DOE OSTI2021

Diamond channel-cut crystals for high-heat-load beam-multiplexing narrow-band X-ray monochromators

Next-generation high-brilliance X-ray photon sources call for new X-ray optics. Here we demonstrate the possibility of using monolithic diamond channel-cut crystals as high-heat-load beam-multiplexing narrow-band mechanically stable X-ray monochromators with high-power X-ray beams at cutting-edge high-repetition-rate X-ray free-electron laser (XFEL) facilities. The diamond channel-cut crystals fabricated and characterized in these studies are designed as two-bounce Bragg reflection monochromators directing 14.4 or 12.4 keV X-rays within a 15 meV bandwidth to 57 Fe or 45 Sc nuclear resonant scattering experiments, respectively. The crystal design allows out-of-band X-rays transmitted with minimal losses to alternative simultaneous experiments. Only ≲2% of the incident ∼100 W X-ray beam is absorbed in the 50 µm-thick first diamond crystal reflector, ensuring that the monochromator crystal is highly stable. Other X-ray optics applications of diamond channel-cut crystals are anticipated.

73 NUCLEAR PHYSICS AND RADIATION PHYSICS↗

DOE OSTI2021

High-brightness self-seeded X-ray free-electron laser covering the 3.5 keV to 14.6 keV range

A self-seeded X-ray free-electron laser (XFEL) is a promising approach to realize bright, fully coherent free-electron laser (FEL) sources in the hard X-ray domain that have been a long-standing issue with longitudinal coherence remaining challenging. Additionally, at the Pohang Accelerator Laboratory XFEL, we have demonstrated a hard X-ray self-seeded XFEL with a peak brightness of 3.2 × 10 35 photons s –1 mm –2 mrad –2 0.1% bandwidth (BW) –1 at 9.7 keV. The bandwidth (0.19 eV) is about 1/70 times as wide (close to the Fourier transform limit) and the peak spectral brightness is 40 times higher than in self-amplified spontaneous emission (SASE), with substantial improvements in the stability of self-seeding and noticeably suppressed pedestal effects. We could reach an excellent self-seeding performance at a photon energy of 3.5 keV (lowest) and 14.6 keV (highest) with the same stability as the 9.7 keV self-seeding. The bandwidth of the 14.6 keV seeded FEL was 0.32 eV, and the peak brightness was 1.3 × 10 35 photons s –1 mm –2 mrad –2 0.1%BW –1 . We show that the use of seeded FEL pulses with higher reproducibility and a cleaner spectrum results in serial femtosecond crystallography data of superior quality compared with data collected using SASE mode.

47 OTHER INSTRUMENTATION↗

DOE OSTI2020

Small Bragg-plane slope errors revealed in synthetic diamond crystals

Wavefront-preserving X-ray diamond crystal optics are essential for numerous applications in X-ray science. Perfect crystals with flat Bragg planes are a prerequisite for wavefront preservation in Bragg diffraction. However, this condition is difficult to realize in practice because of inevitable crystal imperfections. Here, X-ray rocking curve imaging is used to study the smallest achievable Bragg-plane slope errors in the best presently available synthetic diamond crystals and how they compare with those of perfect silicon crystals. It is shown that the smallest specific slope errors in the best diamond crystals are about 0.08 (3) µrad mm -2 . These errors are only 50% larger than the 0.05 (2) µrad mm -2 specific slope errors measured in perfect silicon crystals. High-temperature annealing at 1450°C of almost flawless diamond crystals reduces the slope errors very close to those of silicon. Further investigations are in progress to establish the wavefront-preservation properties of these crystals.

73 NUCLEAR PHYSICS AND RADIATION PHYSICS↗