Low leakage current in heteroepitaxial Al 0.7 Sc 0.3 N ferroelectric films on Ga N

Wurtzite ( Al , Sc ) N ferroelectrics are attractive for microelectronics applications due to their chemical and structural compatibility with wurtzite semiconductors, such as Ga N and ( Al , Ga ) N . However, the leakage current in epitaxial stacks reported to date should be reduced for reliable device operation. Here, we demonstrate low leakage current in epitaxial Al 0.7 Sc 0.3 N films on Ga N with well-saturated ferroelectric hysteresis loops that are orders of magnitude lower (i.e., 0.07 A cm − 2 ) than previously reported films (1–19 A cm − 2 ) having similar or better structural characteristics. We also show that, for these high-quality epitaxial ( Al , Sc ) N films, structural quality (edge and screw dislocations), as measured by diffraction techniques, is not the dominant contributor to leakage. Instead, the small leakage in our films is limited by thermionic emission across the interfaces, which is distinct from the large leakage due to trap-mediated bulk transport in the previously reported ( Al , Sc ) N films. To support this conclusion, we show that Al 0.7 Sc 0.3 N on lattice-matched In 0.18 Ga 0.82 N buffers with improved structural characteristics but higher interface roughness exhibit increased leakage characteristics. This demonstration of low leakage current in heteroepitaxial ( Al , Sc ) N films and understanding of the importance of interface barrier and surface roughness can guide further efforts toward improving the reliability of wurtzite ferroelectric devices. Published by the American Physical Society 2025

36 MATERIALS SCIENCE↗
DOE OSTI2024

Designing Ta C Virtual Substrates for Vertical Al x Ga 1 − x N Power Electronics Devices

Power electronics are critical for a sustainable energy future, playing a key role in electrification and integration of renewable energy sources into the grid. Advances in ultrawide band gap materials are needed to handle higher powers in smaller form factors while reducing electrical and thermal losses. High Al content Al x Ga 1 − x N is theoretically capable of meeting these demands, but its impact in power electronics has been severely restricted by a lack of substrates that can satisfy conductivity, lattice matching, and/or thermal expansion requirements. We demonstrate that electrically conductive Ta C can be used as a virtual substrate for Al x Ga 1 − x N heteroepitaxy. Scaleably sputtered Ta C grown on Al 2 O 3 , followed by high-temperature face-to-face annealing, produces a thin film Ta C template with an effective hexagonal lattice constant matched to Al 0.70 Ga 0.30 N . Annealing of the Ta C promotes recrystallization, significantly improving crystallinity and reducing crystalline defects from as-deposited columnar grains to a step-and-terrace surface morphology, enabling the subsequent growth of high-quality Al 0.70 Ga 0.30 N by molecular beam epitaxy. X-ray diffraction and scanning transmission electron microscopy confirm that the Al x Ga 1 − x N layer is heteroepitaxially aligned, strain-free, and lattice-matched, transitioning abruptly from Ta C to Al x Ga 1 − x N without intermediate phases. These results demonstrate Ta C virtual substrates as electrically conductive, lattice-matched, and thermally compatible templates for vertical Al x Ga 1 − x N devices that can meet the growing power needs of a sustainable energy future. Published by the American Physical Society 2024

36 MATERIALS SCIENCE↗
DOE OSTI2024

Tailoring Growth Interfaces of Virtual Substrates for Power Electronics

Power electronics materials are poised to play a critical role in fulfilling next generation energy needs, with up to 90% of future energy demand predicted to flow through power electronics at some point. AlxGa1-xN ranks high among candidate materials, having bipolar dopability, thermal and chemical stability and an ultra-wide bandgap. However, AlGaN growth is limited by a lack of lattice-matched substrates, ultimately stunting material quality at higher thicknesses needed for power electronics applications. Further, high power applications increasingly call for fully vertical device structures, necessitating a conductive substrate. Recently our group identified the (111) plane of TaC as a conductive surface lattice-matched to Al0.55Ga0.45N, taking inspiration from prior work of AlN and GaN binaries on carbide and boride substrates. In this talk we demonstrate the growth of (111)-oriented TaC by RF sputtering. We investigate the interface of TaC with sapphire and SiC substrates and identify means to suppress competing Ta2C nucleation in order to stabilize (111)-oriented TaC. Potential stacking sequences are identified with respect to crystal structure and observed twinning in the TaC films. We next assess structural changes and film recrystallization that results from face-to-face annealing of TaC thin films at high temperatures above 1500 degrees C. Changes to grain structure and domain size are assessed by x-ray diffraction and surface morphology is explored using atomic force microscopy. Figure 1 shows significant improvements to in- and out-of-plane strain following annealing along with the formation of terraced step edges at the film surface. Strain as a function of material composition and thickness is considered, as this may play a major role in future nucleation of AlGaN layers. (1) R. J. in a face-to-face configuration, as illustrated in the schematic at left. Kaplar et al 2017, ECS J. Solid State Sci. Technol. 6 Q3061; (2) D. M. Roberts et al 2022, https://arxiv.org/abs/2208.11769; (3) T. Aizawa et al 2008, J Crys Growth 310, 1 22; (4) R. Liu et al 2002, Appl. Phys. Lett. 81, 3182-3184.

ENGINEERING↗
DOE OSTI2024

Virtual Substrates for Wide Bandgap AlyX1-yN Growth

Lattice-matched substrates are critical for growth of high quality, compositionally-targeted ternary AlyX1-yN compounds with properties suitable for a wide variety of next-generation opto- and power electronic applications. [DOI:10.1149/2.0111702jss] We have identified the (111) plane of transition metal carbides and nitrides as lattice matched "virtual" substrate layers that have additional benefits of electrical conductivity and appropriate coefficients of thermal expansion for nitride layer at both growth and operating temperatures. [arXiv:2208.11769 2022] In this work, (111)-oriented TaC and ZrN are grown by RF sputtering and optimized as substrate layers for AlyGa1-yN and AlyGd1-yN, respectively. TaC is demonstrated as a full proof of concept. (111)-stabilized TaC layers with a rock-salt crystal structure are annealed to improve surface crystal quality and surface morphology and then used as a template for growth of an Al0.7Ga0.3N layer by molecular beam epitaxy. X-ray diffraction (XRD) demonstrates epitaxial registry of the grown layer to the substrate. High resolution transmission electron microscopy (TEM) is used to investigate interface behavior, showing regions of abrupt interface transitions and nitrogen polar termination of the Al0.7Ga0.3N. We also grew (111)-oriented ZrN on Ti-Zr-N graded buffer layers as a lattice-matched virtual substrate for AlyGd1-yN. Structure, morphology, and strain are analyzed using XRD and atomic force microscopy. Structure and quality of initial Al0.8Gd0.2N thin films are investigated for both in-situ and ex-situ growths.

AlyX1-yN↗
DOE OSTI2023

Tailoring Growth Interfaces of Virtual Substrates for Power Electronics

Power electronics materials are poised to play a critical role in fulfilling next generation energy needs, with up to 90% of future energy demand predicted to flow through power electronics at some point.[1] Among a number of candidate materials, AlxGa1-xN is the strongest, having bipolar dopability, thermal and chemical stability, an ultra-wide bandgap, and demonstrated experimental feasibility. However, AlGaN growth is limited by a lack of lattice-matched substrates, ultimately stunting material quality at higher thicknesses needed for power electronics applications. Further, high power applications increasingly call for fully vertical device structures, necessitating a conductive substrate. [1] Recently our group identified the (111) plane of TaC as a conductive surface lattice-matched to Al0.55Ga0.45N, taking inspiration from prior work of AlN and GaN binaries on carbide and boride substrates. [2,3,4] In this talk we demonstrate the growth of (111)-oriented TaC by RF sputtering. We investigate the interface of TaC with sapphire and SiC substrates and identify means to suppress competing Ta2C nucleation in order to stabilize (111)-oriented TaC. Potential stacking sequences are identified with respect to crystal structure and observed twinning in the TaC films. We next assess structural changes and film recrystallization that results from face-to-face annealing of TaC thin films at high temperatures above 1500 degrees Celsius. Changes to grain structure and domain size are assessed by x-ray diffraction and surface morphology is explored using atomic force microscopy. Figure 1 shows significant improvements to in- and out-of-plane strain following annealing along with the formation of terraced step edges at the film surface. Strain as a function of material composition and thickness is considered, as this may play a major role in future nucleation of AlGaN layers.

CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SU↗
DOE OSTI2023

Gallium Oxide Heterojunction Diodes for 400 °C High‐Temperature Applications

β ‐Ga 2 O 3 ‐based semiconductor devices are expected to have significantly improved high‐power and high‐temperature performance due to its ultrawide bandgap of close to 5 eV. However, the high‐temperature operation of these ultrawide‐bandgap devices is usually limited by the relatively low 1–2 eV built‐in potential at the Schottky barrier with most high‐work‐function metals. Herein, heterojunction p ‐NiO/n‐ β ‐Ga 2 O 3 diodes fabrication and optimization for high‐temperature device applications are reported, demonstrating a current rectification ratio ( I ON / I OFF ) of more than 10 6 at 410 °C. The NiO heterojunction diode can achieve higher turn‐on ( V ON ) voltage and lower reverse leakage current compared to the Ni‐based Schottky diode fabricated on the same single‐crystal β ‐Ga 2 O 3 substrate, despite charge transport dominated by interfacial recombination. Electrical characterization and device modeling show that these advantages are due to a higher built‐in potential and additional band offset. These results suggest that heterojunction p–n diodes based on β ‐Ga 2 O 3 can significantly improve high‐temperature electronic device and sensor performance.

Sohel, Shahadat H.↗