Ultrafast microscopy and image segmentation of spatially heterogeneous excited state and trap passivation in Cu2BaSnSSe3
Not Available
37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
Engineering topics
Teymur, Betul
Publications and source records attributed to Teymur, Betul.
Top Stack Optimization for Cu 2 BaSn(S, Se) 4 Photovoltaic Cell Leads to Improved Device Power Conversion Efficiency beyond 6%
Earth-abundant and air-stable Cu 2 BaSnS 4-x Se x (CBTSSe) and related thin-film absorbers are regarded as prospective options to meet the increasing demand for low-cost solar cell deployment. Devices based on vacuum-deposited CBTSSe absorbers have achieved record power conversion efficiency (PCE) of 5.2 % based on a conventional device structure using CdS buffer and i-ZnO/ITO window layers, with open-circuit voltage (V OC ) posing the major bottleneck for improving solar cell performance. The current study demonstrates a >20 % improvement in V OC (from 0.62 V to 0.75 V) and corresponding enhancement in PCE (from 5.1 % to 6.2 % without anti-reflection coating; to 6.5 % with MgF 2 anti-reflection coating) for solution-deposited CBTSSe solar cells. This performance improvement is realized by introducing an alternative successive ionic layer adsorption and reaction (SILAR)-deposited Zn 1-x Cd x S buffer combined with sputtered Zn 1-x Mg x O/Al-doped ZnO window/top contact layer, which offer lower electron affinities relative to the conventional CdS/i-ZnO/ITO stack and better matching with the low electron affinity of CBTSSe. A combined experimental (temperature- and light intensity-dependent V OC measurements) and device simulation (SCAPS-1D) evaluation points to the importance of addressing relative band offsets for both the buffer and window layers relative to the absorber in mitigating interfacial recombination and optimizing CBTSSe solar cell performance.
25 ENERGY STORAGE↗
Influence of Copper Composition on Cu 2 BaSn(S,Se) 4 Solution-Deposited Films and Photovoltaic Devices with Over 5% Efficiency
Cu 2 BaSn(S,Se) 4 is currently in the spotlight for prospective environmentally friendly, stable, thin-film solar cell application, with demonstrated device power conversion efficiency (PCE) exceeding 5% for vacuum-deposited absorbers. As suggested by first-principles calculations, experimental studies involving related Cu 2 ZnSn(S,Se) 4 and Cu(In,Ga)(S,Se) 2 absorbers prove that the detailed chemical composition typically plays a sensitive role in altering defects and electronic properties of these complicated compound semiconductors. Herein, the copper composition of Cu 2 BaSn(S,Se) 4 has been systematically modified, employing a solution-based deposition approach, to provide a more complete picture of the phase stability and optoelectronic property sensitivity for this material. X-ray diffraction and scanning electron microscopy show that phase purity is preserved over a film Cu content range of nominally 0.94 ≤ [Cu]/[Ba + Sn] ≤ 1.01. Terahertz spectroscopy and Hall effect measurements reveal that the majority carrier hole density of ~10 13 cm –3 and mobility (~5 cm 2 /V s), as well as the minority carrier lifetime (a bulk lifetime of 180 ps and a surface recombination velocity >106 cm/s), are nominally independent of Cu content. The champion PCEs exceed 4.7% for all copper compositions in the phase-pure region, with a record value of 5.1%, similar to the reported values for record vacuum-deposited devices. Furthermore, these results suggest that Cu 2 BaSn(S,Se) 4 films and solar cells (at the current performance level) may be less sensitive to Cu stoichiometry compared to kesterite materials and therefore may provide a more stable material platform to prepare thin-film solar cells.
(CBTSSe)↗
Porous Cu 2 BaSn(S,Se) 4 Film as a Photocathode Using Non-Toxic Solvent and a Ball-Milling Approach
Cu 2 BaSn(S,Se) 4 (CBTSSe) has been proposed as an alternative to Cu 2 ZnSn(S,Se) 4 (CZTSSe) for solar absorbers due to its reduced propensity for antisite disorder and band tailing, while maintaining the desirable characteristics of band gap tunability, earth-abundance, and low toxicity constituent metals. However, current film deposition methods require high-vacuum conditions or toxic solvents, less desirable features for prospective large-scale production. Here, ball milling is demonstrated as a route towards a scalable processing method for CBTSSe, using a precursor ink consisting of common elements Cu 2 S, BaS, Sn, and S in low-toxicity ethanol. A final film with a thickness and average grain size on the order of 1 µm was synthesized with a band gap of 1.56 eV, corresponding to a Cu 2 BaSnS 4-x Se x (x ≈ 3) stoichiometry. A porous CBTSSe photocathode with Pt/TiO 2 /CdS overlayers was fabricated to demonstrate the photocurrent-generating capabilities of the film, yielding current densities of as high as 5.54 mA/cm 2 at 0 V versus a reversible hydrogen electrode (V/RHE) .
14 SOLAR ENERGY↗
Optoelectronic and material properties of solution-processed Earth-abundant Cu 2 BaSn(S, Se) 4 films for solar cell applications
Copper barium thioselenostannate, Cu 2 BaSnS 4-x Se x (CBTSSe), absorbers employ low-toxicity and abundant metals while offering low-cost manufacturing options, controllable stoichiometry and band gap tunability (from 2 eV at x = 0 to 1.55 eV at x = 3). CBTSSe can therefore be considered a prospective candidate for maintaining or improving upon the advantages of already commercialized Cu(In,Ga)(S,Se) 2 (CIGSSe) and CdTe absorbers. Here, we focus on solution-deposited stoichiometric CBTSSe films with band gap of 1.59 eV (x ≈ 3) and explore the fundamental film properties. Temperature- and excitation-dependent photoluminescence studies reveal a dominant defect emission at ~1.5 eV and a second deep defect feature at 1.15 eV. From time-resolved terahertz measurements, we find a charge carrier (electron and hole sum) mobility of ~140 cm 2 /Vs—i.e., comparable to values in CIGSSe or Cu 2 ZnSnS 4-x Se x (CZTSSe)—as well as a two-component minority carrier lifetime. A longer-lived lifetime component (~2 ns) arises from bulk recombination. However, strong recombination at the (bare) surface leads to a ~50 ps lifetime, inferior to state-of-the-art CIGSSe or CZTSSe absorbers. This recombination issue may worsen for CBTSSe/CdS interfaces, due to a cliff-like band alignment with 0.6 eV band offset, as revealed by ultraviolet photoemission spectroscopy. A low number of charge carriers within the absorber further contributes to a high series resistance. Employing these films, we also report the highest performance achieved from solution-processed trigonal CBTSSe thin-film photovoltaic devices, with open circuit voltage, short-circuit current density, fill factor and efficiency of 470 mV, 14.3 mA/cm 2 , 43.6% and 2.9%, respectively. The physical measurements provided on the stoichiometric solution-processed CBTSSe absorber further point to critical areas for future improvement of CBTSSe and related photovoltaic cells in the quest for higher efficiency devices based on earth abundant metals.
14 SOLAR ENERGY↗