DOE OSTI2020

LiAlO 2 /LiAl 5 O 8 Membranes Derived from Flame-Synthesized Nanopowders as a Potential Electrolyte and Coating Material for All-Solid-State Batteries

Recently, γ-LiAlO 2 has attracted considerable attention as a coating in Li-ion battery electrodes. However, its potential as a Li + ceramic electrolyte is limited due to its poor ionic conductivity (<10 –10 S cm –1 ). Here, we demonstrate an effective method of processing LiAlO 2 membranes (<50 μm) using nanopowders (NPs) produced via liquid-feed flame spray pyrolysis (LF-FSP). Here, membranes consisting of selected mixtures of lithium aluminate polymorphs and Li contents were processed by conventional tape casting of NPs followed by thermocompression of the green films (100 °C/10 kpsi/10 min). The sintered green films (1100 °C/2 h/air) present a mixture of LiAlO 2 (~72 wt %) and LiAl 5 O 8 (~27 wt %) phases, offering ionic conductivities (>10 –6 S cm –1 ) at ambient with an activation energy of 0.5 eV. This greatly increases their potential utility as ceramic electrolytes for all-solid-state batteries, which could simplify battery designs, significantly reduce costs, and increase their safety. Furthermore, a solid-state Li/Li 3.1 AlO 2 /Li symmetric cell was assembled and galvanostatically cycled at 0.375 mA cm –2 current density, exhibiting a transference number ≈ 1.

25 ENERGY STORAGE↗

DOE OSTI2020

Solid Electrolytes for Li–S Batteries: Solid Solutions of Poly(ethylene oxide) with Li x PON- and Li x SiPON-Based Polymers

We report here efforts to synthesize free-standing, dry polymer electrolytes that exhibit superior ionic conductivities at ambient for Li–S batteries. Co-dissolution of poly(ethylene oxide) (PEO) (M n 900k) with Li x PON and Li x SiPON polymer systems at a ratio of approximately 3:2 followed by casting provides transparent, solid-solution films 25–50 μm thick, lowering PEO crystallinity, and providing measured impedance values of 0.1–2.8 × 10 –3 S/cm at ambient. These values are much higher than simple PEO/Li + salt systems. These solid-solution polymer electrolytes (PEs) are (1) thermally stable to 100 °C; (2) offer activation energies of 0.2–0.5 eV; (3) suppress dendrite formation; and (4) enable the use of lithium anodes at current densities as high as 3.5 mAh/cm 2 . Here, galvanostatic cycling of SPAN/PEs/Li cell (SPAN = sulfurized, carbonized polyacrylonitrile) shows discharge capacities of 1000 mAh/g sulfur at 0.25C and 800 mAh/g sulfur at 1C with high coulumbic efficiency over 100 cycles.

25 ENERGY STORAGE↗

DOE OSTI2020

Polymer Precursor Derived Li x PON Electrolytes: Toward Li–S Batteries

Efforts to develop polymer precursor electrolytes that offer properties anticipated to be similar or superior to (lithium phosphorus oxynitride, LiPON) glasses are reported. Such precursors offer the potential to be used to process LiPON-like thin glass/ceramic coatings for use in all solid state batteries, ASBs. Here, LiPON glasses provide a design basis for the synthesis of sets of oligomers/polymers by lithiation of OP(NH 2 ) 3–x (NH) x [from OP(NH) 3 ],OP(NH 2 ) 3-x (NHSiMe 3 ) x and [P=N] 3 (NHSiMe 3 ) 6–x (NH) x . Furthermore, the resulting systems have degrees of polymerization of 5–20. Treatment with selected amounts of LiNH 2 provides varying degrees of lithiation and Li + conducting properties commensurate with Li + content. Polymer electrolytes impregnated in/on Celgard exhibit Li + conductivities up to ~1 × 10 –5 S cm –1 at room temperature and are thermally stable to ~150 °C. A Li–S battery assembled using a Li 6 SiPON composition polymer electrolyte exhibits an initial reversible capacity of 1500 mAh g sulfur –1 and excellent cycle performance at 0.25 and 0.5 C rate over 120 cycles at room temperature.

25 ENERGY STORAGE↗

DOE OSTI2020

Design, Synthesis, and Characterization of Polymer Precursors to Li x PON and Li x SiPON Glasses: Materials That Enable All-Solid-State Batteries (ASBs)

LiPON-like glasses that form lithium dendrite impenetrable interfaces between lithium battery components are enabling materials that may replace liquid electrolytes permitting production of all-solid-state batteries (ASBs). Unfortunately, to date, such materials are introduced only via gas-phase deposition. Furthermore, we demonstrate the design and synthesis of easily scaled, lowtemperature, low-cost, solution-processable inorganic polymers containing LiPON/LiSiPON elements. OPCl 3 and hexachlorophosphazene [Cl 2 P=N] 3 provide starting points for elaboration using MNH 2 (M = Li/Na) or (Me 3 Si)NH followed by reaction with controlled amounts of LiNH 2 to produce oligomers/polymers with molecular weights (MWs) ≈1–2 kDa characterized by multinuclear NMR, gel permeation chromatography (GPC), thermogravimetric analysis (TGA), Fourier-transform infrared (FTIR), X-ray powder diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and matrix-assisted laser desorption/ ionization (MALDI)-time-of-flight (ToF) offering stabilities to 150–200 °C and ceramic yields (800 °C) of 50–60%. 7 Li NMR suggests that precursor-bound Li + dissociates easily, beneficial for electrochemical applications. XPS shows higher N/P ratios (1–3) than via gas-phase methods (<1) correlating N/P ratios, 7 Li shifts, and Li + conductivities. Li 2 SiPHN offers the highest ambient conductivity of 3 × 10 –1 mS cm –1 at 400 °C/2 h/N 2 .

36 MATERIALS SCIENCE↗