Effect of high iron content on direct recycling of unhomogenized aluminum 6063 scrap by Shear Assisted Processing and Extrusion
Not Available
36 MATERIALS SCIENCE↗
Engineering topics
Taysom, Brandon Scott
Publications and source records attributed to Taysom, Brandon Scott.
In situ temperature measurement of a deforming interface with thermoelectricity
Accurate temperature measurement is critical to understanding the thermomechanical conditions and microstructural evolution that materials experience during severe plastic deformation (SPD). Others have previously measured the interface between a non-deforming tool and metal workpiece using thermocouples, infrared measurement, and the thermoelectric principle. Measuring temperature within the deforming material itself, especially at a high-shear deforming interface, has proven to be extremely difficult, thus limiting the application of these measurements to fundamental SPD research. In this study, the thermoelectric principle is used to directly measure temperature at the interface between copper and nickel billets undergoing SPD. This is done by utilizing the deforming materials themselves as two halves of a thermocouple junction. The spatial resolution of this measurement is shown via microscopy to be less than 1 micron. Temperature changes are sensed almost instantly, with time delays on the order of the data logger frequency (0.01 seconds). Process variations that are both very brief (<0.05 seconds) and minute (<3°C) are able to be detected by this method.
Taysom, Brandon Scott↗
Porthole die extrusion of aluminum 6063 industrial scrap by shear assisted processing and extrusion
Shear Assisted Processing and Extrusion (ShAPE) is presented as a new manufacturing technology for converting aluminum scrap directly into extruded products. In this work, a porthole die configuration is integrated within the rotating ShAPE process to extrude circular, square, trapezoidal, and two-cell trapezoidal profiles from aluminum alloy 6063 industrial scrap. This is the first time that a rotating billet has been used to impart severe plastic deformation (SPD) during extrusion of noncircular profiles. Microstructural characterization is presented for a trapezoidal profile having an average grain size of 6.7 µm in the as-extruded condition. Dimensional stability was evaluated by measuring wall thickness along the extrusion length; the thickness varied by <5%. Round tubes achieved yield strength (246.9 ± 10.4 MPa), ultimate tensile strength (270.8 ± 9.6 MPa), and uniform elongation (16.5 ± 2.4%) exceeding industry standards.
36 MATERIALS SCIENCE↗
Shear Assisted Processing and Extrusion (ShAPE) of Lightweight Automotive Components (CRADA 418)
Shear Assisted Processing and Extrusion (ShAPE) was developed to manufacture non-circular multicell profiles from secondary aluminum. This was accomplished by integrating a porthole die approach within the rotating ShAPE process. Complexity of the profile geometry was deliberately advanced over the course of the project from round to square, to asymmetric trapezoidal, to two-cell asymmetric trapezoidal. Aluminum alloy 6063 in the form of briquettes (compacted shreddings and engineered machining chips) and castings from pre-consumer industrial scrap were utilized as the feedstock. Tensile properties were shown to exceed the ASTM minimum standard and ASM typical values with the best results reaching yield strength = 247 ± 10 MPa, ultimate tensile strength = 271 ± 10 MPa, and uniform elongation = 16.5 ± 2.4%. These values were achieved for porthole extrusion using unhomogenized castings made from 100% aluminum 6063 industrial scrap. The ability to extrude unhomogenized billet was made possible by in situ conversion of plate-like β-type Fe-rich intermetallics to more extrudable needle-like α-type which is not possible with conventional extrusion. By eliminating the need to dilute iron with primary aluminum during the recycling process, savings of >90% on lifecycle carbon footprint and >50% on embedded energy could ultimately result in lower cost, more environmentally friendly, automotive components.
42 ENGINEERING↗
Devices and methods for performing shear-assisted extrusion, extrusion feedstocks, extrusion processes, and methods for preparing metal sheets
Devices and methods for performing shear-assisted extrusion processes for forming extrusions of a desired composition from a feedstock material are provided. The processes can use a device having a scroll face having an inner diameter portion bounded by an outer diameter portion, and a member extending from the inner diameter portion beyond a surface of the outer diameter portion.Extrusion feedstocks and extrusion processes are provided for forming extrusions of a desired composition from a feedstock. The processes can include providing a feedstock having at least two different materials and engaging the materials with one another within a feedstock container.Methods for preparing metal sheets are provided that can include preparing a metal tube via shear assisted processing and extrusion; opening the metal tube to form a sheet having a first thickness; and rolling the sheet to a second thickness that is less than the first thickness.
Whalen, Scott A.↗
Shear Assisted Processing and Extrusion (ShAPE) of Aluminum Alloy 7075, 2024, and Al-12.4TM
The most common aluminum alloys utilized in the aerospace industry are 7075 and 2024 due to their high strength-to-weight ratio compared to advanced high strength steels and other aluminum alloys. Despite excellent performance, these aluminum alloys have seen limited use outside of the aerospace industry due in part to high cost. If high-performance aluminum extrusions could be made more cost effectively by eliminating energy intensive process steps typical of conventional extrusion, then numerous opportunities exist for more widespread adoption. A key reason for the high cost of 7075 and 2024 extrusions (25-75% higher than 6061) is their slow extrusion speed. 7075 and 2024 are limited to 2 m/min and 3.5 m/min respectively, in contrast to 6061 which can be extruded at 20–80 m/min. In addition to slow speed, aluminum alloys require numerous thermal treatments throughout the extrusion process including homogenization and pre-heating prior to extrusion, and solution heat treating and artificial aging after extrusion. Each of these steps contribute to the total energy consumed during manufacturing of extruded components. This project investigates the use of ShAPE to improve extrusion speed and reduce, or even eliminate, the typical thermal treatments for high strength aluminum alloys, all while improving material performance. The overarching goal of this project was to demonstrate that Shear Assisted Processing and Extrusion (ShAPE) can manufacture high-performance aluminum alloy tubing with lower manufacturing energy and improved mechanical properties compared to conventional extrusion. Unlike conventional extrusion where the billet is rammed against a stationary die using a strictly linear motion, the ShAPE process superimposes a rotational shear force by spinning the die while the billet is plunged. Compared to conventional linear extrusion, the ShAPE process imparts significantly more strain into the feedstock material, which enables the formation of novel microstructures. These microstructures manifest an array of property and process improvements for extrusion of high-performance aluminum alloys. The following accomplishments were achieved for this project: Extrusion of 7075 at 12.2 meters/min compared to 2 meters/min for conventional extrusion; Elimination of 7075 billet homogenization (430 °C for 20 hours) which is required prior to conventional extrusion; Elimination of 7075 billet pre-heating (400 °C for 1 hour) in a separate furnace which is required prior to conventional extrusion; Achieved 7075-T6with yield strength = 595 MPa, ultimate tensile strength = 531MPa, and elongation = 17.4% for extrusions made from unhomogenized billets. Exceeds the ASTM and ASM standard, and typical industry values; Achieved 7075-T5 (i.e., no solution heat treatment) with yield strength = 588 MPa, ultimate tensile strength = 535 MPa, and elongation = 14.8% for extrusions made from homogenized billets; Extrusion of 2024 at 7.4 meters/min compared to 3.5 meters/min for conventional extrusion; Achieved 2024-T8510 yield strength = 522 MPa, ultimate strength = 510MPa, and elongation = 7.1% for extrusions made from wrought billets. Exceeds the ASTM and ASM standard, and typical industry values; Extrusion of Al-12.4TM high-performance aluminum powder directly into tubing, in a single step, which eliminates process steps typical of powder metallurgy extrusion.
36 MATERIALS SCIENCE↗
Strength in Rotary Friction Welding of Five Dissimilar Nickel-Based Superalloys
Advanced manufacturing processes improve the cost and quality of goods. Rotary friction welding is a fast, energy-efficient, and reliable joining process for metals, but new applications are hindered by large development costs for each new alloy. Each alloy set has different welding characteristics; therefore, lessons learned from a single alloy are not always broadly applicable. To establish knowledge that is applicable across multiple alloys, a family of different superalloys were welded to discover process trends that were applicable beyond a single alloy set. In this study, weld symmetry did not correlate to weld strength across alloy systems. Some alloys’ strongest welds occurred at maximum symmetry, whereas high asymmetry was associated with different alloys’ maximum strength. High feed rates, high welding forces, low energy, and low temperatures all resulted in high-strength welds across all alloy and geometry combinations. Tensile strengths greater than 95% of base-metal strength were recorded for most alloy systems.
36 MATERIALS SCIENCE↗
Shear assisted processing and extrusion of enhanced strength aluminum alloy tubing
Hollow extrusions are used in many industries to make strong, lightweight, and affordable structures. Shear Assisted Processing and Extrusion (ShAPE) enables the extrusion of many alloys, often with noteworthy properties. In this investigation, ShAPE was used to extrude 1 and 2 mm wall tubes of aluminum alloy 6063 measuring 12 mm in diameter at extrusion speeds up to 3.8 m/min. This speed is 10 and 15 times faster than has been reported for any alloy using ShAPE and friction stir back extrusion, respectively. Increasing the extrusion speed from 0.7 to 3.8 m/s resulted in using 68% less process energy at steady state. Microstructural analysis and tensile testing were performed on as-extruded tubes and tubes with a direct T5 heat treatment. Grain refinement from 65 µm to below 20 µm was observed. Growth of macroscale Mg 2 Si strengthening precipitates was not observed. ShAPE processing resulted in recrystallization, and extrusion speed was shown to influence final extrudate texture. Here, transmission electron microscopy analysis revealed that the as-extruded microstructure was free of nanoscale ß" strengthening precipitates. Nanoscale ß" was prominent in direct-aged (T5) ShAPE tubes, similar to a slightly over-aged conventional T6 microstructure. As-extruded tubes had ultimate tensile strengths on par with conventional T5 extrusions and approximately double the total elongation. Tubes that underwent a T5 heat treatment had yield and ultimate strengths averaging 198 and 234 MPa, respectively, with an average total elongation of 11%. The tensile test results are comparable to a conventional T6 heat treatment, but without the solutionization heat treatment step. Mechanical properties either remained flat or improved with increased extrusion speed, which suggests that ShAPE can be scaled up to an industrial process to create energy- and economically efficient high-strength extrusions.
36 MATERIALS SCIENCE↗