Publications and source records attributed to Thellen, Christopher.

6 records

DOE OSTI2024

Material characterization of seven photovoltaic backsheets using seven accelerated test conditions

A variety of polymeric backsheet materials can be found in fielded photovoltaic (PV) modules, mostly based on fluoropolymer and polyethylene terephthalate (PET) materials. Cost reduction and sustainability considerations drive the recent development of alternative backsheet materials and designs [1]. In some fielded PV installations, polymeric materials are susceptible to environmental degradation in the form of backsheet cracking. To prevent backsheet degradation that can result in a module failure, thorough laboratory reliability testing is needed. In this report we studied the durability of seven commercial and experimental PV backsheets through accelerated stress testing using seven photolytic, hygrometric, and custom tests with the goal to understand if novel fluoropolymer-free backsheets are sufficiently environmentally durable to be commercialized. We divided the mechanisms observed during aging into two categories: core degradation and surface degradation. Although core degradation due to hydrolysis was observed in all commercial PET-, and polyamide (PA)-based backsheets aged with 85 degrees C/85% relative humidity, this test is unlikely to be field relevant. Photo-oxidative reactions on the exposed surface during UV weathering affected all seven backsheets regardless of the outer layer polymer material and additives. This degradation was limited to the outermost micrometers of the surface, except for backsheets containing PA-12, which resulted in surface cracking. A custom test combining UV with water spray caused the most severe backsheet degradation, including surface erosion and loss of insulating properties in polyolefin (PO)- and PA-based backsheets. This highlights the importance of combined accelerated stress testing to screen for complex backsheet degradation mechanisms. We also showed that, with material and design optimization, coextruded experimental PO-based backsheets have the potential to be a durable alternative to commercial PET- and fluoropolymer-based PV backsheets.

14 SOLAR ENERGY↗

DOE OSTI2022

Arrhenius Analysis of the Degradation Modes in Emerging Photovoltaic Backsheets

With increasingly large-scale deployments of photovoltaic (PV) modules to meet global energy demands, interest in better establishing modules' lifespans is growing. We report on the performance of co-extruded polyolefin- (PO)-based backsheets as environmentally friendly alternatives to fluoropolymer-reinforced polyethylene-terephthalate (PET)-based backsheets using three hygrometric accelerated test conditions. After completing cumulative 4000 hours of aging, we analyzed data from electrical performance (I-V), surface roughness (gloss), and appearance (L, a*, b* color) characterizations to quantify degradation rates, quantify the corresponding activation energy, and cross-correlate between the characteristics examined, thereby providing insights into the relationship between physical characteristics and operating performance.

BackFLIP↗

DOE OSTI2022

Arrhenius Analysis of the Degradation Modes in BackFLIP Study of Emerging Photovoltaic Backsheets: Preprint

With increasingly large-scale deployments of photovoltaic (PV) modules to meet global energy demands, interest in better establishing module lifespans is growing. We report on the performance of co-extruded polyolefin- (PO) based backsheets as environmentally friendly alternatives to fluoropolymer-reinforced polyethylene-terephthalate- (PET)-based backsheets using three hygrometric accelerated test conditions. After completing 4000 cumulative hours of aging, we analyzed data from electrical performance (I-V), surface roughness (gloss), and appearance (L, a*, b* color) characterizations are analyzed to quantify degradation rates, quantify the corresponding activation energy, and cross-correlate between the characteristics examined, thereby providing insights into the relationship between physical characteristics and operating performance.

BackFLIP↗

DOE OSTI2021

Thermomechanical and sequential stress performance of photovoltaic backsheets

Photovoltaic backsheet technology is utilized to protect the interior components of solar modules from environmental stress as well as provide electrical insulation to the module. The growing demand for solar energy and longer module service life requirements have brought backsheet performance into focus. Despite being a protective packaging material, many backsheets have exhibited failure in the field, limiting the performance and service life of entire modules. Most backsheets consist of multiple polymeric layers laminated together using adhesives. A new backsheet, with a high performance polyamide structure, has been developed as the solution to module failure. Primarily, it contains a unique polyamide-ionomer alloy targeted at improved weather resistance. In this study, several photovoltaic industry standard backsheets, and the novel polyamide compositions of multilayered backsheets fabricated from the coextrusion process, were examined using thermomechanical analysis (TMA). The coefficient of thermal expansion (CTE) for entire backsheets and their constituent layers was used to model the thermomechanical behavior of various backsheet constructions. Subsequently, thermal cycling was performed in the TMA to examine the intrinsic thermal behavior of the backsheets. Thermal cycling in the TMA indicates the resilience and dimensional stability in the coextruded structures as opposed to the laminated structures. Lastly, results from a Module Accelerated Sequential Testing (MAST), are included to show the mechanical integrity of these backsheets after sequential exposure to stressors including damp heat, ultra-violet (UV) light radiation, and thermal cycling. The laminate backsheets deteriorated extensively after sequential exposure to these stressors, while the novel coextruded structures retained their physical properties.

14 SOLAR ENERGY↗

DOE OSTI2021

Evaluating Non-Fluoropolymer-Based Co-Extruded Backsheets Using Combined-Accelerated Stress Testing and Materials Forensics

Co-extruded, non-fluoropolymer backsheet films for photovoltaic (PV) modules have gained popularity in recent years based on their cost competitiveness. However, their viability has been thrown into question as a result of widespread, early-life field-failures of some materials, particularly the polyamide (PA)-based “AAA” backsheet product. Failure to detect weaknesses in those earlier products could be due, in part, to insufficient quality testing practices. New testing protocols have recently been developed to better evaluate such materials. Here we show the testing results for a non-fluoropolymer, co-extruded PA-based backsheet film, which demonstrates greater durability than AAA and some commercial fluoropolymers. Using material characterization techniques including Fourier-transform infrared spectroscopy (FTIR), wide-angle x-ray scattering (WAXS), differential scanning calorimetry (DSC), X-ray photoelectron spectroscopy (XPS), elongation-to-break (ETB), and optical microscopy we perform a comprehensive failure analysis to better understand the materials weaknesses. This analysis can ultimately inform how best to improve the material and extend its lifetime. This work serves as a demonstration that some materials should not be discounted due to a single poorly designed product and that more appropriate qualification testing with subsequent materials analysis can be used to develop better materials.

41 EE - Solar Energy Technologies Office (EE-4S)↗

DOE OSTI2020

Cost Efficient and Highly Weather-Resistant Solar Panel Backsheet Produced through Continuous Co-Extrusion Processing

The efficient generation and delivery of ‘clean energy” through photovoltaic (PV) technology relies heavily on the cost, performance and reliability of solar panels, along with the individual components used in assembly of those panels. In order to continue towards the Department of Energy’s (DOE) goals of driving costs down, the lifetime of high-output power generation equipment (i.e. solar modules) must be extended to reduce costs associated with power output degradation and replacement of failed or degraded panels. One of the major sources of module failures in the past 30 years has been the failure of the solar panel backsheet. Failure of this component causes severe output losses due to oxidation and yellowing of the module while creating safety concerns as the major electrical insulation of the module is compromised. Tomark-Worthen LLC was formed in 2012 with the goal of designing and manufacturing novel PV backsheets and encapsulants that would be produced in the United States of America and exceed expectations of domestic and international module producers. These backsheets would improve upon known backsheet design failures (i.e. Isovoltaic’s AAA backsheet) and create domestic manufacturing jobs in the PV sector. This goal became a reality with a first-generation product in 2018 and now, with the support of the DOE, Tomark-Worthen has launched a second-generation product known as PhotoMark® Reflections™ 205-3 and 360-3. This 2+ year effort began in late 2017 with a screening of potential polymeric materials and backsheet structural designs. Performance evaluations of each material provided the necessary data needed to select the proper material combinations and move forward into the design of the manufacturing process. These decisions were made by teaming with a local university, well-respected government laboratories, and private research organizations who provided the tools necessary to predict long-term performance of these materials in much shorter periods of time. Once the go/no-go criteria were met at the mid-point of the project, the effort transitioned to predicting 30+ year performance, achieving certifications, and improving manufacturing efficiencies designed to lower costs in order to be competitive in a cost-driven market. Major project accomplishments include recognition of the new backsheet by Underwriters Laboratories (UL) and international certification for 1000V and 1500V modules by TUV Sud. Both 1000V and 1500V products have been proven on several module manufacturing lines and initial customer orders have been received by both domestic and international module producers. Accelerated exposure testing has shown that the performance of this backsheet exceeds the prior polyamide-based backsheet known to fail in the field. Cost-models and initial customer orders have shown the ability to produce this backsheet at a cost acceptable to many domestic manufacturers, while International costs for standard backsheet remains extremely low. Tomark-Worthen remains one of the only U.S. companies manufacturing backsheet domestically and this has drawn interest from many domestic module manufacturers looking to improve their material supply logistics by avoiding long lead times and custom’s headaches while avoiding current tariffs on Chinese-made components. Along with the launch of a new PV backsheet, this project has provided a critical deliverable to the PV R&D community. This deliverable is the knowledge that not all polyamide-containing backsheets are doomed to failure as the earlier versions did. There has been a fear amongst the PV community to consider these materials due to the failure of one design. This effort has brought a new level of interest to the scientific community as it has been shown that polyamides can be used successfully in a well-designed backsheet. As we move forward from this project, we are excited to see how backsheet technology and manufacturing in the U.S. will continue to progress and grow.

14 SOLAR ENERGY↗