Engineering topics
Thoma, D. J.
Publications and source records attributed to Thoma, D. J..
Spall damage mechanisms in laser powder bed fabricated stainless steel 316L
This paper reports on spall damage mechanisms in laser powder bed fusion (LPBF) fabricated stainless steel 316L (SS316L) subjected to uniaxial, strain plate-impact loading and explores failure evolution with increasing impact velocity and peak pressure. Analysis of velocimetry profiles reveals a heterogeneous failure response with several different failure mechanisms activated during impact and resulting spall. The analysis is supported by optical microscopy and electron backscattered diffraction (EBSD) observation of soft recovered impacted samples, which show evidence of localized nano-twinning, twin growth, severe grain rotation, and grain refinement along the spall plane, in addition to pore nucleation, coalescence, and growth. Furthermore, the observed failure mechanisms, including crack formation and propagation along high angle grain boundaries (HAGBs), are not consistently indicative of ductile fracture typical of wrought stainless steel.
Hydrogen embrittlement of additively manufactured austenitic stainless steel 316 L
Additive manufacturing (AM) is a promising means of production of austenitic stainless steel (SS) parts for hydrogen service. The hydrogen embrittlement resistance of SS 316 L parts manufactured by powder-bed-fed selective laser melting (SLM) and directed energy deposition (DED) was examined using slow strain rate tensile testing. The influence of the hierarchical AM microstructures on mechanical response, microstructural evolution, and void formation were analyzed using multiscale electron microscopy. Furthermore, the presence of hydrogen reduced ductility in as-built DED materials, but did not significantly influence the response in as-built SLM material or heat-treated materials. Microstructural features driving these different responses are discussed.
Origin of dislocation structures in an additively manufactured austenitic stainless steel 316L
In this experiment, the origin of dislocation structures in AM stainless steels was systematically investigated by controlling the effect of thermal stress through geometric constraints for the first time. Stainless steel 316L parts were produced in the form of “1D” rods, “2D” walls, and "3D" rectangular prisms to evaluate the effect of constraints to thermal expansion/shrinkage on the development of defect microstructures and to elucidate the origin of additively manufactured (AM) dislocation microstructures. Dislocation density, organization, chemical micro-segregation, precipitate structures, and misorientations were analyzed as a function of increasing constraints around solidifying material in 1D, 2D, and 3D components built using both directed energy deposition (DED) and powder-bed selective laser melting (SLM). In DED parts, the dislocation density was not dependent on local misorientations or micro-segregation patterns, but evolved from approximately ρ ⊥ = 10 12 m -2 in 1D parts to ρ ⊥ = 10 14 m -2 in 3D parts, indicating that it is primarily thermal distortions that produce AM dislocation structures. In DED 3D parts and SLM parts, dislocation densities were highest (ρ ⊥ ≈ 10 14 m -2 ) and corresponded to the formation of dislocation cells approximately 300-450 nm in diameter. Dislocation cells overlapped with dendrite micro-segregation in some but not all cases. The results illustrate that dendritic micro-segregation, precipitates, or local misorientations influence how the dislocations organize during processing, but are not responsible for producing the organized cell structures. Furthermore, this work shows that AM dislocation structures originate due to thermal distortions during printing, which are primarily dictated by constraints surrounding the melt pool and thermal cycling.
Microstructural transitions during containerless processing of undercooled Fe-Ni alloys
In order to identify the possible hierarchy of microstructural pathways and transitions, a systematic evaluation of the microstructural evolution in undercooled Fe-Ni alloys was performed on uniformly processed samples covering seven orders of magnitude in volume. At appropriate undercooling levels, alternate solidification pathways become thermodynamically possible and metastable product structures can result from the operation of competitive solidification kinetics. For thermal history evaluation, a heat flow analysis was applied and tested with large Fe-Ni alloy particles (1 to 3 mm) to assess undercooling potential. Alloy powders (10 to 150 microns), with large liquid undercoolings, were studied under the same composition and processing conditions to evaluate the solidification kinetics and microstructural evolution, including fcc/bcc phase selection and the thermal stability of a retained metastable bcc phase. The identification of microstructural transitions with controlled variations in sample size and composition during containerless solidification processing was used to develop a microstructure map which delineates regimes of structural evolutions and provides a unified analysis of experimental observations in the Fe-Ni system.