Optical and electrical characterizations of laser-chemical-vapor-deposited aluminum oxynitride films
Composition-dependent optical and electrical properties of L-CVD (Al2O3)1-c-(AlN)c composite films are examined. The optical properties exhibit a continuous change from Al2O3 to AlN with increasing value of the composition parameter c from zero to one. There is a critical concentration value of about 0.3 below and above which Al2O3- and AlN-like optical properties are observed. The impurity absorption regions are 5.1-6.7 eV for Al2O32 and 4.6-6.0 for AlN, while the energy gap is about 6.7 eV for Al2O3 and 6.0 eV for AlN. The electrical properties of Al-insulator n-Si MIS structures display externally programmable states when bulk-controlled electron emission occurs from the traps. In the high-field region a persistent polarization field is established within the insulator. C-V characteristics of the samples are more sensitive to the concentration factor c than the I-V characteristics. A large clockwise hysteresis is observed for AlN, but a smaller counterclockwise one is observed for Al2O3.