 MPa, and elongation of 16.4 ± 1.0 % were measured for extrusion made at 362°C and heat treated to the T6 condition.
Shear Assisted Processing and Extrusion (ShAPE) was used to fabricate thin-walled AA6063 tubing with improved mechanical properties compared to conventional extrusion. Namely, tensile properties for ShAPE extrusions after T5 heat treating far exceed conventional T5 properties and are on par with T6 tensile properties. Die rotational speed did not affect tensile properties, although increased extrusion speed did lead to moderate increases in elongation.
Thick plate and lower temperature friction stir welding results in good post-weld properties by welding at very low tool rotational speeds. Low speeds cause large variations in the measured shoulder temperature, making temperature control difficult. This paper describes a computationally light method to correct for oscillating measured temperatures. Data is collected over the previous two revolutions and used to build a compensation table and calculate a derivative. In simulation, measured temperature variations are reduced by a factor of five to ten. Temperature data is preserved and not cornered, nor is any time delay induced by this method, unlike with filtering methods.
Sold phase processing (SPP) utilizes large deformations and elevated but sub-melting temperatures to process materials in an energy-efficient manner to achieve high-performance properties. Studying the fundamental material science and kinetics requires an accurate temperature history of the process, but accurately measuring temperature at the point of deformation is very difficult. This study uses the thermoelectric principle to allow for the direct measurement of a deforming surface by turning the workpieces themselves into the measurement device. By so doing, results measured temperatures are closer to the actual deforming interface, more accurate, more responsive, and more reliable than corresponding measurements taken with standard thermocouples.
When a traditional relay feedback test is biased, asymmetry is induced, erroneous system identification occurs, and the test may stop oscillating. Adaptive methods which restore symmetry to the relay test are developed, and additional methods are presented to detect and recover from a non-oscillation condition. This is demonstrated both in simulation and in a process with significant transients and disturbances - friction stir welding (FSW). In testing, it is shown that the adaptive method is able to restore symmetry even in the presence of severe and changing disturbances, including after the weld plunge where temperature gradients change rapidly. Finally, these improvements enable system identification of systems such as FSW in a more robust and accurate manner.