NASA NTRS1979

Mechanical property degradation and chemical interactions in Borsic/titanium composite

A study was undertaken to identify the mechanisms of mechanical property degradation in a Borsic (silicon-carbide coated boron) fiber reinforced Ti-3Al-2.5V composite exposed to elevated temperature. Samples containing 0.45 volume fraction of fibers were exposed, in vacuum, to temperatures from 700 K to 1255 K for times up to 240 hours. Room temperature tensile properties of unidirectional material were determined in both the longitudinal and transverse directions, before and after high-temperature exposure. Electron micro-probe analysis, scanning electron microscopy, and X-ray diffraction were used to determine the compounds formed and the extent of interaction between the boron, SiC coating, and matrix materials.

Brewer, W. D.↗

NASA NTRS1979

Interfacial reactions in borsic/Ti-3Al-2-1/2V composite

The paper provides a detailed X-ray characterization of a borsic/Ti-3Al-2-1/2V composite, and to correlate the relative intensities of the reaction products with the mechanical properties. Based on X-ray integrated intensity data two stages of interface reactions were identified: during the first stage there is a simultaneous interdiffusion of Si, C, and Ti atoms at the filament/matrix interface resulting in the formation of Ti5Si3, TiSi and small amounts of TiSi2 and TiC. The second stage is associated with considerable TiSi2 and boride formation. It appears that the alpha-phase of Ti is more reactive in forming silicides and borides than the beta-phase. The silicide intensities and the reaction zone thicknesses are shown to be directly related to the reduction of the ultimate tensile strength by thermal degradation, and the results indicate that silicide reaction products are as detrimental to strength as the borides.

Rao, V. B.↗

NASA NTRS1978

Geometric relationships for homogenization in single-phase binary alloy systems

A semiempirical relationship is presented which describes the extent of interaction between constituents in single-phase binary alloy systems having planar, cylindrical, or spherical interfaces. This relationship makes possible a quick estimate of the extent of interaction without lengthy numerical calculations. It includes two parameters which are functions of mean concentration and interface geometry. Experimental data for the copper-nickel system are included to demonstrate the usefulness of this relationship.

Unnam, J.↗

NASA NTRS1978

Effect of concentration dependence of the diffusion coefficient on homogenization kinetics in multiphase binary alloy systems

Diffusion calculations were performed to establish the conditions under which concentration dependence of the diffusion coefficient was important in single, two, and three phase binary alloy systems. Finite-difference solutions were obtained for each type of system using diffusion coefficient variations typical of those observed in real alloy systems. Solutions were also obtained using average diffusion coefficients determined by taking a logarithmic average of each diffusion coefficient variation considered. The constant diffusion coefficient solutions were used as reference in assessing diffusion coefficient variation effects. Calculations were performed for planar, cylindrical, and spherical geometries in order to compare the effect of diffusion coefficient variations with the effect of interface geometries. In most of the cases considered, the diffusion coefficient of the major-alloy phase was the key parameter that controlled the kinetics of interdiffusion.

Tenney, D. R.↗

NASA NTRS1978

Prediction of moisture and temperature changes in composites during atmospheric exposure

The effects of variations in diffusion coefficients, surface properties of the composite, panel tilt, ground reflection, and geographical location on the moisture concentration profiles and average moisture content of composite laminates were studied analytically. A heat balance which included heat input due to direct and sky diffuse solar radiation, ground reflection, and heat loss due to reradiation and convection was used to determine the temperature of composites during atmospheric exposure. The equilibrium moisture content was assumed proportional to the relative humidity of the air in the boundary layer of the composite. Condensation on the surface was neglected. Histograms of composite temperatures were determined and compared with those for the ambient environment.

Tompkins, S. S.↗

NASA NTRS1978

Tensile and compressive stress-strain behavior of heat treated boron-aluminum

An experimental study was conducted to assess the effects of heat treatment and cyclic mechanical loading on the tensile and compressive stress-strain behavior of six boron-aluminum composites having different laminate orientations and being subjected to different heat treatments. The heat treatments were as-fabricated, T6, and T6N consisting of T6 treatment followed by cryogenic quench in liquid nitrogen prior to testing. All laminates were tested in monotonic and cyclic compression, while the tensile-test data are taken from the literature for comparison purposes. It is shown that the linear elastic range of the T6- and T6N-condition specimens is larger than that of the as-fabricated specimens, and that cyclic loading in tension or compression strain hardens the specimens and extends the linear elastic range. For laminates containing 0-deg plies, the stress-strain behavior upon unloading is found to be nonlinear, whereas the other laminates exhibit a linear behavior upon unloading. Specimens in the T6 and T6N conditions show higher strain hardening than the as-fabricated specimens.

Kennedy, J. M.↗

NASA NTRS1978

Numerical analyses for treating diffusion in single-, two- and three-phase binary alloy systems

Numerical solutions were applicable for planar, cylindrical, or spherical geometries with any diffusion-zone size and any continuous variation of the diffusion coefficient with concentration. Special techniques were included in the analyses to account for differences in molal volumes, initiation and growth of an intermediate phase, disappearance of a phase, and the presence of an initial composition profile in the specimen. A major improvement in solution accuracy was achieved in the two phase analysis by employing a mass conservation criterion to establish the location of the interface rather than the conventional interface-flux-balance criterion. In the three phase analysis, computation time was minimized without sacrificing solution accuracy by treating the three phase problem as a two phase problem when the thickness of the intermediate phase was less than a preset small value. Three computer codes were developed to perform these analyses.

Tenney, D. R.↗

NASA NTRS1978

Effect of cyclic loading and temper condition on the tensile behavior of boron-aluminum

Experimental results from monotonic and cyclic tension tests on six different 6061 boron-aluminum laminates show that the strength of fiber dominated laminates is decreased and the strength of matrix dominated laminates is increased by T6 heat treatment. Cyrogenic exposure and cyclic loading are shown to have little influence on strength. Cyclic loading is also shown to produce small reductions in modulus for some laminates and some temper conditions. The results are discussed in light of expected metallurgical and residual stress changes due to temperature excursions and loading cycles.

Herakovich, C. T.↗

NASA NTRS1977

Correction factors for on-line microprobe analysis of multielement alloy systems

An on-line correction technique was developed for the conversion of electron probe X-ray intensities into concentrations of emitting elements. This technique consisted of off-line calculation and representation of binary interaction data which were read into an on-line minicomputer to calculate variable correction coefficients. These coefficients were used to correct the X-ray data without significantly increasing computer core requirements. The binary interaction data were obtained by running Colby's MAGIC 4 program in the reverse mode. The data for each binary interaction were represented by polynomial coefficients obtained by least-squares fitting a third-order polynomial. Polynomial coefficients were generated for most of the common binary interactions at different accelerating potentials and are included. Results are presented for the analyses of several alloy standards to demonstrate the applicability of this correction procedure.

Unnam, J.↗

NASA NTRS1977

Influence of temper condition on the nonlinear stress-strain behavior of boron-aluminum

The influence of temper condition on the tensile and compressive stress-strain behavior for six boron-aluminum laminates was investigated. In addition to monotonic tension and compression tests, tension-tension, compression-compression, and tension--compression tests were conducted to study the effects of cyclic loading. Tensile strength results are a function of the laminate configuration; unidirectional laminates were affected considerably more than other laminates with some strength values increasing and others decreasing.

Kennedy, J. M.↗

NASA NTRS1977

Analytical prediction of moisture absorption/desorption in resin matrix composites exposed to aircraft environments

The moisture absorption/desorption behavior of resin matrix composites was mathematically modeled by classical diffusion theory using an effective diffusion coefficient. Good agreement was found between calculated moisture content and published data for T300/5208 graphite fiber reinforced epoxy matrix composite. Weather Bureau data for Langley Air Force Base and Norfolk, Va., were used to calculate the amount of moisture a T300/5208 composite panel would contain if exposed outdoors. Results obtained by using average monthly weather data for several high aircraft usage locations around the world suggest that, except for desert areas, geographical locations should have only minimal effect on the moisture absorption level reached in composites. Solar radiation data together with cloud and wind information were included in the analysis to estimate an effective temperature of the composite panel during ground exposure.

Unnam, J.↗

NASA NTRS1976

Diffusion analysis for two-phase metal-matrix composite

Diffusion controlled filament matrix interaction in a metal matrix composite, where the filaments and matrix comprise a two phase binary alloy system, was mathematically modeled. The problem of a diffusion controlled, two phase moving interface by means of a one dimensional, variable grid, finite difference technique was analyzed. Concentration dependent diffusion coefficients and equilibrium solubility limits were used, and the change in filament diameter and compositional changes in the matrix were calculated as a function of exposure time at elevated temperatures. With the tungsten nickel (W-Ni) system as a model composite system, unidirectional composites containing from 0.06 to 0.44 initial filament volume fraction were modeled. Compositional changes in the matrix were calculated by superposition of the contributions from neighboring filaments. Alternate methods for determining compositional changes between first and second nearest neighbor filaments were also considered. The results show the relative importance of filament volume fraction, filament diameter, exposure temperature, and exposure time as they affect the rate and extent of filament matrix interaction.

Tenney, D. R.↗

NASA NTRS1975

Dynamic oxidation behavior of TD-NiCr alloy with different surface pretreatments

Oxidation tests of TD-NiCr alloy with different surface pretreatments were conducted in a Mach-5 arc-jet at 1200 C and 0.002 lb/sec flowing air environment. The mechanisms responsible for the observed oxidation behavior are examined. The presence of atomic oxygen in the air stream plays a significant role in determining the oxidation characteristic of the alloy. The rate of Cr2O3 vaporization by formation of volatile CrO3 is greatly enhanced by the flowing conditions. The typical microstructure of oxides formed in the dynamic tests consists of an external layer of NiO with a porous mushroom-type morphology, an intermediate layer of NiO and Cr2O3 oxide mixture, and a continuous inner layer of Cr2O3 in contact with the Cr-depleted alloy substrate. Three basic processes underlying the formation of mushroom-type NiO are identified and discussed. The oxidation rate is determined by the rate of vaporization of NiO. Surface pretreatment has a significant effect on the oxidation behavior of the alloy in the early stage of oxidation, but becomes less important as exposure time increases. Mechanical polishing induces surface recrystallization, but promotes the concurrence of external growth of NiO and internal oxidation of the alloy in the dynamic atmosphere.

Young, C. T.↗

NASA NTRS1974

Interdiffusion in the Ni/TD-NiCr and Cr/TD-NiCr systems

The diffusion of Ni and Cr into TD-NiCr has been studied over the 900 to 1100 C temperature range. The diffusion couples were prepared by electroplating Cr and Ni on polished TD-NiCr wafers. Concentration profiles produced as a result of isothermal diffusion at 905, 1000, and 1100 C were determined by electron microprobe analysis. The Boltzmann-Matano analysis was used to determine concentration-dependent diffusion coefficients which were found to compare favorably with previously reported values. These data suggest that 2 vol % ThO2 distribution has no appreciable effect on the rates of diffusion in TD-NiCr with a large grain size. This supports the view that an inert dispersoid in an alloy matrix will not in itself lead to enhanced diffusion unless a short-circuit diffusion structure is stabilized.

Pawar, A. V.↗

NASA NTRS1974

Oxidation behavior of TD-NiCr in a dynamic high temperature environment

The oxidation behavior of TD-NiCr has been studied in static and high-speed flowing air environments at 1100 and 1200 C. It has been found that the stable oxide morphologies formed on the specimens exposed to the static and dynamic environments were markedly different. The faceted crystal morphology characteristic of static oxidation was found to be unstable under high-temperature, high-speed flow conditions and was quickly replaced by a porous NiO 'mushroom' type structure. Also, it was found that the rate of formation of CrO3 from Cr2O3 was greatly enhanced by high gas velocity conditions. The stability of Cr2-O3 was found to be greatly improved by the presence of an outer NiO layer, even though the NiO layer was very porous. An oxidation model is proposed to explain the observed microstructures and overall oxidation behavior of TD-NiCr alloys.

Tenney, D. R.↗

NASA NTRS1974

Investigation of the oxidation behavior of dispersion stabilized alloys when exposed to a dynamic high temperature environment

The oxidation behavior of TD-NiCr and TD-NiCrAlY alloys have been studied at 2000 and 2200 F in static and high speed flowing air environments. The TD-NiCrAlY alloys preoxidized to produce an Al2O3 scale on the surface showed good oxidation resistance in both types of environments. The TD-NiCr alloy which had a Cr2O3 oxide scale after preoxidation was found to oxidize more than an order of magnitude faster under the dynamic test conditions than at comparable static test conditions. Although Cr2O3 normally provides good oxidation protection, it was rapidly lost due to formation of volatile CrO3 when exposed to the high speed air stream. The preferred oxide arrangement for the dynamic test consisted of an external layer of NiO with a porous mushroom type morphology, an intermediate duplex layer of NiO and Cr2O3, and a continuous inner layer of Cr2O3 in contact with the alloy substrate. An oxidation model has been developed to explain the observed microstructure and overall oxidation behavior of all alloys.

Tenney, D. R.↗

NASA NTRS1974

A study of the diffusional behavior of a two-phase metal matrix composite exposed to a high temperature environment

The progress of diffusion-controlled filament-matrix interaction in a metal matrix composite where the filaments and matrix comprise a two-phase binary alloy system was studied by mathematically modeling compositional changes resulting from prolonged elevated temperature exposure. The analysis treats a finite, diffusion-controlled, two-phase moving-interface problem by means of a variable-grid finite-difference technique. The Ni-W system was selected as an example system. Modeling was carried out for the 1000 to 1200 C temperature range for unidirectional composites containing from 6 to 40 volume percent tungsten filaments in a Ni matrix. The results are displayed to show both the change in filament diameter and matrix composition as a function of exposure time. Compositional profiles produced between first and second nearest neighbor filaments were calculated by superposition of finite-difference solutions of the diffusion equations.

Tenney, D. R.↗

NASA NTRS1973

Diffusion in a unidirectional filament reinforced metal composite.

A theoretical analysis has been developed to describe composition changes resulting from exposure of a unidirectional filament reinforced metal composite to an elevated temperature environment. The analysis was based on a simple superposition of finite-difference solutions of the diffusion equation, and was applicable to the case for which the filament and matrix metals comprised an isomorphous binary alloy system. The possibility of chemical reaction between filaments and matrix was excluded. Excellent agreement was obtained between calculated concentration profiles and results of quantitative electron microprobe analyses of nickel filament reinforced copper samples.

Herring, H. W.↗